1 July 2011 Slab optical waveguides in Er3 +-doped tellurite glass by N+ ion implantation at 1.5 MeV
Author Affiliations +
Slab optical waveguides were fabricated in tung-sten-tellurite glass doped with Er3 + ions by means of nitrogen ion implantation at 1.5 MeV. A wide range of ion doses (from 5·1012 to 8·1016 ions/cm2) was used. Optical characterization, performed by dark-line spectroscopy, revealed that the waveguides were of optical barrier type: the implanted layer exhibited a decrease of the refractive index with respect to the virgin bulk glass, while the region comprised between the sample surface and the end of the ion track acted as an optical guiding structure. It was also demonstrated that a post-implantation annealing process, performed at various temperatures on the samples implanted at higher doses, contributes to the reduction of the barrier region.
© (2011) Society of Photo-Optical Instrumentation Engineers (SPIE)
Simone Berneschi, Simone Berneschi, Massimo Brenci, Massimo Brenci, Gualtiero Nunzi Conti, Gualtiero Nunzi Conti, Stefano Pelli, Stefano Pelli, Marco Bettinelli, Marco Bettinelli, Adolfo Speghini, Adolfo Speghini, István Bányász, István Bányász, Andrea Watterich, Andrea Watterich, Miklós Fried, Miklós Fried, Tivadar Lohner, Tivadar Lohner, Péter Petrik, Péter Petrik, Nguyen Q. Khanh, Nguyen Q. Khanh, Zsolt Zolnai, Zsolt Zolnai, } "Slab optical waveguides in Er3 +-doped tellurite glass by N+ ion implantation at 1.5 MeV," Optical Engineering 50(7), 071110 (1 July 2011). https://doi.org/10.1117/1.3559209 . Submission:

Back to Top