2 December 2009 Effect of fabrication parameters on luminescent properties of ZnS:Mn nanocrystals
Author Affiliations +
Proceedings Volume 7631, Optoelectronic Materials and Devices IV; 76310U (2009) https://doi.org/10.1117/12.852944
Event: Asia Communications and Photonics, 2009, Shanghai, Shanghai , China
Abstract
In this work, we mainly focused on the luminescence properties of ZnS:Mn nanocrystals. Various samples of ZnS:Mn have been characterized at different doping concentration, annealing temperature, spin speed and time. The present study shows the application of spin speed, spin time, doping concentration and temperature affect the luminescent intensity performance. Luminescent intensity becomes higher with the increasing film thickness. Spin speed and spin time are two major concerns for coating film to a demanded thickness on the glass slide. Film thickness is the main reasons of the increasing intensity with spin speed and time. Temperature dependent PL measurements provide thermally activated energy transfer from other defects to Mn2+ ions. As the temperature increase, the carriers can be trapped at Mn sites, enhancing the luminescence spectra. Meanwhile, the quenching process influenced the PL intensity with doping concentration. This process occurs at high Mn concentration which the energy transfer from Mn ions to the other nearest Mn atom is weak. Therefore, the luminescence of transition from 4T1 to 6A1 of ions becomes stronger. From this reason, it is shown that luminescent intensity increased with higher doping concentration but decreased with higher annealing temperature, spin speed and spin time during spin coating process.
© (2009) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
S. Shaari, Muhammad S. A. Rahman, Noor A. A. M. Arif, "Effect of fabrication parameters on luminescent properties of ZnS:Mn nanocrystals", Proc. SPIE 7631, Optoelectronic Materials and Devices IV, 76310U (2 December 2009); doi: 10.1117/12.852944; https://doi.org/10.1117/12.852944
PROCEEDINGS
6 PAGES


SHARE
RELATED CONTENT

Glass and glass-ceramic photonic systems
Proceedings of SPIE (February 22 2017)
Luminescence of CdSiP2 crystals
Proceedings of SPIE (April 20 1998)
Optical studies of ZnO doped with transition metals
Proceedings of SPIE (March 02 2006)

Back to Top