14 May 2004 Dependence of ArF resist on exposed area ratio
Author Affiliations +
Abstract
We investigated dependence of ArF resist on Exposed Area Ratio (EAR). Because it can be one of the CD variation factor and it is difficult to correct by OPC. Acrylate polymer based resist showed dependence on EAR. At low EAR, resist showed T-top profile and its CD became large. It could be considered that the profile change was caused by acid evaporation and re-sticking. Resist profile simulation indicated that CD variation appeared at only low EAR. To decreasing the effect of acid evaporation and re-sticking, we tried to increase the amount of acid evaporation by increasing PAB temperature. CD variation by EAR was decreased with increasing PAB temperature.
© (2004) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Eishi Shiobara, Eishi Shiobara, Kenji Chiba, Kenji Chiba, Kei Hayasaki, Kei Hayasaki, Daisuke Kawamura, Daisuke Kawamura, } "Dependence of ArF resist on exposed area ratio", Proc. SPIE 5376, Advances in Resist Technology and Processing XXI, (14 May 2004); doi: 10.1117/12.535142; https://doi.org/10.1117/12.535142
PROCEEDINGS
10 PAGES


SHARE
RELATED CONTENT

NIL defect performance toward high volume mass production
Proceedings of SPIE (March 22 2016)
SNR200 chemically amplified resist optimization
Proceedings of SPIE (July 07 1997)
Dependence of resist profile on exposed area ratio
Proceedings of SPIE (August 24 2001)
Enhanced flexible mask specifications
Proceedings of SPIE (August 28 2003)
Etching of 42 nm and 32 nm half pitch features...
Proceedings of SPIE (March 20 2008)

Back to Top