The role of oxygen in secondary electron contrast of doped semiconductors in LVSEM

M. M. El Gomati; F. N. Zaggout; C. G. H. Walker; X. Zha

doi:10.1117/12.821810

22 May 2009 The role of oxygen in secondary electron contrast of doped semiconductors in LVSEM

M. M. El Gomati, F. N. Zaggout, C. G. H. Walker, X. Zha

Proceedings Volume 7378, Scanning Microscopy 2009; 73780Y (2009) https://doi.org/10.1117/12.821810
Event: SPIE Scanning Microscopy, 2009, Monterey, California, United States

Abstract

Patterned Si surfaces, p- and n-type doped, were examined for different secondary electron yield (contrast between ptype and n-type regions) under the electron beam of a scanning electron microscope. The contrast as a function of primary beam energy was studied for samples with a thick oxide layer and with the layer removed using an HF solution. It was found that the contrast between p- and n- type areas reversed on the samples with a thick oxide layer as the primary beam energy was increased. However, after the oxide layer was removed, the contrast reversal was no longer apparent. In addition, it was also found that regions on a patterned Si sample could reverse in contrast when the scan speed of the electron beam was changed. The various competing theories describing the dopant contrast effect of doped semiconductors are discussed and compared to the results reported here and elsewhere in the literature. It is concluded that oxygen at sub-monolayer coverage through to thick films plays an important role in the dopant contrast effect. However, adventitious carbon is equally important where a metal-oxide-semiconductor structure could exist with the presence of these two materials. Results from the literature using other techniques such as photoemission and field emission are also considered and it is found that these studies give results which are inconsistent with several of the current theories which attempt to explain the dopant contrast effect.

Citation Download Citation

M. M. El Gomati, F. N. Zaggout, C. G. H. Walker, and X. Zha "The role of oxygen in secondary electron contrast of doped semiconductors in LVSEM", Proc. SPIE 7378, Scanning Microscopy 2009, 73780Y (22 May 2009); https://doi.org/10.1117/12.821810

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available