7 May 2009 Visible to SWIR response of HgCdTe HDVIP detectors
A. I. D'Souza; E. W. Robinson; M. G. Stapelbroek; W. Wong; M. Skokan; H.-D. Shih
Author Affiliations +
Proceedings Volume 7298, Infrared Technology and Applications XXXV; 72981X (2009) https://doi.org/10.1117/12.819206
Event: SPIE Defense, Security, and Sensing, 2009, Orlando, Florida, United States
Abstract
Detectors that have broadband response from the visible (~ 400 nm) to near infrared (~ 2.5 μm) have remote sensing hyperspectral applications on a single chip. 2.2 and 2.5 μm cutoff detectors permit operation in the 200 K range. The DRS HDVIP detector technology is a front side illuminated detector technology. Consequently, there is no substrate to absorb the visible photons as in backside-illuminated detectors and these 2.2 and 2.5-μm-cutoff detectors should be well suited to respond to visible light. However, HDVIP detectors are passivated using CdTe that absorbs the visible light photons. CdTe with a direct bandgap ~ 1.6 eV strongly absorbs photons of wavelength shorter than about 800 nm. Detectors in 320 x 6 arrays with varying thickness of CdTe passivation layers were fabricated to investigate the visible response of the 2.5-μm-cutoff detectors. The SWIR HDVIP detectors have well known high quantum efficiency (QE) in the near infrared region. Focus here was in acquiring array level data in the visible region of the spectrum. 320 x 6 FPA QE and NEI data was acquired using a 642 nm narrow band filter with 50 % points at 612 nm and 698 nm. The array QE average is ~ 70 % for the array with CdTe passivation thickness = 44.5 nm. The NEI is ~ 5 x 1010 ph/cm2/s at a flux Φ = 5.36 x 1013 ph/cm2/s. QE for an array with CdTe passivation thickness = 44.5 nm is ~ 10 % higher than an array with CdTe passivation thickness = 79.3 nm. In addition, a model that takes into account the complex optical properties of every layer in the HDVIP photodiode architecture was developed to predict the QE of the detectors in the near infrared and visible wavelength regions as a function of CdTe thickness. Measured QE as a function of wavelength is not a good match to the model QE probably due to limitations in the measured QE and knowledge of optical constants that are input into the model.
© (2009) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Citation Download Citation
A. I. D'Souza, E. W. Robinson, M. G. Stapelbroek, W. Wong, M. Skokan, and H.-D. Shih "Visible to SWIR response of HgCdTe HDVIP detectors", Proc. SPIE 7298, Infrared Technology and Applications XXXV, 72981X (7 May 2009); https://doi.org/10.1117/12.819206
PROCEEDINGS
 7 PAGES
DOWNLOAD PDF SAVE TO MY LIBRARY
SHARE
GET CITATION
< Previous Article
|
Next Article >
Advertisement
Advertisement
KEYWORDS
RELATED CONTENT
Subscribe to Digital Library
Receive Erratum Email Alert
Back to Top