4 April 2005 Emission and gain characteristics of Er-doped multicomponent bismuthate channel waveguide
Author Affiliations +
This paper reports on the preparation and the characteristics of Er-doped muliticomponent bismuthate channel waveguide. Dependence of emission lifetime of Er3+ ions on concentration of Er3+ ions is investigated. The concentration of Er3+ in the core film where concentration quenching effect starts is one order of magnitude higher than that of silicate materials. We show that the lower the hydroxyl ion content is, the longer the emission lifetime becomes and the emission lifetime of dehydrated core is the same as that of the fiber perform, namely the same quantum efficiency. The loss of the fabricated channel waveguide measured by cut-back method is 0.15 dB/cm at 1310 nm. Net gain of 8 dB is obtained at 1530 nm by using a 6-cm long waveguide pumped at 980 nm.
© (2005) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Yuki Kondo, Yuki Kondo, Motoshi Ono, Motoshi Ono, Manuel Reyes, Manuel Reyes, Hideaki Hayashi, Hideaki Hayashi, Junichi Kageyama, Junichi Kageyama, Naoki Sugimoto, Naoki Sugimoto, } "Emission and gain characteristics of Er-doped multicomponent bismuthate channel waveguide", Proc. SPIE 5723, Optical Components and Materials II, (4 April 2005); doi: 10.1117/12.588837; https://doi.org/10.1117/12.588837

Back to Top