29 March 2013 Novel ArF photoresist polymer to suppress the roughness formation in plasma etching processes
Author Affiliations +
Abstract
The serious problem associated with 193-nm lithography using an ArF photoresist is roughness formation of photoresist polymer during plasma processes. We have previously investigated the mechanism of roughness formation caused by plasma. The main deciding factor for roughness formation is a chemical reaction between photoresist polymer and reactive species from plasma. The lactone group in photoresist polymer is highly chemically reactive, and shrinking the lactone structure enhances the roughness formation. In this paper, on the basis of the mechanism of roughness formation, we propose a novel ArF photoresist polymer. The roughness formation was much more suppressed in the novel photoresist polymer during plasma etching process than in the previous type. In the novel photoresist polymer, chemical reactions were spread evenly on the photoresist film surface by adding the polar structure. As a result, decreases in the lactone group were inhibited, leading to suppressing ArF photoresist roughness.
© (2013) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Keisuke Kato, Keisuke Kato, Atsushi Yasuda, Atsushi Yasuda, Shin-ichi Maeda, Shin-ichi Maeda, Takuji Uesugi, Takuji Uesugi, Takeru Okada, Takeru Okada, Akira Wada, Akira Wada, Seiji Samukawa, Seiji Samukawa, } "Novel ArF photoresist polymer to suppress the roughness formation in plasma etching processes", Proc. SPIE 8682, Advances in Resist Materials and Processing Technology XXX, 86821R (29 March 2013); doi: 10.1117/12.2011096; https://doi.org/10.1117/12.2011096
PROCEEDINGS
10 PAGES


SHARE
Back to Top