30 May 2022 Applications of thin-film lithium niobate in nonlinear integrated photonics
Author Affiliations +
Abstract

Photonics on thin-film lithium niobate (TFLN) has emerged as one of the most pursued disciplines within integrated optics. Ultracompact and low-loss optical waveguides and related devices on this modern material platform have rejuvenated the traditional and commercial applications of lithium niobate for optical modulators based on the electro-optic effect, as well as optical wavelength converters based on second-order nonlinear effects, e.g., second-harmonic, sum-, and difference-frequency generations. TFLN has also created vast opportunities for applications and integrated solutions for optical parametric amplification and oscillation, cascaded nonlinear effects, such as low-harmonic generation; third-order nonlinear effects, such as supercontinuum generation; optical frequency comb generation and stabilization; and nonclassical nonlinear effects, such as spontaneous parametric downconversion for quantum optics. Recent progress in nonlinear integrated photonics on TFLN for all these applications, their current trends, and future opportunities and challenges are reviewed.

1.

Introduction

The excellent electro-optic (EO) and nonlinear optical properties of lithium niobate (LiNbO3 or LN) have long established it as a prevailing photonic material for the long-haul telecom modulator and wavelength-converter markets. Indeed, the first nonlinear experiment in any waveguide platform was a demonstration of Cherenkov radiation from titanium-diffused LN.1 Conventional LN waveguides are most commonly formed by in-diffusion of titanium (Ti) dopants2 or by the proton exchange process.3 However, these conventional lithium niobate optical waveguides have a low index-contrast, hence are bulky compared with modern integrated platforms, such as silicon photonics. The bulkiness impedes photonic circuit implementations and imposes high optical power requirements for nonlinear applications.

Achieving thin films of LN (with a thickness of a few hundred nanometers) that reside on an insulator cladding with a much lower index (e.g., silicon dioxide, SiO2)— along with methods to achieve low-loss ridge or channel waveguides on the thin films—can address the above issues and yield high-contrast waveguides. Thin-film lithium niobate (TFLN) wafers on silicon (Si) substrates and high-contrast waveguides (with submicron cross-sectional dimensions) were developed for the first time at CREOL in 2013.4 Since the commercialization of TFLN wafers by a few vendors,57 efforts by several research teams have tremendously advanced the field of TFLN-integrated photonics. A plethora of ultracompact linear and nonlinear optical devices and circuits (waveguides, microring resonators, modulators, grating couplers, wavelength converters, entangled photon sources, isolators, supercontinuum, and comb sources) with unprecedented or significantly superior performances than the conventional (bulk) LN counterparts have been demonstrated. The combined efforts have rejuvenated LN for EO, nonlinear-, and quantum-optics applications, and the material is considered to be among the top candidates for heterogeneous integrated photonics. That is when multiple materials are monolithically integrated on the same substrate (preferably silicon), while each material is chosen for the functionalities that it suits the best.

TFLN is still under investigation for a better understanding of its fundamental properties, such as crystal defects, optical damage,8 and the photorefractive effect.9 First-principle studies have also been used to explore new capabilities of the material.10,11 Dry etching of LN is challenging in bulky conventional waveguides with deep sidewalls, hence diffusion or implantation of dopants is typically preferred. Etching appeared to be challenging in the early years of TFLN, thus rib-loading techniques were adopted,4,12,13 which is indeed advantageous for EO devices in some respects.14 However, direct etching of LN is preferred for nonlinear-optic applications. Partially due to the shallow etching required in TFLN waveguides, optical propagation losses as low as 0.027  dB/cm,15 as well as intrinsic Q-factors beyond 108,16 have been achieved. Even at the wafer level, a propagation loss of 0.27  dB/cm has been demonstrated,17 which is an important milestone for large-scale integration. Progress in fabrication processes on TFLN is reviewed elsewhere.18,19

Numerous studies have also been conducted on the technological improvement of the platform such as domain engineering,18,2023 which is particularly important for nonlinear devices based on periodic poling. Increasing numbers of functionalities are being demonstrated on TFLN and are rendering it a fully functional integrated platform. For example, light sources including rare-earth ion-doped2429 and Raman lasers30,31 as well as heterogeneously integrated electrically pumped III-V lasers32,33 have been demonstrated. Shams et al.33 adopted flip-chip bonding and demonstrated electrically pumped DFB lasers on TFLN with up to 60 mW of optical power coupled to the TFLN waveguide. The performance of EO modulators is still being further improved,34,35 with a recently reported data transmission rate of 1.96  Tb/s at a single wavelength with a 110 GHz 3-dB bandwidth and <1  V of driving voltage.36 Progress has been made in design and experimental results to enhance the EO bandwidth of TFLN modulators into the subterahertz regime.14,37 Other components, such as highly efficient couplers,38 tunable filters,39 optical isolators,40 and programmable spatial light modulators,41 have also been reported. This review paper, however, primarily covers research studies related to nonlinear optics.

Nonlinear optical processes have numerous applications in spectroscopy, quantum optics, and optical communication, among others. Since the first demonstration of second-harmonic generation (SHG) over six decades ago,42 a vast variety of materials and platforms have been explored for nonlinear optics applications.43 This review paper exclusively focuses on recent advancements in nonlinear integrated photonics on TFLN. Overviews of early developments of nonlinear effects in TFLN devices and recent progress on other materials can be found elsewhere.4446

2.

Second-Order Nonlinearity in Thin-Film Lithium Niobate

LN has been the primary material of choice for second-order nonlinear optics, owing to its large optical susceptibility (χ(2)) with the largest coefficient of it being diagonal, relatively large refractive index (no=2.21 and ne=2.14 at λ=1550  nm), low optical absorption, ultraviolet to mid-infrared optical transmission, and its ferroelectric property, which allows for efficient nonlinear processes through domain reversal. Several other materials have been traditionally considered for second-order nonlinear applications (e.g., see Table 1.5.3 in Ref. 43). For integrated solutions and in addition to LN, materials such as AlN,47 (Al)GaAs,48,49 and GaN,50 have lent themselves to thin film on insulator waveguide platforms. Their nonlinear coefficients and refractive indices are listed in Table 1 and compared with LNs. GaAs has a very high d36 value but it is not a ferroeletric material, hence modal-phase matching (PM) is typically pursued, which, as argued later, is less favorable than quasi-PM among fundamental guided modes.

Table 1

Optical properties of some of the materials used for second-order nonlinear applications.

MaterialLargest dcoefficientRefractive index at 1550 nm
LiNbO351d33=27  pm/V2.2
AlN52d33=4.7  pm/V2.1
GaAs51d36=119  pm/V3.4
GaN53d33=16.5  pm/V2.3

Initially, bulk material and conventional waveguides were used to explore the capabilities of LN for nonlinear applications.5457 Conventional waveguides, based on proton-exchange or titanium-diffusion, have demonstrated phenomenal performance and have been commercially available for several years.

Shortly after the emergence of TFLN on silicon substrates,4 it was realized that this new platform could take the performance of nonlinear devices to a much higher level.13,58 As shown in Fig. 1, owing to the compactness of TFLN waveguides provided by the high index contrast, optical mode sizes are remarkably smaller than those in conventional counterparts, hence much higher intensities can be achieved for the same optical power. Moreover, the overlap integral between the interacting optical modes at different wavelengths with the same parity is much larger. These differences result in significant improvements in efficiencies of various nonlinear processes. For example, the normalized conversion efficiency of second harmonic generation (SHG) has a direct relation to the overlap integral of the fundamental and second harmonic modes and an inverse relation to mode areas.46 Moreover, bending radii in the TFLN platform are much smaller than in the conventional LN because of its high index contrast, hence efficient and ultracompact microresonator structures can be easily realized on this platform for integrated nonlinear applications.

Fig. 1

Comparison of optical mode areas, index contrast, and crystal orientations in (a) conventional LN waveguides and (b) thin-film LN waveguides.

AP_4_3_034001_f001.png

Single-pass straight microwaveguides and resonant-based structures, such as microrings, microdisks, racetracks, and photonic crystals, have been used to investigate nonlinear integrated photonics on the TFLN platform. Classical second-order nonlinearities, such as SHG, sum-frequency generation (SFG), difference-frequency generation (DFG), optical parametric amplification (OPA), optical parametric oscillation (OPO), and the nonclassical spontaneous parametric downconversion (SPDC) process have been demonstrated, which are all covered in more details in the following sections.

