20 May 2011 Anisotropy in structural and optical properties of chemical vapor deposited ZnS
Author Affiliations +
Abstract
Significant anisotropy in as-deposited CVD ZnS at several length scales has been demonstrated through investigation of structural and optical properties. Compressive strength of cylinders of CVD ZnS oriented in the growth direction is ~50% higher than cylinders taken perpendicular to the growth direction. Lattice parameter measurements of mandrel side (first-to-grow) material is ~0.4% smaller than growth side (last-to-grow) material in a cored sample representing ~500 hours of CVD growth, indicating significant strain along the growth direction. X-ray diffraction also shows evidence of preferred orientations for hexagonality which differ depending on position in the growth history. In crosssection, the cored sample shows several large bands which are correlated with different degrees of infrared absorption and BTDF scattering. However, no universal trend is found that applies to the whole length from the mandrel to the growth side regarding optical properties. The extinction in the visible and infrared is lower for measurements perpendicular to the growth axis than parallel to it, possibly due to scattering from the growth bands.
© (2011) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
John McCloy, John McCloy, Eric Fest, Eric Fest, Ralph Korenstein, Ralph Korenstein, W. Howard Poisl, W. Howard Poisl, } "Anisotropy in structural and optical properties of chemical vapor deposited ZnS", Proc. SPIE 8016, Window and Dome Technologies and Materials XII, 80160I (20 May 2011); doi: 10.1117/12.886138; https://doi.org/10.1117/12.886138
PROCEEDINGS
11 PAGES


SHARE
RELATED CONTENT

Fundamental optical properties of Zn3P2
Proceedings of SPIE (February 01 1992)
Growth and nonvolatile storage properties of Zn:Ce:Cu:LiNbO3
Proceedings of SPIE (September 17 2002)
Optical properties of ZnS/diamond composites
Proceedings of SPIE (December 01 1991)
Optical properties of Zn,Er-codoped Li-rich LiNbO3 crystal
Proceedings of SPIE (October 19 2001)

Back to Top