12 June 2006 Influence of radiation defects on exciton-magnon interactions in nickel oxide
Author Affiliations +
Proceedings Volume 5946, Optical Materials and Applications; 59460D (2006) https://doi.org/10.1117/12.639158
Event: Optical Materials and Applications, 2005, Tartu, Estonia
Abstract
Influence of radiation defects on the optical absorption spectrum of nickel oxide (NiO) was studied at 6 K in the near-IR energy range of 7750-8300 cm-1 corresponding to the magnetic-dipole transition 3A2g(F)->3T2g(F) at nickel sites. NiO single crystals grown by the method of chemical transport reactions on the MgO(100) substrates were irradiated by the neutron fluences up to 5x1018 cm-2. Two sharp lines were observed at the low-energy side of the band: the peak at 7805 cm-1 is assigned to the pure exciton transition, whereas the peak at 7845 cm-1, to the exciton-magnon excitation that occurs at the Brillouin zone-center (BZC). An increase of the defect concentration at higher fluences results in the lowering of the magnon-satellite-peak intensity. The long-wavelength BZC magnon absorption is sensitive to the long- range magnetic ordering, which becomes destroyed in the presence of the radiation defects. Therefore, the observed decrease of the peak intensity is attributed to the decrease of the spin-spin correlation length due to inhomogeneous broadening.
© (2006) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Nina Mironova-Ulmane, Nina Mironova-Ulmane, Vera Skvortsova, Vera Skvortsova, Alexei Kuzmin, Alexei Kuzmin, Ilmo Sildos, Ilmo Sildos, } "Influence of radiation defects on exciton-magnon interactions in nickel oxide", Proc. SPIE 5946, Optical Materials and Applications, 59460D (12 June 2006); doi: 10.1117/12.639158; https://doi.org/10.1117/12.639158
PROCEEDINGS
5 PAGES


SHARE
Back to Top