16 September 2011 Pulsed laser deposition of epitaxial BaFeO3 thin films
Author Affiliations +
Epitaxial thin films of Barium Ferrite (BaFeO3) have been fabricated by the pulsed laser deposition technique on a Si substrate. The magnetic parameters were measured using vibrating sample magnetometer. The ferromagnetic resonance (FMR) measurements of the thin film were found to be close to the parameters associated with bulk materials. The Atomic Force Microscope was used to determine the surface morphology at different temperatures. The derivative FMR line width was measured to be 70 Oe at 60 GHz and 50 Oe at 90 GHz. The relationship among the Coercivity, crystalline orientation, and grain shape and size is presented.
© (2011) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Abdalla Darwish, Abdalla Darwish, Simeon Wilson, Simeon Wilson, Brent Koplitz, Brent Koplitz, } "Pulsed laser deposition of epitaxial BaFeO3 thin films", Proc. SPIE 8120, Photonic Fiber and Crystal Devices: Advances in Materials and Innovations in Device Applications V, 81200D (16 September 2011); doi: 10.1117/12.914083; https://doi.org/10.1117/12.914083

Back to Top