26 September 2016 How heat influences CIGSSe solar cells properties
Author Affiliations +
Abstract
Non-encapsulated CIGSSe solar cells, with a silver grid, were exposed to different temperatures for various periods in order to measure the effect of the heat exposure in CIGSSe modules. The heat treatment time and temperature were varied during the experiments, which were executed at atmospheric conditions. In all the cases, after reaching a temperature of about 300°C, the IV measurement showed a reduction of 2-3% in terms of VOC and JSC. This is confirmed respectively by Raman and EQE measurements as well. The efficiency drop was -7%, -29% and -48% respectively for 30 seconds, 300 seconds and 600 seconds of exposure time. With temperatures larger than 225°C, the series resistance starts to increase exponentially and a secondary barrier becomes visible in the IV curve. This barrier prevents the extraction of electrons and consequently reducing the solar cells efficiency. Lock-in thermography demonstrated the formation of shunts on the mechanical scribes only for 300 and 600 seconds exposure times. The shunt resistance reduction is in the range of 5% for all time periods.
Conference Presentation
© (2016) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Marco Giacomo Flammini, Marco Giacomo Flammini, Nicola Debernardi, Nicola Debernardi, Maxime Le Ster, Maxime Le Ster, Klaas Bakker, Klaas Bakker, Brendan Dunne, Brendan Dunne, Johan Bosman, Johan Bosman, Mirjam Theelen, Mirjam Theelen, } "How heat influences CIGSSe solar cells properties", Proc. SPIE 9938, Reliability of Photovoltaic Cells, Modules, Components, and Systems IX, 99380C (26 September 2016); doi: 10.1117/12.2240266; https://doi.org/10.1117/12.2240266
PROCEEDINGS
11 PAGES + PRESENTATION

SHARE
Back to Top