It is well known that for an efficient nonlinear process, both the energy and momentum conservation conditions should be satisfied, the latter of which is not trivial due to waveguide and material dispersion. For example, SFG requires ω1+ω2=ω3 and k1+k2=k3 or n1ω1/c+n2ω2/c=n3ω3/c, where ωi denotes the angular frequencies of the participating signals in the nonlinear process, and ki and ni are the corresponding wavevector and refractive index, respectively.43 For the case of SHG, in which ω1=ω2, k1=k2, and n1=n2, the energy and momentum conservation conditions are simplified to ω3=2ω1, k3=2k1, or n(ω1)=n(2ω1). Similarly, these conditions should be fulfilled for other efficient nonlinear processes. In the presence of a wavevector mismatch (or as often referred to as phase mismatch), e.g., Δk=k1+k2k30 for SFG, the power oscillates between the participating frequencies instead of efficiently generating the targeted frequency. Therefore, PM becomes the most critical aspect of any nonlinear process. In addition, and in resonant-based structures, all the frequencies involved in an efficient nonlinear process should meet the resonance condition.

Various phase-matching methods are covered in Sec. 2.1 for SHG, which can be similarly applied to other three-wave mixing processes in TFLN. It is worth mentioning that for all these methods and considering the crystal orientation, the preferred polarization is, if possible, the one that utilizes the largest element in the χ(2) tensor of LN, i.e., d33. For instance, Fig. 2 shows the crystal orientation and preferred polarization for periodic poling and modal PM methods for straight waveguides. As shown in this figure, TFLN wafers are available in X-, Y-, and Z-cut orientations, and the desired polarization is chosen accordingly.

Fig. 2

Crystal orientations and corresponding preferred polarization to achieve maximum efficiency for nonlinear processes in TFLN using [(a), (b)] quasi phase matching via periodic poling and [(c), (d)] modal phase matching.

AP_4_3_034001_f002.png

2.1.

Second-Harmonic Generation in TFLN

SHG is considered the most fundamental three-wave mixing process, and it is commonly used to evaluate the performance of new materials and platforms. Hence, it is not surprising that SHG accounts for a sizable portion of the published works on three-wave mixing in TFLN. SHG can be used in applications such as light generation at inconvenient wavelengths for conventional semiconductor light sources, ultrashort pulse width measurement, and second-harmonic microscopy. This section reviews influential SHG studies that use straight waveguides, as well as resonator-based with various phase-matching methods. It is noted that for SHG, when the polarizations of both the pump (fundamental) and the second harmonic (SH) waves are the same and along the extraordinary axis, the PM method is called type-0 PM; otherwise, it is called type-I PM.

Several phase-matching methods have been adopted or developed on TFLN (see Fig. 3). They can be divided into two broad categories.46 The first group is perfect PM, which achieves Δk=0 by keeping the refractive indices for the fundamental and SH modes equal. Birefringent PM (BPM) and modal PM (MPM) are two examples of perfect PM methods. Cyclic PM (CMP), which is used in microrings and microdisks, meets the Δk=0 condition for perfect PM in certain azimuthal angles. The second category is quasi-PM (QPM), Δk0, which is based on perturbing the nonlinear process to compensate for phase mismatches and includes grating-assisted QPM (GA-QPM) and periodic poling. Using metasurfaces, PM-free SHG is also possible.

Fig. 3

Various phase-matching methods used on the TFLN platform. (a) Birefringent phase-matching.59 (b) Modal phase matching.60 (c) Grating-assisted quasi phase matching or mode shape modulation.61 (d) PPLN on a straight waveguide.13 (e) Natural quasi phase matching, which is conceptually similar to cyclic phase-matching.62 (f) Phase-matching-free metasurface.63

AP_4_3_034001_f003.png

The power relation of SHG in a lossless medium follows P2(P1L)2, where P1 and P2 are the pump and SH powers, respectively, and L is the device length.43 Therefore, a normalized conversion efficiency is defined as η=P2/(P12L2) with the unit of %W1cm2. However, the proportionality to L2 is rarely held in practical waveguides, since the relation is only valid in the low-loss regime.46 Therefore, it is worth considering the efficiency in units of %W1 as well for better performance evaluation and comparison. Such a normalized conversion efficiency, i.e., P2/P12, is typically reported for resonant-based structures. However, this again can lead to absurdly large numbers if P1 is very small, but without useful P2 values. It appears that the unitless absolute ratio of the output–input powers, P2/P1 (expressed in %), may be the ultimate meaningful efficiency for most practical applications.

2.1.1.

Birefringent phase matching

BPM can be attained in anisotropic materials by polarizing the fundamental and SH waves along different axes (type-I) to match the refractive indices at these frequencies and satisfy perfect PM. Although LN is a birefringent material, it is uncommon to use this method for SHG on TFLN, since it precludes the process from taking advantage of the largest element in the χ(2) tensor, corresponding to the nonlinear coefficient d33=27  pm/V. This is in addition to the spatial walk-off issue and practical difficulties in implementing BPM, particularly in integrated chips. Nonetheless, Lu et al.59 adopted an idea to demonstrate BPM on X-cut TFLN with an LN thickness of 10  μm. The refractive index of the TM00 mode at the C-band fundamental wavelength was matched to that of the TE00 mode at the SH by deviating the 20-mm-long straight waveguide from the optical axis of LN by an angle of θ=52  deg. Furthermore, the strong birefringence thermo-optic effect of LN was used to demonstrate a wide thermal tunability at a rate of 1.06  nm/K. The normalized conversion efficiency was, however, low (2.7%W1cm2). It seems that this design concept can be harnessed in other integrated birefringent materials, where QPM is not easily accessible.

2.1.2.

Modal phase matching

In MPM, the dispersion of a multimode waveguide is engineered to accomplish equal effective refractive indices for the fundamental mode at the pump wavelength and a higher-order mode at the SH wavelength. Nonlinear devices based on MPM are easy to fabricate and are functional after forming the waveguide or the microring without the need for postprocessing steps, such as periodic poling. MPM has been employed for straight waveguides64,65 and microresonator structures60,66 in both type-0 and type-I configurations. The type-I implementation leverages the strong thermo-optic birefringence of LN and can tune the wavelength efficiently over a wide span at the expense of using the d31=4.7  pm/V coefficient, which is more than five times smaller than d33. However, even in the type-0 configuration, the SHG efficiency is limited due to using higher-order modes at the SH wavelength, which are less confined, have a higher propagation loss, and have a much weaker overlap integral with the fundamental mode at the pump wavelength. Luo et al.65 demonstrated a type-I MPM in an 8-mm-long straight waveguide with a normalized SHG conversion efficiency of η=7.3%W1cm2 and a tuning slope of 0.84  nm/K from 1560 to 1620 nm. Wang et al.64 reported an η=41%W1cm2 for a 1-mm-long device using type-0 MPM. Usually, the third-order mode is used at the SH wavelength, since the overlap integral between modes with different parities is equal to zero in a homogeneous waveguide. However, by adding complexity to the fabrication process and by having inhomogeneous waveguides consisting of TiO2 on LN, the TE00 mode for the pump and the TE01 mode for the SH were utilized with much stronger overlap integral, resulting in η=650%W1cm2 in a 2.35-mm-long device.67 Chen et al.66 employed type-0 MPM and observed a 10-fold enhancement in SHG efficiency in a microring with 80  μm radius compared with a 1-mm-long straight waveguide with the same cross-section. A relatively high conversion efficiency of 1500%W1 was demonstrated in a microring resonator with a 50  μm radius using type-0 MPM.60 MPM has been used in microdisk resonators as well, in type-0 configuration on a Z-cut TFLN.6870 However, the efficiencies in microdisks are much lower than microrings, and one of the best reported values for the normalized conversion efficiency appears to be 11%W1.68

2.1.3.

Grating-assisted quasi phase matching

In GA-QPM, also known as mode shape modulation,61 guided modes are periodically perturbed to induce an extra phase term and compensate for the phase mismatch. Rao et al.61 implemented a sinusoidal width variation in a TFLN waveguide rib-loaded with SiN, which resulted in an estimated η of 1%W1cm2 for a 4.9-mm-long waveguide. Wang et al.64 employed direct etching of TFLN to form periodically grooved waveguides with a groove depth of 80 nm and obtained η=6.8%W1cm2 for a 500-μm-long device.

