13 March 2015 Negative-tone imaging with EUV exposure for 14nm hp and beyond
Author Affiliations +
Abstract
Manipulation of dissolution properties by changing organic solvent developer and rinse material provides a novel technology to obtain fine pattern beyond the limitation of imaging system based on alkaline developer. QCM study showed no swelling character in negative-tone imaging (NTI) process even for current developer of n-butyl acetate (nBA). Actually, NTI process has shown advantages on resolution and line-width roughness (LWR) in loose pitch around 30 ~ 45 nm hp as a consequence of its non-swelling character. On the other hand, bridge and collapse limited its resolution below 20 nm hp, indicating that non-negligible amount of swelling still exists for tight pitch resolution. We investigated effects of solubility parameter of organic solvents on resolution below 20 nm hp. A bridge was reduced with a decrease in the solubility parameter dp from nBA. On the other hand, much lower dp caused film remaining due to its extremely slow Rmax. Based on these results, we newly developed FN-DP301 containing organic solvent with smaller dp than nBA. Although rinse solvent gave negligible effects on bridge, there is a clear improvement on pattern collapse only in case of using new rinse solvent of FN-RP311. Lithographic performances of NTI process using nBA and FN-DP301 together with the other organic solvents were described in this paper under exposures with an E-beam and a EUV light. It is emphasized that 14 nm hp resolution was obtained only using FN-DP301 as a developer and FN-RP311 as a rinse under E-beam exposure. NTI showed 43% faster photospeed in comparison with PTI at 16 nm hp, indicating that NTI is applicable to obtain high throughput with maintaining resolution. In addition, sub-20 nm trench was obtained using NTI without bridge under EUV exposure, all of which are attributed to the low swelling character of NTI process. Similarly, NTI was able to print 20 nm dots using NXE:3100 with only a little peeling. Conversely CH patterning was significantly worse with NTI compared to PTI, that is, only 36 nm contacts with 60 nm pitch was resolved under EUV exposure.
© (2015) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Hideaki Tsubaki, Hideaki Tsubaki, Wataru Nihashi, Wataru Nihashi, Toru Tsuchihashi, Toru Tsuchihashi, Toru Fujimori, Toru Fujimori, Makoto Momota, Makoto Momota, Takahiro Goto, Takahiro Goto, } "Negative-tone imaging with EUV exposure for 14nm hp and beyond", Proc. SPIE 9422, Extreme Ultraviolet (EUV) Lithography VI, 94220N (13 March 2015); doi: 10.1117/12.2085696; https://doi.org/10.1117/12.2085696
PROCEEDINGS
12 PAGES


SHARE
Back to Top