28 February 2014 Spectroscopic characterization and energy transfer process in cobalt and cobalt-iron co-doped ZnSe/ZnS crystals
Author Affiliations +
Abstract
Cobalt doped II-VI wide band semiconductors (e.g. ZnSe, ZnS, CdSe) are promising media for infrared (IR) laser applications. They could be utilized as effective passive Q-switches for cavities of Alexandrite as well as Nd and Er lasers operating over 0.7-0.8, 1.3-1.6, and ~2.8 μm spectral ranges. We report spectroscopic characterization of Co:ZnSe and Co:ZnS crystals. Absorption cross-sections were measured for 4A2(F) → 4T1(P), 4A2(F) → 4T1(F), and 4A2(F) → 4T2(F) transitions with maximum absorption at 768(726), 1615(1500), 2690(2740) nm for ZnSe(ZnS) crystals, respectively. The calculated absorption cross-sections of the above transitions were estimated to be 64(56)×1019, 7.5(7.8)×1019, and 0.52(0.49)×1019 cm2 for ZnSe(ZnS) crystal hosts. In addition to the above applications the cobalt ions could be utilized for excitation of Fe2+ ions via resonance energy transfer process. Tunable room temperature lasing of Fe 2+ doped binary and ternary chalcogenides has been successfully demonstrated over 3.5-6 μm spectral range. However, II-VI lasers based on Fe2+ active ions don’t feature convenient commercially available pump sources (e.g. some Fe doped crystal hosts require pump wavelengths longer than 3 μm). Therefore, the process of energy transfer from Co2+ to Fe2+ ions could enable utilization of commercially available visible and near-infrared pump sources. We report a spectroscopic characterization of iron-cobalt co-doped ZnS and ZnSe crystals over 14-300K temperature range. Mid-IR laser oscillation at 3.9 μm(3.6 μm) via energy transfer in the Co:Fe:ZnSe (Co:Fe:ZnS) co-doped crystals was demonstrated under cobalt excitation at 4A2(F) → 4T1(P) (~0.7μm) and 4A2(F) → 4T1(F) (~1.56 μm) transitions.
© (2014) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
J. Peppers, J. Peppers, D. V. Martyshkin, D. V. Martyshkin, V. V. Fedorov, V. V. Fedorov, S. B. Mirov, S. B. Mirov, } "Spectroscopic characterization and energy transfer process in cobalt and cobalt-iron co-doped ZnSe/ZnS crystals", Proc. SPIE 8959, Solid State Lasers XXIII: Technology and Devices, 89591P (28 February 2014); doi: 10.1117/12.2040825; https://doi.org/10.1117/12.2040825
PROCEEDINGS
7 PAGES


SHARE
RELATED CONTENT


Back to Top