7 March 2014 Ga-rich GaxIn1-xP solar cells on Si with 1.95 eV bandgap for ideal III-V/Si photovoltaics
Author Affiliations +
Abstract
Theoretical models for III-V compound multijunction solar cells show that solar cells with bandgaps of 1.95-2.3 eV are needed to create ideal optical partitioning of the solar spectrum for device architectures containing three, four and more junctions. For III-V solar cells integrated with an active Si sub-cell, GaInP alloys in the Ga-rich regime are ideal since direct bandgaps of up to ~ 2.25 eV are achieved at lattice constants that can be integrated with appropriate GaAsP, SiGe and Si materials, with efficiencies of almost 50% being predicted using practical solar cell models under concentrated sunlight. Here we report on Ga-rich, lattice-mismatched Ga0.57In0.43P sub-cell prototypes with a bandgap of 1.95 eV grown on tensile step-graded metamorphic GaAsyP1-y buffers on GaAs substrates. The goal is to create a high bandgap top cell for integration with Si-based III-V/Si triple-junction devices. Excellent carrier collection efficiency was measured via internal quantum efficiency measurements and with their design being targeted for multijunction implementation (i.e. they are too thin for single junction cells), initial cell results are encouraging. The first generation of identical 1.95 eV cells on Si were fabricated as well, with efficiencies for these large bandgap, thin single junction cells ranging from 7% on Si to 11% on GaAs without antireflection coatings, systematically tracking the change in defect density as a function of growth substrate.
© (2014) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Christopher Ratcliff, T. J. Grassman, J. A. Carlin, D. J. Chmielewski, S. A. Ringel, "Ga-rich GaxIn1-xP solar cells on Si with 1.95 eV bandgap for ideal III-V/Si photovoltaics", Proc. SPIE 8981, Physics, Simulation, and Photonic Engineering of Photovoltaic Devices III, 898118 (7 March 2014); doi: 10.1117/12.2042017; https://doi.org/10.1117/12.2042017
PROCEEDINGS
8 PAGES


SHARE
RELATED CONTENT


Back to Top