18 December 2014 Preparation and spectral properties of Ho3+/Tm3+ co-doped Germanium glass active optical fiber material
Author Affiliations +
Abstract
A series of Tm3+/Ho3+ sensitized 65GeO2-7BaF2-10B2O3-4Al2O3-4ZnO2-10Na2O glass samples were synthesized using high temperature melting method. The spectral properties were systematically studied when Ho3+ concentration was 0.1, 0.3, 0.5 mol% and Tm2O3 changed from 0.3 mol% to 2.5mol%. Differential thermal analysis showed that ΔT was higher than 190°C, which illustrated this kind of matrix glass have better thermal stability. The absorption cross section peak height, free energy of Ho3+ from 5I8 to 5I7, and emission cross section were calculated according to Mc-Cumber theory. Under the excitation of 808nm laser diode, fluorescence intensity at 1954nm reached the highest value when the concentration of Ho3+ was 0.1mol% and Tm3+ was 0.7mol%. However the fluorescence intensity reduced greatly when Ho3+ concentration was 0.5mol% and Tm3+ exceeded 1.5mol%. The sensitized function and influence of different Tm3+/Ho3+ doped ion ratios on the spectral properties were studied.
© (2014) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
L. L. Wang, Y. Y. Guo, C. M. Gao, F. Tan, J. Wang, K. X. Han, F. X. Yu, "Preparation and spectral properties of Ho3+/Tm3+ co-doped Germanium glass active optical fiber material", Proc. SPIE 9295, International Symposium on Optoelectronic Technology and Application 2014: Laser Materials Processing; and Micro/Nano Technologies, 92950F (18 December 2014); doi: 10.1117/12.2069470; https://doi.org/10.1117/12.2069470
PROCEEDINGS
8 PAGES


SHARE
Back to Top