2.1.4.

Periodic poling in straight waveguides

Periodic poling, demonstrated first on bulk LN devices over a few decades ago,71 is the most common and efficient QPM technique on LN, especially for straight waveguides, despite Δk0. In this method, to compensate for Δk, the sign of the relevant nonlinear coefficient is periodically altered in the areas that the power is supposed to be converted back to the pump frequency. A periodicity of Λ=2π/Δk with a 50% duty cycle prevents power oscillation between interactive waves and facilitates a much more efficient power transfer from the pump to the targeted frequency. Devices made with this technique are called periodically poled lithium niobate (PPLN) and have been commercialized for many years. Poling is accomplished by utilizing the ferroelectric property of LN through domain inversion by applying electric fields greater than the coercive field. For congruent bulk LN, the coercive field value is 21  V/μm.72 This value is higher in TFLN (40 to 48  V/μm), which is possibly related to the interface of SiO2/LN bonding73 or the annealing step of the wafer fabrication process and the subsequent out-diffusion of Li+ ions.74 PPLN devices typically utilize d33 in a type-0 PM configuration in which the fundamental modes can be used for both the pump and SH wavelengths, resulting in a strong overlap integral and enhanced overall conversion efficiency. Extensive studies have been conducted to optimize the poling process parameters, e.g., preheat treatment, temporal waveform, and electric field strength for achieving a stable and uniform 50% duty cycle throughout the entire device.2123,75 Recently, several groups have successfully demonstrated submicron poling periods,7678 which are capable of compensating for large values of Δk and are of high demand, particularly for short-wavelength nonlinear devices and counterpropagating processes. Also, nondestructive measurement methods, such as piezo-response force microscopy (PFM), SH confocal microscopy,79 and far-field diffraction,80 are employed to visualize and evaluate the poling quality.

In 2016, PPLN devices were demonstrated for the first time on the TFLN platform on LN73 and Si13 substrates. Both devices relied on silicon nitride (SiN) rib-loaded waveguides on TFLN. Using SiN rib-loaded waveguides and by engineering the lateral leakage, a normalized conversion efficiency of 1160%W1cm2 was achieved in 2019 for a 4.8-mm-long device.81 Figure 4 shows various types of PPLN devices demonstrated in TFLN, such as straight waveguides and resonator structures.

Fig. 4

PPLN devices in different structures. (a) Straight waveguide.82 (b) Racetrack resonator that is poled on one of the straight arms.83 (c) Radially poled microring resonator.84 (d) Radially poled microdisk, poled using the PFM technique in which they also demonstrated a poling period as small as 200 nm.85

AP_4_3_034001_f004.png

Following the development of low loss etching processes,15 ultrahigh efficient nonlinear processes on TFLN using direct etching emerged. In 2018, using direct etching on a MgO-doped X-cut TFLN, Wang et al.86 reported normalized SHG conversion efficiencies of 2600 and 2300%W1cm2 for 4-mm-long devices on two different waveguide widths operating at two distinct wavelengths. MgO-doping mitigates any potential photorefractive effects in LN, and hence enables high-power operation. Chen et al.87 achieved a very similar performance on an undoped X-cut TFLN with an η of 2200%W1cm2 for a 4-mm-long device. In 2019, our group showed a record high normalized SHG conversion efficiency to date of 4600%W1cm2 on a 300-μm-long device by actively monitoring the poling process and by performing multiple iterative cycles of poling and depoling.82 In 2020, another very high η of 3757%W1cm2 was reported on a longer device length of 5 mm.88 Recently, a normalized conversion efficiency of 320%W1cm2 was reported for a 20-mm-long device corresponding to 1280%W1,89 which is relatively high for conversion efficiencies reported to this date in units of %W1 for straight waveguides (see Table 2).

Table 2

Performance of various devices based on straight waveguide structure for SHG using different phase-matching methods. Power values for the pump and SH wavelength and the absolute conversion efficiency (in %) correspond to the maximum normalized conversion efficiency and are not necessarily the maximum reported numbers in these papers.

PM methodPump/SH powerLength% W−1 cm−2%  W−1Absolute %
BPM type-I5925  mW/67  μW2 cm2.710.70.27
MPM type-067630  μW/140  nW2.35 mm650360.022
PPLN type-0823  mW/370  nW300  μm46004.140.012
PPLN type-088530  μW/2.7  μW5 mm3757939.250.5
PPLN type-0861.5  mW/9.4  μW4 mm26004160.6
PPLN type-0872.95  mW/31.6  μW4 mm22003521
PPLN type-0896  mW/550  μW20 mm32012809

2.1.5.

Periodic poling in microresonators

Combining highly efficient PPLN devices with the intensified light–matter interaction in resonant-based structures has led to a new front in nonlinear processes. In 2019, Chen et al.83 utilized a doubly resonant microcavity in a racetrack shape on X-cut MgO-doped TFLN and periodically poled the 300-μm-long straight waveguide on one arm to achieve a normalized conversion efficiency of 230,000%W1 with only 5.6  μW of pump power and a moderate Q-factor of 3.7×105. Lu et al.90 radially poled a doubly resonant microring resonator on a Z-cut TFLN and were able to demonstrate η=250,000%W1. This is while they employed d31 by using TE00 for the pump mode and TM00 for the SH mode due to the difficulty of poling, since the poling period of type-0 PM would have been almost three times smaller. By utilizing d33 in the type-0 configuration through overcoming the poling issues and by improving the Q-factor of resonators, the same group reached 5,000,000%W1 conversion efficiency at the low power regime with a pump power of 10  μW.84 As mentioned above, such very high efficiencies in %W1 are possible because the ratio P2/P12 would increase inversely with a decrease of the pump power for the same order of absolute power efficiency (see Table 3). Nonlinear optics at such low pump powers is a welcome development. However, as mentioned before, in most practical applications, the amount of the generated output power is more important and the absolute power efficiency, P2/P1 in %, is therefore a more relevant figure of merit.

Table 3

Comparison of resonant-based structures for SHG using different phase-matching methods.

StructurePM methodPump/SH powerQL at FW% W−1Absolute %
Microring60MPM type-0440  μW/2.9  μW1.4×10515000.65
Microring84PPLN type-01.05  μW/56  nW1.8×1065×1065.3
Microring90PPLN type-I55  μW/7.5  μW8×1052.5×10513.5
Racetrack83PPLN type-05.6  μW/73  nW3.7×1052.3×1051.3
Microdisk91CPM type-I10  mW/110  μW1.1×1051101.1
Microdisk16NQPM type-030  μW/4.2  μW7.5×1074.7×10514

With a high single-photon coupling rate of 1.2 MHz and a reasonably low dissipation rate of 184.6 MHz, the previously cited work84 reached a single-photon anharmonicity of 0.7%,84 which could find application in integrated quantum photonics.92,93 Periodically poled whispering-gallery resonators and microdisks are also demonstrated,85,94,95 but with much lower conversion efficiencies. Nonetheless, the developed poling techniques for microdisks using PFM are invaluable and pave the way for reaching poling periods below 100 nm95 [see Fig. 4(d)].

2.1.6.

Cyclic phase matching

The CPM method96 is used in microresonators on X- and Y-cut TFLN in a type-I configuration.91,97,98 Since the ordinary refractive index of LN is larger than the extraordinary value, the pump signal is polarized perpendicularly to the optical axis and hence holds a constant ordinary refractive index while the SH wave is in-plane and experiences an oscillating refractive index between the ordinary and extraordinary indices as it rotates around the resonator structure. Accordingly, the PM condition is met at four different azimuthal angles at each round. The normalized conversion efficiency for the CPM method has a record of only 110%W1.91 However, it benefits from wider PM bandwidths97 and does not require periodic poling.

In 2019, a method very similar to CPM, but in type-0 configurations, was demonstrated and was called natural QPM.62 Herein, the in-plane waves on X- or Y-cut TFLN undergo different effective nonlinear coefficients as they rotate around the resonator structure, which resembles the domain inversion and QPM without periodic poling. Using this method, a broad PM bandwidth with a normalized conversion efficiency of 9900%W1 was reported.62 Recently and partially due to a record high intrinsic Q of above 108, natural QPM with a conversion efficiency of 470,000%W1 was achieved in an ultrabroadband nonlinear device.16 Also, an absolute conversion efficiency of 23% was reported at a saturation pump power of 110  μW.

