14 July 2015 Effects of annealing on properties of Al2O3 monolayer film at 355 nm
Author Affiliations +
Al2O3 monolayer films were deposited on fused silica substrate and K9 glass substrate by electron-beam deposition. Annealing as a general post-treatment was used to enhance the quality of the Al2O3 coatings. The optical properties of the films were analyzed from the transmission spectra of the samples. The composition of the samples before and after annealing were measured by X-ray photoelectron spectroscopy (XPS). According to the analysis of the results, it can be found that the oxidation degree of the coatings increases after annealing in O2 inside coating chamber. The laser-induced damage thresholds of the Al2O3 films can be increased after the annealing process. Finally, the damage morphologies of the Al2O3 coatings were analyzed.
© (2015) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Feifei Tu, Feifei Tu, Hu Wang, Hu Wang, Huanbin Xing, Huanbin Xing, Ruxi Zheng, Ruxi Zheng, Weili Zhang, Weili Zhang, Kui Yi, Kui Yi, } "Effects of annealing on properties of Al2O3 monolayer film at 355 nm", Proc. SPIE 9532, Pacific Rim Laser Damage 2015: Optical Materials for High-Power Lasers, 95321F (14 July 2015); doi: 10.1117/12.2185988; https://doi.org/10.1117/12.2185988


Laser thin films with very high damage threshold
Proceedings of SPIE (October 04 2005)
Optical coatings in space
Proceedings of SPIE (October 04 2011)

Back to Top