2 September 2008 Increased efficient copolymers with PFV and PPDFV for light emitting diodes
Author Affiliations +
Abstract
New electroluminescent copolymers with fluoro groups in vinylene unit, poly(9,9-di-hexylfluorene-2, 7-vinylene-co-pphenylenedifluorovinylene) (PFVPDFV), have been synthesized by the GILCH polymerization. The fluoro groups were introduced on vinylene units to increase the electron affinities of the copolymers. The PFVPDFVs exhibit absorption spectra with maximum peaks at 371 ~ 413 nm. In the PL spectra of PFVPDFVs, as the PDFV content increases up to 50% in the copolymer system, fwhm was decreased by 4 - 38 nm as compared to PFV. The HOMO energy levels of the copolymers were about 5.25 - 5.50 eV, and the LUMO energy levels were about 2.67-2.97 eV. The polymer LEDs (ITO/PEDOT/polymer/Al) of PFVPDFVs showed emission with maximum peaks at around 472 - 538 nm. By adjusting the feed ratios of PDFV in the copolymers, it was possible to tune the emission colors from greenish yellow to orange depending on the obtained CIE coordinates. The luminescence efficiencies of the copolymers at room temperature are about 0.1-1.47 cd/A. The introduction of up to 50 % of PDFV in PFVPDFVS can enhance the device performance to result in high current density, brightness and efficiency due to the increased electron injection ability caused by the presence of fluoro groups in the vinylene units.
© (2008) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Jun Kuk Kim, Youngeup Jin, Sung Heum Park, Jaeyeon Jung, Joo Young Shim, Kwanghee Lee, and Hongsuk Suh "Increased efficient copolymers with PFV and PPDFV for light emitting diodes", Proc. SPIE 7051, Organic Light Emitting Materials and Devices XII, 70511W (2 September 2008); https://doi.org/10.1117/12.799044
PROCEEDINGS
10 PAGES


SHARE
Advertisement
Advertisement
Back to Top