4 May 2005 Enhanced inorganic bimetallic thermal resists transparency and resolution for photomask fabrication
Author Affiliations +
Abstract
Bimetallic films have been found to be promising direct write binary and grayscale photomask materials, as they turn transparent after laser exposure. Current structural analysis shows that the laser exposure is an oxidation process. The amount of the oxidized metal created during the laser writing process is related to the laser power, which in turn, determines the gray level (OD) of the exposed film. New exposure conditions have greatly increased the transparency of exposed films (down to 0.18 OD at 365 nm). Furthermore, this extended to deeper UV (300 nm). As the transparency of exposed area changes with the laser exposure power, grayscale photomasks can be created with the bimetallic films, and 3D structures can be produced in the substrate. Interference lithography has been used to investigate the bimetallic films resolution limit, which can generate much finer structures. Lines of 100-180 nm wide were successfully created on silicon and silicon dioxide. Aluminum thin films were found to turn transparent (0.28 OD) after laser exposure with high power, indicating that Al can also be a potential direct-write photomask material.
© (2005) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Glenn Chapman, Glenn Chapman, David Poon, David Poon, Chinheng Choo, Chinheng Choo, Yuqiang Tu, Yuqiang Tu, James Dykes, James Dykes, Jun Wang, Jun Wang, Jun Peng, Jun Peng, Willy Lennard, Willy Lennard, Karen Kavanagh, Karen Kavanagh, } "Enhanced inorganic bimetallic thermal resists transparency and resolution for photomask fabrication", Proc. SPIE 5753, Advances in Resist Technology and Processing XXII, (4 May 2005); doi: 10.1117/12.600463; https://doi.org/10.1117/12.600463
PROCEEDINGS
12 PAGES


SHARE
Back to Top