1 April 1985 Heterojunction Stripe Geometry Lead Salt Diode Lasers Grown By Molecular Beam Epitaxy
Author Affiliations +
Abstract
Abstract. Lead-rare earth-chalcogenide diode lasers have been grown by molecular beam epitaxy. Emission wavelengths shorter than 5 to 6 Am have been obtained from lead-europium-selenide-telluride (Pb1 -xEuxSeyTe1-y) double heterojunction diode lasers grown lattice-matched to PbTe substrates. Mesa diodes with -25 um wide stripes have been fabricated that have a wide range of single longitudinal mode emission at up to -1 mW/facet output power. These diodes have operated at up to 147 K cw, which to our knowledge is the highest cw operating temperature ever achieved with lead-chalcogenide diode lasers. The wavelength coverage of the PbTe system has so far been extended to 4.06 um cw. Longer wavelength coverage is obtained from double heterojunction diode lasers with Ma1-ySnyTe active regions lattice-matched to (Pb1-ySny)1-xYbxTe confinement layers. I n preliminary studies of diodes with x = 0.034, y = 0.14, the cw emission wavelength varied from 10.7 µm (at 10 K) to 7.1 µm (at 128 K).
D. L. Partin, D. L. Partin, } "Heterojunction Stripe Geometry Lead Salt Diode Lasers Grown By Molecular Beam Epitaxy," Optical Engineering 24(2), 242367 (1 April 1985). https://doi.org/10.1117/12.7973487 . Submission:
JOURNAL ARTICLE
4 PAGES


SHARE
RELATED CONTENT

Developments In Lead-Salt Diode Lasers
Proceedings of SPIE (July 08 1986)
An Overview Of Tunable Diode Laser Technology Development
Proceedings of SPIE (December 25 1984)
Review Of State Of The Art Lead Salt Diode Laser...
Proceedings of SPIE (October 15 1984)
Lead salt tunable diode lasers key devices for high...
Proceedings of SPIE (March 31 1999)
Recent progress in lead-salt lasers
Proceedings of SPIE (April 11 1996)

Back to Top