2.1.7.

Metasurfaces and photonic crystals

Phase-matching-free SHG is also possible using metasurface structures, which usually can operate over a wide range of wavelengths. This has been done, for example, by utilizing Mie-type resonant structures,63,99,100 optical anapole modes,101 and resonant waveguide gratings.102,103 Among these, one of the best performances so far (ηmax=1660%W1cm2) belongs to phased-array antennas forming a gradient metasurface, which provides a unidirectional wavevector and deprives the SH of converting back to the pump wavelength. A more detailed review on SHG using metasurface structures can be found elsewhere.104

Also, photonic crystals can be potentially very efficient in nonlinear processes due to their extremely small mode sizes and a strong light–matter interaction.105,106 However, they require an elaborate doubly resonant design to overcome their typical low Q-factors and external coupling at SH, which remains a challenging task.

2.1.8.

Summary and concluding remarks on SHG

Tables 2 and 3 summarize the performance of various devices for SHG using different phase-matching methods for straight waveguides and resonant-based structures, respectively. In these tables, maximum normalized conversion efficiencies along with the corresponding on-chip optical power at the fundamental and SH wavelengths and the absolute conversion efficiency are reported. The power values are mostly extracted from the related plots in these published works. It is noted that some of these studies reported higher absolute conversion efficiencies at the high-power regime, where SH and pump powers do not follow the quadratic relation anymore and hence the normalized conversion efficiency is lower. In straight waveguides, PPLN devices have demonstrated the best performance in all conversion efficiency units. In resonant-based structures, again PPLN devices have exhibited a superior performance. However, the best absolute conversion efficiency belongs to a microdisk working with the natural QPM method,16 which originates from the record-high loaded Q-factor of this resonator that is almost two orders of magnitude higher than the PPLN-based counterparts.

Comparing the two tables shows that conversion efficiencies reported in units of %W1 are mostly orders of magnitude larger for resonant-based structures. This notable difference is arising from the fact that straight waveguides are usually pumped at milliwatt levels, while resonant-based structures often work at microwatt levels. The absolute conversion efficiency is also higher in resonant-based structures. However, straight waveguides can handle very high powers, which can result in large absolute conversion efficiency values. For instance, an absolute conversion efficiency of 53% has been reported with 117 mW at SH when it was pumped with 220 mW in a MgO-doped TFLN waveguide.86 Generation of SH at such high power levels is desired for many applications. Moreover, from the practical perspective, straight waveguides are generally less sensitive to thermal, vibrational, and other environmental fluctuations and have higher fabrication yield compared with resonant-based structures, which are very sensitive to fabrication errors. Finally, most of the high-performance resonant structures were pumped with TM polarized light on a Z-cut TFLN to utilize d33, which can be a limiting factor for an ultimate integrated photonic chip, since semiconductor quantum-well lasers typically emit TE-polarized light and hence a polarization rotator is required for TM pumping.

2.2.

Other Three-Wave Mixing Processes in TFLN

Other second-order nonlinearities, such as SFG, DFG, optical parametric oscillation/amplification (OPO/OPA), and SPDC, have been demonstrated on TFLN. Moreover, various three-wave mixing processes have been cascaded on this platform and resulted in outstanding performances for processes such as low (third and fourth) harmonic generation. All these processes will be briefly reviewed in the following sections.

2.2.1.

Sum-frequency generation

The SFG process is very similar to SHG, in principle, with the ability to mix two distinct wavelengths, which makes it suitable for numerous applications. SFG can be used to generate light at frequency ranges where SHG cannot be utilized due to the lack of efficient lasers. It is also very common to use SFG for upconversion detection. For instance, low-power mid-infrared (mid-IR) light, down to a single-photon,107 can be converted to visible wavelengths and detected using low-noise and high-performance visible detectors. SFG on TFLN has been demonstrated on both straight waveguides82,108 and resonant-based structures.105,109,110

Our team demonstrated an SFG bandwidth of 20  nm in a TFLN PPLN device with a normalized conversion efficiency of 900%W1cm2 when one of the lasers was at a fixed wavelength and the other one was swept within its tuning range.82 In addition, swiping both lasers resulted in an SFG from 1460 to 1620 nm. In microdisk resonators, a conversion efficiency of 2.2×103  W1 is reported with a relatively low Q of 1.8×105 using the MPM method.110 Ideally, the conversion efficiencies four times larger than SHG should be achieved for SFG.111 Therefore, having state-of-the-art values for Q and utilizing natural QPM or PPLN—as the most efficient PM methods for resonators so far—can notably boost the efficiency of SFG.

SFG can be combined with other second-order nonlinear phenomena, such as SHG, to obtain highly efficient higher-order nonlinear processes through cascading,62,69,112115 which will be discussed later in a separate subsection. Moreover, SFG has been cascaded with the EO effect, which is in principle a second-order nonlinear process as well. This is very useful for low-power and high-speed control of an SFG.116

2.2.2.

Difference-frequency generation and parametric amplification and oscillation

DFG, OPA, and OPO share similar working principles. DFG has been extensively used for generating terahertz and mid-IR sources on other platforms.117,118 On the TFLN platform, DFG has been demonstrated using both straight waveguides40,119 and resonant-based structures.60 A new hybrid TFLN/Si platform is proposed by providing numerical simulation results to utilize DFG for terahertz generation,120 though it appears to be challenging to be realized from the fabrication perspective. Using periodically poled TFLN on sapphire—with a transparency window up to 4.5  μm—mid-infrared generation up to 3.66  μm with a DFG normalized conversion efficiency of 200%W1cm2 is demonstrated.119 Sapphire helps with circumventing the high absorption loss of the oxide layer at wavelengths longer than 2.5  μm.58,119 Cascaded SHG/DFG is used to demonstrate effective four-wave mixing on a microdisk on TFLN using MPM.70 In collaboration with Johns Hopkins University, we have utilized DFG in a TFLN PPLN device and spectral filtering to demonstrate an optical isolator concept based on nonlinear optics.40 The isolator has a wide bandwidth (>150  nm) with 40 dB transmittance difference between forward and backwardpropagating waves.

OPAs have been recently pursued on TFLN.121,122 On-chip amplification, combined with phenomenal properties of LN, opens the door wide open for applications in sensing, communications, and quantum information processing, among others. Recently, using dispersion engineered PPLN devices, Ledezma et al.123 reported on a phase-sensitive gain of 11.4 dB on a 2.5-mm-long device (45  dB/cm) with a pump pulse energy of 0.8 pJ. They also demonstrated optical parametric generation with a 110  dB/cm gain with <6  pJ of pump pulse energy and more than 600 nm gain bandwidth. Jankowski et al.124 circumvented the group-velocity dispersion and temporal walk-off effects via delicate dispersion engineering in a TFLN PPLN device and reported on a 118  dB/cm of unsaturated parametric gain over 1  μm of bandwidth with 4 pJ pulse energies. They also achieved a saturated gain of 146  dB/cm and a conversion efficiency of 15% for pulse energies above 10 pJ. These gain values are comparable with the state-of-the-art semiconductor optical amplifiers but with a much higher bandwidth that can potentially initiate numerous applications for TFLN.

OPOs can be utilized as a classical source for the generation of coherent radiations throughout a wide range of frequencies or as a nonclassical source for purposes such as quantum random number generation. Ultralow threshold (30  μW) integrated OPO devices are recently reported on the TFLN platform using a radially poled PPLN microring.125 This OPO is widely tunable through varying the temperature and the pump wavelength and showed an 11% conversion efficiency at a pump power of 93  μW.

2.2.3.

Spontaneous parametric downconversion

SPDC is a nonclassical three-wave mixing process in which a pump photon generates two entangled photons, i.e., signal and idler, at lower frequencies.126 For over three decades, SPDC has been used as a source in various quantum mechanical experiments, such as quantum cryptography127 and quantum teleportation,128 and it is usually more efficient than the third-order counterpart of spontaneous four-wave mixing.

