15 February 2012 Influence of undoped YAG cap on diode-pumped composite YAG/Er:Yb:glass laser
Author Affiliations +
Two samples of Er-Yb doped phosphate glass were tested as a gain medium of longitudinally diode pumped laser. One sample was a simple Er:Yb:glass rod (length 2.8 mm), second sample was composite rod consisting of 2.8mm long Er:Yb:glass and 6mm long YAG crystal. Diameter of both samples was 6 mm. Dopant concentration for Er:Yb:glass was 0.75 × 1020 cm−3 Er and 1.7 × 1021 cm−3 Yb. The goal of the experiment was to investigate an effect of the undoped YAG cap on the Er:Yb:glass laser operation. The active medium, fixed in cupreous heatsink, was placed inside the 150mm long resonator consisted of a flat pumping mirror (HR @ 1.52−1.65 μm, HT @ 0.97 μm) and curved output coupler (r = 150 mm, R = 97% @ 1.52−1.61 μm). For Er:Yb:glass pumping a fiber coupled laser diode, operating in pulsed regime, was used. The pumping pulse width, energy, and wavelength were 1 ms, 10 mJ, and 975 nm, respectively. The decrease of Er:Yb:glass laser output pulse energy with increasing pumping repetition rate was observed for both samples. In case of simple Er:Yb:glass the energy dropped from 1.4mJ to 0.6mJ after pumping duty cycle increase from 0.5% to 6 %. In case of composite YAG/Er:Yb:glass active medium the relative output energy decrease was only 20% for pumping duty cycle increase from 0.5% to 10%. This result showed that the slope of the output energy decrease with increasing duty cycle was approximately four times slower for composite active media in comparison with simple Er:Yb:glass.
© (2012) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Jan Šulc, Helena Jelínková, Karel Nejezchleb, and Václav Škoda "Influence of undoped YAG cap on diode-pumped composite YAG/Er:Yb:glass laser", Proc. SPIE 8235, Solid State Lasers XXI: Technology and Devices, 82351Z (15 February 2012);


Erbium-based edge-pumped disk laser
Proceedings of SPIE (March 26 2013)
Space Qualified Diode Pumped Slab Laser
Proceedings of SPIE (July 06 1989)
Erbium-based gas-cooled disk laser
Proceedings of SPIE (February 14 2008)
Resonantly diode pumped Ho3+:YVO4 2.1-μm laser
Proceedings of SPIE (May 25 2011)

Back to Top