9 May 2005 Fatigue crack propagation of magnesium alloy in biaxial stress fields
Author Affiliations +
Abstract
Fatigue crack propagation tests of magnesium alloy were conducted under conditions of biaxial and uniaxial loading by using a cruciform specimen in a biaxial fatigue machine, in order to investigate the effect of non-singular stress cycling on the fatigue crack growth properties ΔKI -da/dN. The Magnesium alloys (AZ31B-O) used for this research are 2.5mm thickness plates. There are four different kinds of plates due to their heat treatment conditions. These conditions are (a) with no heat treatments (AZ31B-O), (b) 200-degree 2 hours (AZ31B-200), (c) 350-degree 2 hours (AZ31B-350), and (d) 430-degree 2 hours (AZ31B-430). From these comprehensive experiments, the remarkable effect was found in the specific biaxial load stress ratio σx0y0 on ΔKI -da/dN relation. When biaxial load stress ratio was 0.5, it turned out that the fatigue crack propagation rate of a magnesium alloy becomes very slow. Of course, in other biaxial load stress ratios, fatigue crack propagation velocity was influenced to some extent. It turned out that fatigue crack propagation rate becomes fast when a biaxial load stress ratio is minus, and it becomes slow when a biaxial load stress ratio is plus. Some discussion is made on the effect of microstructure on fatigue crack propagation of magnesium alloy in a biaxial stress field.
© (2005) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Yasumi Itoh, Yasumi Itoh, Akira Shimamoto, Akira Shimamoto, } "Fatigue crack propagation of magnesium alloy in biaxial stress fields", Proc. SPIE 5769, Nondestructive Detection and Measurement for Homeland Security III, (9 May 2005); doi: 10.1117/12.599238; https://doi.org/10.1117/12.599238
PROCEEDINGS
12 PAGES


SHARE
Back to Top