27 April 2009 High growth rate deposition of highly oriented polycrystalline diamond film
Author Affiliations +
Abstract
(100) oriented polycrystalline diamond films are of benefit to applications such as optical windows and coatings due to its smoother as-grown surface and potentially better optical performance than randomly oriented diamond films. (100) Highly Oriented Diamond (HOD) films have been successfully grown on polished silicon wafer using the plasmaenhanced chemical vapor deposition technique (PECVD). The seeding procedure was based on Bias Enhanced Nucleation (BEN), which provided a high-density and uniform diamond nucleation on the entire two inch diameter silicon wafer. During the diamond deposition step subsequent to the BEN process, nitrogen gas was added in the standard methane/hydrogen processing gas mixture. The addition of small amount of nitrogen has three effects: 1) It increases the growth rate almost 3 times. 2) It stabilizes and enhances the (100) orientation growth. 3) It makes the HOD growth possible at high pressures (over 100 Torr) and high temperatures (over 1300 K). The diamond film has been characterized by confocal Raman and SEM, and an optimal temperature window for HOD growth has been identified. The growth rate of the (100) HOD growth rate reached > 16 μm/hour.
© (2009) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Chao Liu, Chao Liu, Wei Qiu, Wei Qiu, Helmuth Meissner, Helmuth Meissner, } "High growth rate deposition of highly oriented polycrystalline diamond film", Proc. SPIE 7302, Window and Dome Technologies and Materials XI, 73020H (27 April 2009); doi: 10.1117/12.818711; https://doi.org/10.1117/12.818711
PROCEEDINGS
10 PAGES


SHARE
RELATED CONTENT

Micro CVD diamond heat sink
Proceedings of SPIE (August 09 2013)
High rate chemical vapor deposition of diamond films by dc...
Proceedings of SPIE (December 01 1990)
Synthesis of thin diamond films on Si substrate by the...
Proceedings of SPIE (September 20 2002)
Diamond film: a promising passivation film of porous silicon
Proceedings of SPIE (November 29 2000)

Back to Top