26 September 2016 Reliability and efficacy of organic passivation for polycrystalline silicon solar cells at room temperature
Author Affiliations +
Oleylamine is used as a passivating layer instead of commercial high temperature SiNx. Oleylamine coating applied on the n-type emitter side with p-type base polycrystalline silicon solar cells at room temperature using a simple spin coating method. It has been observed that there is 16% increase in efficiency after Oleylamine coating. Further, the solar cell was subjected to standard characterization namely current-voltage measurement for electrical parameters and Fourier transform infrared spectroscopy to understand the interaction of emitter surface and passivating Oleylamine. However, the passivation layer is not stable due to the reaction between Oleylamine and ambient air content such as humidity and carbon dioxide. This degradation can be prevented with suitable overcoating.
Conference Presentation
© (2016) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Onkar S. Shinde, Onkar S. Shinde, Adinath M. Funde, Adinath M. Funde, Sandesh R. Jadkar, Sandesh R. Jadkar, Rajiv O. Dusane, Rajiv O. Dusane, Neelkanth G. Dhere, Neelkanth G. Dhere, Subhash V. Ghaisas, Subhash V. Ghaisas, } "Reliability and efficacy of organic passivation for polycrystalline silicon solar cells at room temperature", Proc. SPIE 9938, Reliability of Photovoltaic Cells, Modules, Components, and Systems IX, 99380G (26 September 2016); doi: 10.1117/12.2237414; https://doi.org/10.1117/12.2237414


Prismatic bioinspired compound lenses for solar cells
Proceedings of SPIE (March 23 2011)
Performance of a new type of module based on back...
Proceedings of SPIE (August 19 2010)
Reliability of PV systems
Proceedings of SPIE (September 10 2008)

Back to Top