You have requested a machine translation of selected content from our databases. This functionality is provided solely for your convenience and is in no way intended to replace human translation. Neither SPIE nor the owners and publishers of the content make, and they explicitly disclaim, any express or implied representations or warranties of any kind, including, without limitation, representations and warranties as to the functionality of the translation feature or the accuracy or completeness of the translations.
Translations are not retained in our system. Your use of this feature and the translations is subject to all use restrictions contained in the Terms and Conditions of Use of the SPIE website.
4 June 2015Effects of AlSb interfaces on InAs/InAsSb type-II infrared superlattice material properties
Significant attention has recently been given to photoluminescence (PL) spectra and lifetime measurements on InAs/InAsSb superlattices, as high quality optical material with long carrier lifetimes are required for infrared detectors. The standard sample structure for PL measurements includes energy barriers to block photo-generated carriers from being lost through non-radiative recombination at interfaces between the superlattice and the surface or between the superlattice and the buffer/substrate. However, defect, surface, and/or interface states in AlSb, a commonly used barrier material, are known to contribute carriers to InAs quantum wells. Due to the similarity of the AlSb interface with the InAs/InAsSb superlattice, the effects of the barriers on the electrical and optical properties of the superlattice were investigated. Structures with AlSb barriers at the top and bottom of the superlattice, with no AlSb barriers, and with an AlSb barrier only at the top of the superlattice structure were studied. Hall Effect measurements revealed little change in the sheet carrier concentration at 10 K due to the barriers, but significant increases in low temperature mobility and a two-dimensional-like mobility temperature dependence were observed when barriers were present. Further high magnetic field measurements are necessary, however, to understand the transport properties of these samples due to the likelihood that multiple carriers are present. The photoluminescence (PL) spectra were almost identical regardless of the barriers, except for a 15% increase in intensity with the AlSb barrier between the buffer layer and the superlattice. The surface AlSb barrier had little effect on the intensity. The barriers are therefore recommended for PL measurements to increase the signal intensity; however, they complicate the analysis of single-field Hall Effect measurements.
The alert did not successfully save. Please try again later.
Elizabeth H. Steenbergen, Zhiyuan Lin, Said Elhamri, William C Mitchel, Yong-Hang Zhang, Ron Kaspi, "Effects of AlSb interfaces on InAs/InAsSb type-II infrared superlattice material properties," Proc. SPIE 9451, Infrared Technology and Applications XLI, 945114 (4 June 2015); https://doi.org/10.1117/12.2177696