TFLN is a propitious candidate for integrated quantum photonics. SPDC has been demonstrated on straight PPLN waveguides,87,129133 as well as on resonant-based structures.97,134 In collaboration with Northwestern University, our team has reported quantum-correlated photon pairs with a high coincidence-to-accidental ratio (CAR) of beyond 103 over 140 nm129 (on the same discussed PPLN devices with 300  μm lengths that exhibited an SHG efficiency of 4600%W1cm2).82 In another publication, we demonstrated correlated photon pairs using cascaded SHG and SPDC in a single 4-mm-long PPLN device.130 A comprehensive review of integrated quantum photonics on the TFLN platform can be found elsewhere.135

Over the past two years, several high-performance SPDC devices based on PPLN structures are demonstrated. Zhao et al.132 reported a CAR of 67,000 at a pair flux of 76 kHz and a CAR of 670 at a pair flux of 11.4 MHz for a 5-mm-long PPLN waveguide. A spectral brightness of 5.6×107Hznm1mW1, visibility of >99%, and heralded single-photon autocorrelation of gH(2)(0)<0.025 were measured for this device as well. Xue et al.131 showed an ultrahigh pair flux rate and a spectral brightness of 2.79×1011  HzmW1 and 1.53×109Hznm1mW1, respectively, on a 6-mm-long PPLN waveguide at the expense of a lower CAR value of about 600. This device possessed 160 nm of bandwidth and maximum visibility of 99%. Recently, Javid et al.133 demonstrated a record high bandwidth of 800 nm (100 THz) in a 5-mm-long dispersion engineered PPLN waveguide. A CAR of >150,000 at a pair flux of 176 kHz, a spectral brightness of 3.8×107  Hznm1mW1, and a visibility of 98.8% were reported for this device. Using a radially poled microring resonator on the TFLN platform, Ma et al.134 demonstrated pair fluxes of 36.3 and 8.5 MHz at pump powers as low as 13.4 and 3.4  μW, respectively. Also, a maximal CAR of 15,000 and a minimal gH(2)(0) of 0.008 were reported for this PPLN microring. These devices have already met or in some cases surpassed the performance of other materials, such as Si, SiN, AlN, and bulk LN. Therefore, a bright future is expected for quantum integrated photonics on TFLN.

2.2.4.

Cascading second-order nonlinear processes

Higher-order harmonics and wave mixing effects can occur by cascading χ(2) processes in a single or multiple TFLN devices. Furthermore, effective third-order nonlinearities can be realized through cascading χ(2) processes.136 This is specifically very intriguing for the TFLN platform since χ(2) of LN is much stronger than its other nonlinearities. Cascading χ(2) processes has been extensively studied on the TFLN platform to further improve the performance of other nonlinear processes.69,70,89,114,115,130,137139

There are several methods to achieve such cascading effects (see Fig. 5). A straightforward method is by placing two or more different periodically poled sections, each being responsible for a specific χ(2) process. For instance, our group demonstrated two devices (each with two cascaded PPLN sections) for low-harmonic generation, namely third- and fourth- harmonic generations (THG and FHG). For THG, the first PPLN segment was designed for SHG while the second PPLN was responsible for SFG, resulting in a cascaded SHG/SFG (ω+ω2ω/2ω+ω3ω). For FHG, both PPLN segments were poled for SHG, resulting in SHG/SHG (ω+ω2ω/2ω+2ω4ω).137 Another method is to have more than one period in a PPLN device and generate a wider range of k-vectors to compensate for different phase-mismatching required for various nonlinear processes. This has been done in a chirped PPLN straight waveguide, which resulted in illustration of high-harmonics up to the 13th harmonic.115 Also, a PPLN microdisk with a dual period was utilized for THG and FHG.95 In addition, it is possible to achieve cascading in a single PPLN waveguide for THG and FHG via pulse pumping and by slightly detuning the pump wavelength from the QPM wavelength.82,89,139 This latter method was used to demonstrate self-phase modulation with an effective nonlinear refractive index, i.e. n2,eff, that is almost 200 times larger than the intrinsic n2 of LN in a dispersion-engineered PPLN waveguide.139 The effective χeff(3) reported in this paper is larger than that of other well-known photonic Kerr-based platforms (such as Si and SiN) and proves the effectiveness of the cascading process. Moreover, in the first reported cascaded χ(2) for THG in a resonator, it was shown that natural BPM can be employed to observe both SHG and THG at higher values of pump power.69

Fig. 5

Some of the schemes used for implementing cascaded χ(2) processes in TFLN and the corresponding harmonic generations. (a) Two PPLN sections with different poling periods to enable SHG/SFG cascading for a THG device and SHG/SHG for an FHG device.137 (b) Dual-period PPLN microdisk with demonstrated THG and FHG.95 (c) THG and FHG on a single PPLN device via pulse pumping.82 (d) SHG and THG on a microdisk through cascaded SHG/SFG by taking advantage of the natural BPM.69

AP_4_3_034001_f005.png

2.3.

Applications of Second-Order Nonlinearity in Optical Frequency Combs

An optical frequency comb (OFC) consists of a large number of equidistant teeth in the optical spectra with potential applications in accurate optical clocks, optical communication, detection and ranging, spectroscopy, and sensing.140 TFLN in particular is a very attractive platform for OFCs since dispersion engineering is fairly easy on this platform, and it enables OFC generation through different processes, such as χ(3), cascaded χ(2), and the EO effect. Moreover, TFLN can leverage other phenomenal properties of LN to provide additional devices, such as self-referencing components, EO modulators, frequency converters, and filters to materialize a fully functional integrated chip for OFC generation.

The most common method for OFC generation is based on the Kerr effect, which is a third-order nonlinear process and will be discussed in Sec. 3.2. In another approach, OFC generation through only χ(2) processes is also possible and is called quadratic frequency combs. This can be done through an OPO cascaded with SHG/SFG or the other way around. In other words, quadratic frequency combs leverage LN’s large second-order nonlinear coefficients and can result in a lower threshold and higher efficiency compared with Kerr combs. Moreover, the frequency shifting nature of this process makes it possible to generate OFCs at the mid-IR or ultraviolet wavelengths using the commonly available visible and near-IR lasers. On-chip integration of f2f self-referencing is feasible as well. However, such combs have been mostly demonstrated on table-top systems.141 Recently, an on-chip quadratic frequency comb with a soliton state was illustrated in an AlN platform.142 Quadratic OFCs, operating in the modulation instability regime, have been reported on conventional LN chips using PPLN waveguides and a microresonator143147 [Fig. 6(a)]. This type of OFC has yet to be demonstrated on the TFLN platform.

Fig. 6

Using second-order nonlinear processes for generating OFCs on lithium niobate. (a) Quadratic frequency comb generation on conventional LN143 using cascaded χ(2) processes, which has yet to be demonstrated on the TFLN platform. (b) Electro-optic frequency comb generation in TFLN using coupled microring and racetrack resonators and the resulting spectrum exhibiting a high conversion efficiency.148

AP_4_3_034001_f006.png

EO combs are another alternative for OFC generation. Although EO is fundamentally a χ(2) nonlinear process, the EO combs are not regarded as a variant of the quadratic frequency combs discussed above, since their working principle is different. In the EO scheme, comb lines are formed by generating sidebands of the pump signal through phase modulation.149 To increase the number of lines, usually a resonator structure such as a Fabry–Pérot cavity150 or a microresonator151 is used in which the frequency of the applied RF signal matches an integer number of the resonator’s free-spectral range. The line spacings of these OFCs are tunable, and the spectral flatness compared with Kerr combs can be achieved on them by proper designs. However, due to the small frequency spacing compared with Kerr combs, EO combs have limited bandwidths. A review on the advancement of integrated EO combs on different platforms can be found elsewhere.152

On the TFLN platform and by proper dispersion engineering in a microresonator structure with Q1.5×106, Zhang et al.151 were able to expand the spectral span of an EO comb to 80 nm with a spectral slope of 1  dB/nm and a pump to comb conversion efficiency of 0.3%. The spectra comprised more than 900 comb lines with a repetition rate of 10.45  GHz. Recently, the same group used two coupled resonators that were critically coupled when applying the RF modulation signal and hence transferred the pump power much more efficiently into the microresonator.148 This new configuration resulted in conversion efficiency of 30% with a spectral span of 132 nm and a comb line spacing of 31  GHz [Fig. 6(b)]. In addition, it was shown that this EO comb, with such bandwidth and conversion efficiency, can be used as a high peak power ultrafast pulse source (336  fs pulse duration) for other on-chip nonlinear processes including Kerr comb generation.

