Optical loss and residual stress measurement of infrared chalcogenide glasses and analysis on its influencing factors

Baoan Song; Yan Yang; Zhitai Jia; Feifei Chen; Changgui Lin; Shixun Dai; Xunsi Wang; Xiang Shen; Tiefeng Xu; Qiuhua Nie

doi:10.1117/12.2021071

22 June 2013 Optical loss and residual stress measurement of infrared chalcogenide glasses and analysis on its influencing factors

Baoan Song, Yan Yang, Zhitai Jia, Feifei Chen, Changgui Lin, Shixun Dai, Xunsi Wang, Xiang Shen, Tiefeng Xu, Qiuhua Nie

Author Affiliations +

Proceedings Volume 8769, International Conference on Optics in Precision Engineering and Nanotechnology (icOPEN2013); 87693R (2013) https://doi.org/10.1117/12.2021071
Event: International Conference on Optics in Precision Engineering and Nanotechnology (icOPEN2013), 2013, Singapore, Singapore

Abstract

Chalcogenide glasses (ChGs) have a relatively small temperature coefficient of refractive index, broad transmission range from almost visible to mid-infrared. It is suitable for precision molding. With the help of above mentioned merits, ChGs have a vast reservoir of value in the field of military and civilian infrared imaging. However, the internal defects of ChGs are caused by melting, cool-demoulding and annealing in a high vacuumed ampoule. The defects include the optical inhomogeneity, chemical inhomogeneity and built-in stress which trouble the homogeneity of ChGs and directly affect the imaging quality of infrared imaging devices. The detection and control of internal defects is a key technique. In this paper the platform for testing, characterization and evaluation of the inhomogeneity of ChGs will be designed and built. The appropriate testing and evaluation criteria of inhomogeneity during the preparation procedure of ChGs in the vacuumed ampoule will be studied. The transmittance of ChGs sample is measured repeatedly. The factor of internal multple reflection in ChGs sample is analysed and discussed. Analysis shows that the mean transmissivity of ChGs sample (Ge28Sb12Se60) with thick of 1 cm is approximately 66% in 8 to 11 microns. The loss is less than 2.40%/cm. The optical path difference (OPD) caused by residual stress in ChGs sample is less than 5.2 nm/cm. The results will provide a technical support to optimize the ChGs preparation process and improve the ChGs homogeneity.

Citation Download Citation

Baoan Song, Baoan Song, Yan Yang, Yan Yang, Zhitai Jia, Zhitai Jia, Feifei Chen, Feifei Chen, Changgui Lin, Changgui Lin, Shixun Dai, Shixun Dai, Xunsi Wang, Xunsi Wang, Xiang Shen, Xiang Shen, Tiefeng Xu, Tiefeng Xu, Qiuhua Nie, Qiuhua Nie, "Optical loss and residual stress measurement of infrared chalcogenide glasses and analysis on its influencing factors", Proc. SPIE 8769, International Conference on Optics in Precision Engineering and Nanotechnology (icOPEN2013), 87693R (22 June 2013); doi: 10.1117/12.2021071; https://doi.org/10.1117/12.2021071

ACCESS THE FULL ARTICLE

PERSONAL SIGN IN
Full access may be available with your subscription

Email or Username Forgot your username?

Password Forgot your password?

Show

Remember Email/Username on this computer

Remember Password

No SPIE account? Create an account
or Institutional Sign In via Shibboleth

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available

Members: $14.40

Non-members: $18.00 ADD TO CART

Show All Keywords

Keywords/Phrases

Search In:

Publication Years