Fatigue crack propagation of magnesium alloy in biaxial stress fields

Yasumi Itoh; Akira Shimamoto

doi:10.1117/12.599238

9 May 2005 Fatigue crack propagation of magnesium alloy in biaxial stress fields

Yasumi Itoh, Akira Shimamoto

Proceedings Volume 5769, Nondestructive Detection and Measurement for Homeland Security III; (2005) https://doi.org/10.1117/12.599238
Event: Nondestructive Evaluation for Health Monitoring and Diagnostics, 2005, San Diego, CA, United States

Abstract

Fatigue crack propagation tests of magnesium alloy were conducted under conditions of biaxial and uniaxial loading by using a cruciform specimen in a biaxial fatigue machine, in order to investigate the effect of non-singular stress cycling on the fatigue crack growth properties ΔK_I -da/dN. The Magnesium alloys (AZ31B-O) used for this research are 2.5mm thickness plates. There are four different kinds of plates due to their heat treatment conditions. These conditions are (a) with no heat treatments (AZ31B-O), (b) 200-degree 2 hours (AZ31B-200), (c) 350-degree 2 hours (AZ31B-350), and (d) 430-degree 2 hours (AZ31B-430). From these comprehensive experiments, the remarkable effect was found in the specific biaxial load stress ratio σ_x⁰/σ_y⁰ on ΔK_I -da/dN relation. When biaxial load stress ratio was 0.5, it turned out that the fatigue crack propagation rate of a magnesium alloy becomes very slow. Of course, in other biaxial load stress ratios, fatigue crack propagation velocity was influenced to some extent. It turned out that fatigue crack propagation rate becomes fast when a biaxial load stress ratio is minus, and it becomes slow when a biaxial load stress ratio is plus. Some discussion is made on the effect of microstructure on fatigue crack propagation of magnesium alloy in a biaxial stress field.

Citation Download Citation

Yasumi Itoh and Akira Shimamoto "Fatigue crack propagation of magnesium alloy in biaxial stress fields", Proc. SPIE 5769, Nondestructive Detection and Measurement for Homeland Security III, (9 May 2005); https://doi.org/10.1117/12.599238

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available