3.

Third-Order Nonlinear Processes in TFLN

Although the third-order nonlinear coefficient of LN (1.6×1021  m2/V2) is not as exceptionally high as its second-order coefficient compared with other materials, it is still very large and comparable to SiN, which is a popular choice for third-order nonlinear applications. Utilizing LN χ(3) coefficients, combined with the recently achieved ultralow propagation loss and compact mode sizes of TFLN, makes the platform appealing for high-performance third-order nonlinear devices.

Among several well-known third-order nonlinear interactions, e.g., four-wave mixing,153 stimulated Brillouin scattering,154 and Raman processes,155 some have been demonstrated on the TFLN platform.30,156 However, due to the limited space, this work only covers supercontinuum generation (SCG) and Kerr effect in resonant structures, with an emphasis on their applications in OFCs.

3.1.

Supercontinuum Generation

SCG is a nonlinear process where an ultrashort pulse with enough intensity experiences spectral broadening after propagating a certain distance through a third-order nonlinear medium.140 SCG typically requires anomalous group velocity dispersion (GVD). However, it can be also achieved in the marginally normal GVD regime at the expense of higher pulse powers.157 Spectral broadening of more than one octave is particularly useful for OFCs, since the wide spectrum allows stabilization of the carrier-envelope offset (CEO) frequency, fCEO, through the f2f self-referencing method. SCG on integrated platforms benefits from ease of dispersion engineering and compact waveguide sizes and hence operates at lower energies. TFLN is a great platform for SCG as it offers a strong χ(2) nonlinearity in addition to the required χ(3), hence enables on-chip f2f self-referencing158 [Fig. 7(c)].

Fig. 7

SCG on the TFLN platform. (a) SCG spanning over two octaves in a dispersion engineered straight waveguide without poling.159 (b) SCG on a periodically poled straight waveguide with a span of more than two octaves at a pulse energy of 11  pJ.139 (c) Using cascaded SCG and SHG for on-chip f2f self-referencing, which is of great importance for realization of on-chip OFCs.158

AP_4_3_034001_f007.png

Lu et al.160 demonstrated SCG with 1.5 octaves of bandwidth using 800 pJ of pulse energy in a 10-mm-long Z-cut TFLN waveguide. In another work, 2.58 octaves of bandwidth using a pulse energy of 185 pJ was achieved in a 5-mm-long waveguide on an X-cut TFLN159 [Fig. 7(a)]. In addition to SCG, SHG and SFG were observed in this study, which were attributed to MPM at higher-order spatial modes. With the SCG spectrum overlapping with that of SHG, the fCEO beat-note was directly detected with a 30-dB signal-to-noise ratio (SNR). Jankowski et al.139 used a 6-mm-long PPLN waveguide to take advantage of cascaded χ(2) processes and achieved more than two orders of magnitude improvement in self-phase modulation compared with that of Kerr nonlinearities. This resulted in an SCG with >2.5 octaves span at only 11  pJ of pulse energy. To confirm the coherency of the SCG, they measured the fCEO beat-note with an SNR of 35 dB.

3.2.

Kerr Effect in Microresonators for Optical Frequency Comb Generation

Soliton OFCs can be generated over a wide bandwidth in microresonator structures with anomalous dispersion and by relying on the Kerr (χ(3)) nonlinearity. Using these combs, as the conceptual schematic in Fig. 8(a) suggests, versatile properties of TFLN can be utilized for the realization of fully integrated soliton combs on a single chip with providing all the necessary components.161 He et al.161 demonstrated soliton microcombs with a comb teeth spacing of 200  GHz over a >200  nm spanning range around λ=1550  nm in a Z-cut microring resonator with a Q of 2.2×106. They also showed that the photorefractive effect of LN (which acts in the opposite direction of the thermo-optic effect) permits the soliton mode-locking process to self-start and, more importantly, makes switching between the soliton states possible through both up- and downtuning of the laser frequency. In a very similar work, operating around λ=2  μm to reduce the impact of stimulated Raman scattering (SRS) on Kerr comb generation, Gong et al.164 illustrated a line spacing of 200  GHz over a span of 300  nm. Wang et al.165 made an integrated chip with filters and modulators to manipulate the output of the generated OFC. They designed a microring resonator capable of supporting both TE and TM polarizations with anomalous dispersion for both cases and reported on OFC generation spanning over 700 and 300 nm for TE and TM polarizations, respectively, with 250  GHz spacing. However, the soliton state was not achieved, and the generated combs were attributed to modulation instability due to the Raman effect. Therefore, the strong Raman effect needs to be circumvented to have frequency combs in soliton states. Gong et al.162 accomplished this goal by increasing the threshold energy for SRS to more than that of the soliton through a delicate design of the external coupling rate with respect to the intrinsic decay rate. As a result, soliton frequency combs spanning over 4/5 octaves, with a spacing of 335  GHz, were demonstrated [see Fig. 8(b)]. Pushing the span over an octave enables highly desired f2f self-referencing for this type of OFCs on the TFLN platform. It should be noted that the conversion efficiency from pump to comb lines is currently low for practical applications and further improvements are required for on-chip Kerr combs. The same group recently demonstrated a cascaded Kerr and EO comb, where the EO comb lines with much lower repetition rates filled the gap between Kerr soliton combs [Figs. 8(c) and 8(d)].163 In addition, this could facilitate the stabilization of Kerr combs.

Fig. 8

OFC generation in TFLN using the Kerr effect. (a) Conceptual schematic of a fully integrated soliton comb system in TFLN with all the required functionalities.161 (b) Soliton Kerr comb generation spanning near one octave.162 (c) Cascaded Kerr and EO combs with green lines corresponding to Kerr comb lines spanning over 200 nm.163 (d) Zoomed in spectra of the cascaded Kerr and EO combs demonstrating that EO combs with much lower repetition rates fill the gap between Kerr combs.163

AP_4_3_034001_f008.png

4.

Conclusions and Outlook

Some of the initial research studies and recent developments in nonlinear photonics on the TFLN platform were reviewed. The improvements are magnificent for such a relatively short period of time, reaching or surpassing the performance of prior platforms for nonlinear applications. Despite outstanding demonstrated performances, this platform is still in its early years of development and will have a lot more to offer in the future.

There is plenty of room left for improvement of the TFLN platform before it becomes a fully functional integrated photonic platform. Fabrication needs to ultimately reach a point that reproducible, high-yield, and wafer-scale processing can be accomplished in foundries, while pushing the propagation losses down to the material absorption limit.

There are more essential photonic components that must be incorporated to the platform either monolithically or through heterogeneous integration. As mentioned before, progress has been made in heterogeneously integrated semiconductor lasers in TFLN.32,33 Similar methods could be adopted for integration of semiconductor photodetectors on this platform. Other examples include cointegration of second- and third-order materials. As discussed, LN has a relatively high third-order Kerr optical susceptibility. But in some applications, such as OFCs, it is still sensible to utilize other materials—such as SiN or chalcogenide glass—that may be advantageous in terms of nonlinear coefficient, optical loss, dispersion management, cost, compatibility with silicon foundry fabrication, etc. To this end, our team and collaborators have made progress in heterogeneous integration of TFLN and chalcogenide glass waveguides on the same silicon substrates.166,167

Furthermore, besides improving the performance of devices based on different optical and other functionalities (e.g., EO, second- and third-order nonlinearities and piezoelectricity), all of them may need to be integrated on the same chip to fully utilize the capabilities of this versatile platform.

A lot of further milestones can be accomplished for nonlinear photonics on TFLN. Material properties, such as the photorefractive effect, need to be more accurately studied. For second-order nonlinearities, QPM using periodic poling still appears to be the most efficient method. The poling process can be perfected and standardized at the foundry level to achieve high-yield and high-performance PPLN devices with <100  nm poling periods. Such small poling periods compensate for large phase mismatches, which can be very functional especially for counterpropagating QPM processes. With the reported performances for PPLN microring devices and considering their small footprint and low power consumption, they could be promising devices for χ(2) processes in certain applications. However, one caveat for PPLN microrings is that the most efficient devices are made on Z-cut TFLN and operate in the TM polarization, which may not be the best option for ultimate fully integrated chips since the output of semiconductor lasers is usually TE-polarized, thus on-chip TE-to-TM polarization rotators will be required. Nonetheless, passive on-chip TM-to-TE polarization rotators168 and polarization rotator-splitters169,170 have been recently reported in TFLN. It is expected that reliable, low-loss, and high extinction ratio passive TE-to-TM polarization rotators will be demonstrated in the platform in the future. Furthermore, and as mentioned before, straight-waveguide PPLNs can typically handle higher powers and are more tolerant to fabrication errors and environmental fluctuations.

