3 January 2005 Investigation of the growth and the holographic storage properties of Fe:LiTaO3 crystal
Author Affiliations +
Abstract
The LiTaO3 crystal doped with 0.03 wt% Fe2O3 was grown in a diameter-controlled Czochraski equipment using Si-Mo bar heater furnace. The photo-damage resistance ability, exponential gain coefficient, diffraction efficiency and response time of Fe:LiTaO3 and Fe:LiNbO3 crystals were measured. The measured results showed that the photo-damage resistance ability of Fe:LiTaO3 crystal was as much as 5 times higher than that of Fe:LiNbO3, the response speed of Fe:LiTaO3 crystal was improved one order of magnitude than that of Fe:LiNbO3, and the exponential gain coefficient and diffraction efficient of Fe:LiTaO3 crystal were smaller than that of Fe:LiNbO3, respectively. Using Fe:LiTaO3 crystal as recording medium, the obtained image was clear and complete in the holographic associative memory experiment using self-pump phase conjugate reflector.
© (2005) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Caixia Liu, Caixia Liu, Tao Zhang, Tao Zhang, Shouzhi Zhao, Shouzhi Zhao, } "Investigation of the growth and the holographic storage properties of Fe:LiTaO3 crystal", Proc. SPIE 5643, Advances in Optical Data Storage Technology, (3 January 2005); doi: 10.1117/12.574258; https://doi.org/10.1117/12.574258
PROCEEDINGS
5 PAGES


SHARE
Back to Top