27 February 2012 Highly efficient InGaN/GaN blue LED on 8-inch Si (111) substrate
Author Affiliations +
We have grown LED structures on top of a robust n-type GaN template on 8-inch diameter silicon substrates achieving both a low dislocation density and a 7 um-thick template without crack even at a sufficient Si doping condition. Such high crystalline quality of n-GaN templates on Si were obtained by optimizing combination of stress compensation layers and dislocation reduction layers. Wafer bowing of LED structures were well controlled and measured below 20 μm and the warpage of LED on Si substrate was found to strongly depend on initial bowing of 8-inch Si substrates. The full-width at half-maximum (FWHM) values of GaN (0002) and (10-12) ω-rocking curves of LED samples grown on 8-inch Si substrates were 220 and 320 arcsec. The difference between minimum and maximum of FWHM GaN (0002) was 40 arcsec. The dislocation densities were measured about 2~3×108/cm2 by atomic force microscopy (AFM) after in-situ SiH4 and NH3 treatment. The measured quasi internal quantum efficiency of 8-inch InGaN/GaN LED was ~ 90 % with excitation power and temperature-dependent photoluminescence method. Under the un-encapsulated measurement condition of vertical InGaN/GaN LED grown on 8-inch Si substrate, the overall output power of the 1.4×1.4 mm2 chips representing a median performance exceeded 484 mW with the forward voltage of 3.2 V at the driving current of 350 mA.
© (2012) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Jun-Youn Kim, Jun-Youn Kim, Youngjo Tak, Youngjo Tak, Jaekyun Kim, Jaekyun Kim, Hyun-Gi Hong, Hyun-Gi Hong, Suhee Chae, Suhee Chae, Jae Won Lee, Jae Won Lee, Hyoji Choi, Hyoji Choi, Youngsoo Park, Youngsoo Park, U-In Chung, U-In Chung, Jong-Ryeol Kim, Jong-Ryeol Kim, Jong-In Shim, Jong-In Shim, "Highly efficient InGaN/GaN blue LED on 8-inch Si (111) substrate", Proc. SPIE 8262, Gallium Nitride Materials and Devices VII, 82621D (27 February 2012); doi: 10.1117/12.913250; https://doi.org/10.1117/12.913250


Highly efficient InGaN MQW LEDs grown on 200 mm Si...
Proceedings of SPIE (March 07 2014)
Large area bow free n+ GaN templates by HVPE for...
Proceedings of SPIE (March 07 2014)
Highly efficient InGaN GaN blue LEDs on large diameter Si...
Proceedings of SPIE (September 23 2011)
GaN substrates by HVPE
Proceedings of SPIE (February 12 2008)
Epitaxy of GaN LEDs on large substrates Si or...
Proceedings of SPIE (September 20 2006)

Back to Top