On-chip amplification in TFLN has been accomplished using heterogeneously integrated semiconductor optical amplifiers,32 Er-doped amplifiers,171173 and OPAs.123,124 Cascaded χ(2) processes are anticipated to be much more sophisticated that can be used for efficient frequency conversion in the ultraviolet and mid-IR wavelength ranges as well as generating broadband OFC and SCG sources. The current high demand for OFCs, along with the miniaturization and robustness that comes with integrated OFC on the TFLN platform, will push the limits for this type of devices to have higher conversion efficiencies and SNR with self-referencing incorporated in them. Also, EO devices are envisioned to be effectively integrated with all types of nonlinear devices for fast tuning or high-speed modulation.

Finally, considering the current progress in the efficiency of nonlinear processes, especially second-order effects, it is expected to achieve very high absolute conversion efficiencies in the future. Reaching large values in absolute efficiency will be a major step forward for integrated nonlinear photonics and its applications. Integrated quantum photonics will be severely pursued at that point since nonlinearity at the single photon level will be accessible.

In summary, TFLN has emerged as a mature platform for integrated photonics on a ferro-electric material with high second- and third-order nonlinearity. The high-contrast and low-loss waveguides on TFLN make them ideal for realization of compact nonlinear devices operating at low powers compared with conventional waveguides on the same material or on other materials. Several applications, such as optical spectroscopy, wavelength conversion for light generation at inconvenient wavelengths, digital optical synthesizers, and quantum optics, can be realized using the discussed efficient nonlinear devices and circuits on TFLN.

Acknowledgments

Some of the results by the authors’ group were funded by Office of Naval Research (N000141712409); Division of Emerging Frontiers in Research and Innovation (1741694) and under the Defense Advanced Research Project Agency (DARPA) DODOS project, Grant No. HR0011-15-C-0057. The views, opinions, and/or findings expressed are those of the authors and should not be interpreted as representing the official views or policies of the Department of Defense or the U.S. Government. The authors have no conflicts of interest to disclose.

References

1. 

N. Uesugi and T. Kimura, “Efficient second-harmonic generation in three-dimensional LiNbO3 optical waveguide,” Appl. Phys. Lett., 29 (9), 572 –574 (1976). https://doi.org/10.1063/1.89191 APPLAB 0003-6951 Google Scholar

2. 

R. Schmidt and I. Kaminow, “Metal-diffused optical waveguides in LiNbO3,” Appl. Phys. Lett., 25 (8), 458 –460 (1974). https://doi.org/10.1063/1.1655547 APPLAB 0003-6951 Google Scholar

3. 

J. L. Jackel, C. Rice and J. Veselka, “Proton exchange for high-index waveguides in LiNbO3,” Appl. Phys. Lett., 41 (7), 607 –608 (1982). https://doi.org/10.1063/1.93615 APPLAB 0003-6951 Google Scholar

4. 

P. Rabiei et al., “Heterogeneous lithium niobate photonics on silicon substrates,” Opt. Express, 21 (21), 25573 –25581 (2013). https://doi.org/10.1364/OE.21.025573 OPEXFF 1094-4087 Google Scholar

8. 

Y. Kong et al., “Recent progress in lithium niobate: optical damage, defect simulation, and on-chip devices,” Adv. Mater., 32 (3), 1806452 (2020). https://doi.org/10.1002/adma.201806452 ADVMEW 0935-9648 Google Scholar

9. 

Y. Xu et al., “Mitigating photorefractive effect in thin-film lithium niobate microring resonators,” Opt. Express, 29 (4), 5497 –5504 (2021). https://doi.org/10.1364/OE.418877 OPEXFF 1094-4087 Google Scholar

10. 

A. L. Kozub et al., “Polaronic enhancement of second-harmonic generation in lithium niobate,” Phys. Rev. B, 104 (17), 174110 (2021). https://doi.org/10.1103/PhysRevB.104.174110 Google Scholar

11. 

M. Boukhtouta et al., “Predictions on structural, electronic, optical and thermal properties of lithium niobate via first-principle computations,” Philos. Mag., 100 (9), 1150 –1171 (2020). https://doi.org/10.1080/14786435.2020.1719286 Google Scholar

12. 

A. Rao et al., “Heterogeneous microring and Mach-Zehnder modulators based on lithium niobate and chalcogenide glasses on silicon,” Opt. Express, 23 (17), 22746 –22752 (2015). https://doi.org/10.1364/OE.23.022746 OPEXFF 1094-4087 Google Scholar

13. 

A. Rao et al., “Second-harmonic generation in periodically-poled thin film lithium niobate wafer-bonded on silicon,” Opt. Express, 24 (26), 29941 –29947 (2016). https://doi.org/10.1364/OE.24.029941 OPEXFF 1094-4087 Google Scholar

14. 

A. Honardoost et al., “Towards subterahertz bandwidth ultracompact lithium niobate electrooptic modulators,” Opt. Express, 27 (5), 6495 –6501 (2019). https://doi.org/10.1364/OE.27.006495 OPEXFF 1094-4087 Google Scholar

15. 

M. Zhang et al., “Monolithic ultra-high-Q lithium niobate microring resonator,” Optica, 4 (12), 1536 –1537 (2017). https://doi.org/10.1364/OPTICA.4.001536 Google Scholar

16. 

R. Gao et al., “Broadband highly efficient nonlinear optical processes in on-chip integrated lithium niobate microdisk resonators of Q-factor above 108,” New J. Phys., 23 (12), 123027 (2021). https://doi.org/10.1088/1367-2630/ac3d52 NJOPFM 1367-2630 Google Scholar

17. 

K. Luke et al., “Wafer-scale low-loss lithium niobate photonic integrated circuits,” Opt. Express, 28 (17), 24452 –24458 (2020). https://doi.org/10.1364/OE.401959 OPEXFF 1094-4087 Google Scholar

18. 

J. Lin et al., “Advances in on-chip photonic devices based on lithium niobate on insulator,” Photonics Res., 8 (12), 1910 –1936 (2020). https://doi.org/10.1364/PRJ.395305 Google Scholar

19. 

Y. Jia, L. Wang and F. Chen, “Ion-cut lithium niobate on insulator technology: recent advances and perspectives,” Appl. Phys. Rev., 8 (1), 011307 (2021). https://doi.org/10.1063/5.0037771 Google Scholar

20. 

D. Sun et al., “Microstructure and domain engineering of lithium niobate crystal films for integrated photonic applications,” Light: Sci. Appl., 9 (1), 197 (2020). https://doi.org/10.1038/s41377-019-0231-1 Google Scholar

21. 

Y. Jiao et al., “Improvement on thermal stability of nano-domains in lithium niobate thin films,” Crystals, 10 (2), 74 (2020). https://doi.org/10.3390/cryst10020074 CRYSBC 2073-4352 Google Scholar

22. 

M. Younesi et al., “Periodic poling with a micrometer-range period in thin-film lithium niobate on insulator,” J. Opt. Soc. Am. B, 38 (3), 685 –691 (2021). https://doi.org/10.1364/JOSAB.414298 JOBPDE 0740-3224 Google Scholar

23. 

B. J. Stanicki et al., “Surface domain engineering in lithium niobate,” OSA Contin., 3 (2), 345 –358 (2020). https://doi.org/10.1364/OSAC.387717 Google Scholar

24. 

Y. Liu et al., “On-chip erbium-doped lithium niobate microcavity laser,” Sci. China Phys. Mech. Astron., 64 (3), 234262 (2021). https://doi.org/10.1007/s11433-020-1625-9 SCPMCL 1674-7348 Google Scholar

25. 

R. Gao et al., “On-chip ultra-narrow-linewidth single-mode microlaser on lithium niobate on insulator,” Opt. Lett., 46 (13), 3131 –3134 (2021). https://doi.org/10.1364/OL.430015 OPLEDP 0146-9592 Google Scholar

26. 

