11 March 2013 Optical characterization of Er-doped glasses for solar-pumped laser applications
Author Affiliations +
Proceedings Volume 8621, Optical Components and Materials X; 86211G (2013) https://doi.org/10.1117/12.2003775
Event: SPIE OPTO, 2013, San Francisco, California, United States
Abstract
Quantum efficiencies of Er3+-doped silicate, phosphate, tellurite and fluoride glasses have been examined under simulated sunlight excitation. The quantum efficiency of the whole emission bands was obtained as about 75 % for fluoride glass and about 2 % for silicate glass. The maximum quantum efficiency of the emission band at 1530 nm was about 35 % for fluoride glass and about 17 % for silicate glass. The product of the stimulated emission cross-section and the emission lifetime σstτf was about 46×10-24 cm2 sec for fluoride glass and about 54×10-24 cm for silicate glass. These values are about 2–4 times larger than that of Nd-doped glasses.
© (2013) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Takenobu Suzuki, Takenobu Suzuki, Yasuyuki Iwata, Yasuyuki Iwata, Kohei Nogata, Kohei Nogata, Shintaro Mizuno, Shintaro Mizuno, Hiroshi Ito, Hiroshi Ito, Kazuo Hasegawa, Kazuo Hasegawa, Yasutake Ohishi, Yasutake Ohishi, } "Optical characterization of Er-doped glasses for solar-pumped laser applications", Proc. SPIE 8621, Optical Components and Materials X, 86211G (11 March 2013); doi: 10.1117/12.2003775; https://doi.org/10.1117/12.2003775
PROCEEDINGS
8 PAGES


SHARE
Back to Top