1 June 2008 Reflectivity and surface roughness of multilayer-coated substrate recovery layers for EUV lithographic optics
Author Affiliations +
Abstract
We investigated the use of separation, or substrate recovery, layers (SRLs), to enable the reuse of optical substrates after the deposition of multilayer reflective coatings, in particular Mo/Si multilayers as used for EUV lithography. An organic material (polyimide), known from other work to reduce the roughness of the substrate, was applied to the optical substrate. It appeared to be possible to remove the multilayer coating, including the SRL, without any damage or roughening of the substrate surface. The SRL was spin-coated at 1500 to 6000 rpm on different substrate types (Si, quartz, Zerodur) with diameters up to 100 mm. For this range of parameters, the multilayer centroid wavelength value remained unchanged, and its reflectivity loss on applying the SRL was limited typically to 0.7%. The latter was shown to be caused by a minor increase of the SRL surface roughness in the high-spatial-frequency domain. The roughness, characterized with an atomic force microscope, remained constant at 0.2 nm during all stages of the substrate recovery process, independent of the initial substrate roughness.
© (2008) Society of Photo-Optical Instrumentation Engineers (SPIE)
Ileana Nedelcu, Ileana Nedelcu, Robbert W. E. van de Kruijs, Robbert W. E. van de Kruijs, Andrey E. Yakshin, Andrey E. Yakshin, Bernhard von Blanckenhagen, Bernhard von Blanckenhagen, Fred Bijkerk, Fred Bijkerk, } "Reflectivity and surface roughness of multilayer-coated substrate recovery layers for EUV lithographic optics," Optical Engineering 47(6), 063801 (1 June 2008). https://doi.org/10.1117/1.2939403 . Submission:
JOURNAL ARTICLE
5 PAGES


SHARE
RELATED CONTENT

X-ray study of surfaces and interfaces
Proceedings of SPIE (December 09 2001)
High-performance multilayer coatings for 106 nm
Proceedings of SPIE (September 27 2007)
EUV multilayer optics for space science and ultrafast science
Proceedings of SPIE (February 17 2011)
EUV multilayers for solar physics
Proceedings of SPIE (January 28 2004)

Back to Top