16 March 2007 Fidelity of rectangular patterns printed with 0.3-NA MET optics
Author Affiliations +
Abstract
Arrays of rectangular patterns of various sizes were printed with the EUV micro-exposure tool (MET) at the Lawrence Berkeley National Laboratory (LBNL) using the chemically-amplified resist MET-1K; and their fidelity to the mask patterns was evaluated. The experimental results showed that the shortening of resist patterns in the lengthwise direction was greater for smaller patterns. For example, the line-end shortening of half-pitch (hp) 45-nm patterns was about 20-25 nm on one side, while that of hp-90-nm patterns was less than 10 nm. However, simulated aerial images exhibited little shortening, even for hp-45-nm patterns. On the other hand, considerable shortening appeared in hp-45-nm patterns after post-exposure-baking (PEB) process. When the acid diffusion length in the PEB process was assumed to be 20 nm, the calculated shapes of resist patterns agreed well with the experimental results for various sizes. Printing experiments showed that lowering the PEB temperature improved fidelity, probably due to the shorter acid diffusion length. Thus, we concluded that acid diffusion is the main cause of shortening in rectangular patterns printed with the MET. For better pattern fidelity, the acid diffusion length must be reduced in accordance with the reduction in pattern size.
© (2007) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Yuusuke Tanaka, Yuusuke Tanaka, Yukiko Kikuchi, Yukiko Kikuchi, DooHoon Goo, DooHoon Goo, Iwao Nishiyama, Iwao Nishiyama, } "Fidelity of rectangular patterns printed with 0.3-NA MET optics", Proc. SPIE 6517, Emerging Lithographic Technologies XI, 65172L (16 March 2007); doi: 10.1117/12.711900; https://doi.org/10.1117/12.711900
PROCEEDINGS
11 PAGES


SHARE
RELATED CONTENT

Ultra-thin-film EUV resists beyond 20nm lithography
Proceedings of SPIE (April 15 2011)
Static EUV micro-exposures using the ETS Set-2 optics
Proceedings of SPIE (June 15 2003)
Defect printability study using EUV lithography
Proceedings of SPIE (March 22 2006)

Back to Top