Core-shell ZnO/γ-Fe2O3 nanoparticles were prepared via a simple method using forced hydrolysis of acetate metallic salts in a polyol medium. Two types of morphologies can be easily obtained: (i) quasi-spherical ZnO core 20 nm in diameter coated with a continuous shell with 3 nm in length, (ii) rod-like ZnO decorated with γ-Fe2O3 nanoparticles. The ZnO nanorods are 80 nm in diameter and 400 nm in length. The maghemite (γ-Fe2O3) nanoparticles with 5 nm in diameter are strongly bonded to ZnO, well separated from each other and form a monolayer on the surface of ZnO nanorods. In both systems, coating ZnO by γ-Fe2O3 inhibits the surface defects and thus enhances the UV luminescence. The two systems present a superparamagnetic behavior with blocking temperature depending on the morphology: the decorated ZnO nanorods present a blocking temperature around 6 K whereas this temperature is significantly higher (300 K) for spherical core-shell nanoparticles.
© (2013) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Imen Balti, Imen Balti, Laila Samia Smiri, Laila Samia Smiri, Pierre Rabu, Pierre Rabu, Philippe Léone, Philippe Léone, Eric Gautron, Eric Gautron, Bruno Viana, Bruno Viana, Noureddine Jouini, Noureddine Jouini, } "Synthesis and characterization of core@shell (ZnO@γ-Fe2O3) structured nanoparticles with two morphologies", Proc. SPIE 8626, Oxide-based Materials and Devices IV, 86261G (18 March 2013); doi: 10.1117/12.2002862; https://doi.org/10.1117/12.2002862
PROCEEDINGS
6 PAGES


SHARE
Back to Top