Mitigation of laser damage growth in fused silica with a galvanometer scanned CO<sub>2</sub> laser

Isaac L. Bass; Gabriel M. Guss; Richard P. Hackel

doi:10.1117/12.638828

7 February 2006 Mitigation of laser damage growth in fused silica with a galvanometer scanned CO₂ laser

Isaac L. Bass, Gabriel M. Guss, Richard P. Hackel

Proceedings Volume 5991, Laser-Induced Damage in Optical Materials: 2005; 59910C (2006) https://doi.org/10.1117/12.638828
Event: Boulder Damage Symposium XXXVII: Annual Symposium on Optical Materials for High Power Lasers, 2005, Boulder, CO, United States

Abstract

At the National Ignition Facility (NIF) at the Lawrence Livermore National Laboratory (LLNL), mitigation of laser surface damage growth on fused silica using single and multiple CO₂ laser pulses has been consistently successful for damage sites whose lateral dimensions are less than 100 μm, but has not been for larger sites. Cracks would often radiate outward from the damage when a CO₂ pulse was applied to the larger sites. An investigation was conducted to mitigate large surface damage sites using galvanometer scanning of a tightly focused CO₂ laser spot over an area encompassing the laser damage. It was thought that by initially scanning the CO₂ spot outside the damage site, radiating crack propagation would be inhibited. Scan patterns were typically inward moving spirals starting at radii somewhat larger than that of the damage site. The duration of the mitigation spiral pattern was ~110 ms during which a total of ~1.3 J of energy was delivered to the sample. The CO₂ laser spot had a 1/e²-diameter of ~200 μm. Thus, there was general heating of a large area around the damage site while rapid evaporation occurred locally at the laser spot position in the spiral. A 30 to 40 μm deep crater was typically generated by this spiral with a diameter of ~600 μm. The spiral would be repeated until there was no evidence of the original damage in microscope images. Using this technique, damage sites as large as 300 μm in size did not display new damage after mitigation when exposed to fluences exceeding 22 J/cm² at 355 nm, 7.5 ns. It was found necessary to use a vacuum nozzle during the mitigation process to reduce the amount of re-deposited fused silica. In addition, curing spiral patterns at lower laser powers were used to presumably "re-melt" any re-deposited fused silica. A compact, shearing interferometer microscope was developed to permit in situ measurement of the depth of mitigation sites.

Citation Download Citation

Isaac L. Bass, Gabriel M. Guss, and Richard P. Hackel "Mitigation of laser damage growth in fused silica with a galvanometer scanned CO₂ laser", Proc. SPIE 5991, Laser-Induced Damage in Optical Materials: 2005, 59910C (7 February 2006); https://doi.org/10.1117/12.638828

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available