15 October 2012 Effect of SiNx interlayer on structural and electrical properties of nonpolar a-plane (11-20) gallium nitrides
Author Affiliations +
We investigated the effects of SiNx interlayers on the structural and electrical properties of nonpolar a-plane (11-20) GaN grown on r-plane (1-102) sapphire substrates by metal–organic chemical vapor deposition (MOCVD). The Nomarski optical microscope images showed that the deposition conditions of the SiNx layer could strongly affect the a-plane GaN surface morphology due to the different SiNx coverage. Basal-plane stacking faults (BSFs) and threading dislocation (TD) densities were reduced in the a-plane GaN samples with high SiNx coverage and multiple SiNx-treated GaN interlayers. These results indicate that TD reduction is associated with an increase in the 3D growth step and with the blocking of TD propagation. From on-axis (11-20) X-ray rocking curve (XRC) measurements, the anisotropy of full width at half maximum (FWHM) can be attributed to the crystal mosaicity due to insertion of different SiNx interlayers. The anisotropy of sheet resistance between the c-and m-axis was also clearly seen in a-plane GaN samples with a high density of defects, which was attributed to the BSFs as scattering centers.
© (2012) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Ji Hoon Kim, Ji Hoon Kim, Sung-Min Hwang, Sung-Min Hwang, Yong Gon Seo, Yong Gon Seo, Doo Soo Kim, Doo Soo Kim, Kwang Hyeon Baik, Kwang Hyeon Baik, Jung Ho Park, Jung Ho Park, } "Effect of SiNx interlayer on structural and electrical properties of nonpolar a-plane (11-20) gallium nitrides", Proc. SPIE 8484, Twelfth International Conference on Solid State Lighting and Fourth International Conference on White LEDs and Solid State Lighting, 84840H (15 October 2012); doi: 10.1117/12.929523; https://doi.org/10.1117/12.929523


Back to Top