8 October 2014 Combined-environment influence on microcrack evolution in mono-crystalline silicon
Author Affiliations +
Abstract
The impact of combined environment conditions (mechanical state, temperature, and relative humidity) on microcrack propagation characteristics in p-type monocrystalline, photovoltaic-grade Si wafers was examined. A four-point bend apparatus was used to impose static strain conditions in 280 micron thick monocrystalline Si wafers containing microindentation-initiated crack centers. The specimen under test was simultaneously subjected to varied temperature and relative humidity conditions within a controlled environment chamber. Microcrack length was monitored after exposure to two sets of temperature and relative humidity conditions (i.e. 20℃ and 33%, 40℃ and 60% respectively) using scanning electron microscopy. Two primary stages of crack elongation behavior were observed under both of the combined environment conditions. Specifically, an early-time, more rapid growth period occurred, followed by more limited crack growth at later times. The deceleration of crack propagation is consistent with stress relaxation accompanying crack elongation under the constant strain conditions imposed. In general, an increase in the average microcrack propagation rate within both growth rate ranges and in the final overall change in average crack length was observed under elevated temperature and humidity conditions. These findings support the probable role of local crack-tip environment on microcrack evolution.
© (2014) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
W.-J. Huang, W.-J. Huang, Z. D. Fortuno, Z. D. Fortuno, M. Li, M. Li, J. Liu, J. Liu, H. Liao, H. Liao, K. Simmons-Potter, K. Simmons-Potter, B. G. Potter, B. G. Potter, } "Combined-environment influence on microcrack evolution in mono-crystalline silicon", Proc. SPIE 9179, Reliability of Photovoltaic Cells, Modules, Components, and Systems VII, 91790U (8 October 2014); doi: 10.1117/12.2062162; https://doi.org/10.1117/12.2062162
PROCEEDINGS
12 PAGES


SHARE
RELATED CONTENT

Detecting loss mechanisms of c Si PV modules in situ...
Proceedings of SPIE (September 26 2016)
Acceleration factor for damp heat testing of PV modules
Proceedings of SPIE (September 17 2018)
Availability model of stand-alone photovoltaic system
Proceedings of SPIE (August 07 2017)
Performance of Amonix multijunction arrays
Proceedings of SPIE (August 24 2009)
Reliability of PV systems
Proceedings of SPIE (September 10 2008)

Back to Top