You have requested a machine translation of selected content from our databases. This functionality is provided solely for your convenience and is in no way intended to replace human translation. Neither SPIE nor the owners and publishers of the content make, and they explicitly disclaim, any express or implied representations or warranties of any kind, including, without limitation, representations and warranties as to the functionality of the translation feature or the accuracy or completeness of the translations.
Translations are not retained in our system. Your use of this feature and the translations is subject to all use restrictions contained in the Terms and Conditions of Use of the SPIE website.
2 March 2006Green-light emission of ZnO nanoparticles spontaneously precipitated in fluorinated polyimide films
The light emitting property of zinc oxide (ZnO) nanoparticles, which were spontaneously precipitated and dispersed in fluorinated polyimide films has been studied because this hybrid material exhibits interesting properties and could be widely applied in optoelectronics and photonics. Polyimides (PI) provide high thermal and chemical stability and outstanding electrical properties. In addition, ZnO presents excellent optical properties due to its wide band gap (3.37 eV) at room temperature and large exciton bonding energy (60 meV), which can be used in light-emitting diodes, transparent electrodes, and piezoelectric devices. By adding small amount of Zinc compounds (5 mol %), either Zinc hexafluoroacetylacetonate dihydrate or Zinc nitrate hexahydrate, to precursor solutions of polyimides followed by thermal curing at 350~390°C, the green light emission at ca. 520 nm of polyimides has been significantly enhanced by 10 to 15 times respectively.
When zinc concentration excesses the saturation level, light emission decreases and emission peak was shifted to higher wavelengths due to the aggregation of ZnO. This can be explained by the quantum confinement mechanism and the interaction between the oxygen of ZnO and PI functional groups. Zinc compound precursors and curing temperature and atmosphere affect the light emitting behavior which will be discussed in detail.