6 January 2009 Study of the transitory formation of α1 bainite, as a precursor of α-phase in tempered SMAs
Author Affiliations +
Proceedings Volume 7297, Advanced Topics in Optoelectronics, Microelectronics, and Nanotechnologies IV; 72970B (2009) https://doi.org/10.1117/12.823620
Event: Advanced Topics in Optoelectronics, Microelectronics, and Nanotechnologies IV, 2008, Constanta, Romania
Abstract
Bainite transitory formation, during the heating of a martensitic copper base SMA, was predicted by DSC and DTA and confirmed by XRD, OM and TEM only in hot pressed air cooled state homogenized and tempered at 573 K. In this heat treatment state, due to the pre-existence of α-phase, bainite amount is expected to be too low, therefore non-distinguishable, for higher tempering temperatures, where it is suggested that transitory α1 bainite turned to equilibrium α-phase. The results suggest that bainite formation could be considered as a precursory of α-phase phase during the heating of Cu-Zn-Al martensitic alloys, with no pre-existing α.
© (2009) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Leandru G. Bujoreanu, Sergiu Stanciu, Paul Bârsănescu, Nicoleta M. Lohan, "Study of the transitory formation of α1 bainite, as a precursor of α-phase in tempered SMAs", Proc. SPIE 7297, Advanced Topics in Optoelectronics, Microelectronics, and Nanotechnologies IV, 72970B (6 January 2009); doi: 10.1117/12.823620; https://doi.org/10.1117/12.823620
PROCEEDINGS
6 PAGES


SHARE
Back to Top