Q. Luo et al., “On-chip erbium-doped lithium niobate microring lasers,” Opt. Lett., 46 (13), 3275 –3278 (2021). https://doi.org/10.1364/OL.425178 OPLEDP 0146-9592 Google Scholar

27. 

X. Liu et al., “Tunable single-mode laser on thin film lithium niobate,” Opt. Lett., 46 (21), 5505 –5508 (2021). https://doi.org/10.1364/OL.441167 OPLEDP 0146-9592 Google Scholar

28. 

D. Yin et al., “Electro-optically tunable microring laser monolithically integrated on lithium niobate on insulator,” Opt. Lett., 46 (9), 2127 –2130 (2021). https://doi.org/10.1364/OL.424996 OPLEDP 0146-9592 Google Scholar

29. 

R. Zhang et al., “Integrated lithium niobate single-mode lasers by the Vernier effect,” Sci. China Phys. Mech. Astron., 64 (9), 294216 (2021). https://doi.org/10.1007/s11433-021-1749-x Google Scholar

30. 

M. Yu et al., “Raman lasing and soliton mode-locking in lithium niobate microresonators,” Light: Sci. Appl., 9 (1), 9 (2020). https://doi.org/10.1038/s41377-019-0231-1 Google Scholar

31. 

D. Zhu et al., “Integrated photonics on thin-film lithium niobate,” Adv. Opt. Photonics, 13 (2), 242 –352 (2021). https://doi.org/10.1364/AOP.411024 AOPAC7 1943-8206 Google Scholar

32. 

C. O. de Beeck et al., “III/V-on-lithium niobate amplifiers and lasers,” Optica, 8 (10), 1288 –1289 (2021). https://doi.org/10.1364/OPTICA.438620 Google Scholar

33. 

A. Shams-Ansari et al., “Electrically pumped laser transmitter integrated on thin-film lithium niobate,” Optica, 9 (4), 408 –411 (2022). https://doi.org/10.1364/OPTICA.448617 Google Scholar

34. 

A. Honardoost, K. Abdelsalam and S. Fathpour, “Rejuvenating a versatile photonic material: thin-film lithium niobate,” Laser Photonics Rev., 14 (9), 2000088 (2020). https://doi.org/10.1002/lpor.202000088 Google Scholar

35. 

Y. Qi and Y. Li, “Integrated lithium niobate photonics,” Nanophotonics, 9 (6), 1287 –1320 (2020). https://doi.org/10.1515/nanoph-2020-0013 Google Scholar

36. 

M. Xu et al., “Dual-polarization thin-film lithium niobate in-phase quadrature modulators for terabit-per-second transmission,” Optica, 9 (1), 61 –62 (2022). https://doi.org/10.1364/OPTICA.449691 Google Scholar

37. 

F. Arab Juneghani et al., “Demonstration of non-symmetric thin-film lithium niobate modulator with a 3-dB bandwidth beyond 100 GHz,” in CLEO: Sci. and Innov., (2022). Google Scholar

38. 

C. Hu et al., “High-efficient coupler for thin-film lithium niobate waveguide devices,” Opt. Express, 29 (4), 5397 –5406 (2021). https://doi.org/10.1364/OE.416492 OPEXFF 1094-4087 Google Scholar

39. 

K. Abdelsalam et al., “Tunable dual-channel ultra-narrowband Bragg grating filter on thin-film lithium niobate,” Opt. Lett., 46 (11), 2730 –2733 (2021). https://doi.org/10.1364/OL.427101 OPLEDP 0146-9592 Google Scholar

40. 

K. Abdelsalam et al., “Linear isolators using wavelength conversion,” Optica, 7 (3), 209 –213 (2020). https://doi.org/10.1364/OPTICA.385639 Google Scholar

41. 

X. Ye et al., “High-speed programmable lithium niobate thin film spatial light modulator,” Opt. Lett., 46 (5), 1037 –1040 (2021). https://doi.org/10.1364/OL.419623 OPLEDP 0146-9592 Google Scholar

42. 

P. Franken et al., “Generation of optical harmonics,” Phys. Rev. Lett., 7 (4), 118 –119 (1961). https://doi.org/10.1103/PhysRevLett.7.118 PRLTAO 0031-9007 Google Scholar

43. 

R. W. Boyd, Nonlinear Optics, Academic Press(2020). Google Scholar

44. 

A. Rao and S. Fathpour, “Second-harmonic generation in integrated photonics on silicon,” Phys. Status Solidi A, 215 (4), 1700684 (2018). https://doi.org/10.1002/pssa.201700684 Google Scholar

45. 

A. Rao and S. Fathpour, “Heterogeneous thin-film lithium niobate integrated photonics for electrooptics and nonlinear optics,” IEEE J. Sel. Top. Quantum Electron., 24 (6), 8200912 (2018). https://doi.org/10.1109/JSTQE.2018.2836939 IJSQEN 1077-260X Google Scholar

46. 

S. Fathpour, “Heterogeneous nonlinear integrated photonics,” IEEE J. Quantum Electron., 54 (6), 6300776 (2018). https://doi.org/10.1109/JQE.2018.2876903 IEJQA7 0018-9197 Google Scholar

47. 

W. H. P. Pernice et al., “Second harmonic generation in phase matched aluminum nitride waveguides and micro-ring resonators,” Appl. Phys. Lett., 100 (22), 223501 (2012). https://doi.org/10.1063/1.4722941 APPLAB 0003-6951 Google Scholar

48. 

S. May et al., “Second-harmonic generation in AlGaAs-on-insulator waveguides,” Opt. Lett., 44 (6), 1339 –1342 (2019). https://doi.org/10.1364/OL.44.001339 OPLEDP 0146-9592 Google Scholar

49. 

L. Chang et al., “Heterogeneously integrated GaAs waveguides on insulator for efficient frequency conversion,” Laser Photonics Rev., 12 (10), 1800149 (2018). https://doi.org/10.1002/lpor.201800149 Google Scholar

50. 

C. Xiong et al., “Integrated GaN photonic circuits on silicon (100) for second harmonic generation,” Opt. Express, 19 (11), 10462 –10470 (2011). https://doi.org/10.1364/OE.19.010462 OPEXFF 1094-4087 Google Scholar

51. 

D. N. Nikogosyan, Nonlinear Optical Crystals: A Complete Survey, Springer Science & Business Media(2006). Google Scholar

52. 

N. Li et al., “Aluminium nitride integrated photonics: a review,” Nanophotonics, 10 2347 –2387 (2021). https://doi.org/10.1515/nanoph-2021-0130 Google Scholar

53. 

H. Zhang et al., “Study of nonlinear optical effects in GaN: Mg epitaxial film,” Appl. Phys. Lett., 69 (20), 2953 –2955 (1996). https://doi.org/10.1063/1.117741 APPLAB 0003-6951 Google Scholar

54. 

J. Webjorn, F. Laurell and G. Arvidsson, “Fabrication of periodically domain-inverted channel waveguides in lithium niobate for second harmonic generation,” J. Lightwave Technol., 7 (10), 1597 –1600 (1989). https://doi.org/10.1109/50.39103 JLTEDG 0733-8724 Google Scholar

55. 

E. Lim, M. Fejer and R. Byer, “Second-harmonic generation of green light in periodically poled planar lithium niobate waveguide,” Electron. Lett., 25 (3), 174 –175 (1989). https://doi.org/10.1049/el:19890127 ELLEAK 0013-5194 Google Scholar

56. 

L. E. Myers et al., “Multigrating quasi-phase-matched optical parametric oscillator in periodically poled LiNbO3,” Opt. Lett., 21 (8), 591 –593 (1996). https://doi.org/10.1364/OL.21.000591 OPLEDP 0146-9592 Google Scholar

57. 

G. Miller et al., “42%-efficient single-pass CW second-harmonic generation in periodically poled lithium niobate,” Opt. Lett., 22 (24), 1834 –1836 (1997). https://doi.org/10.1364/OL.22.001834 OPLEDP 0146-9592 Google Scholar

58. 

S. Fathpour, “Emerging heterogeneous integrated photonic platforms on silicon,” Nanophotonics, 4 (1), 143 –164 (2015). https://doi.org/10.1515/nanoph-2014-0024 Google Scholar

59. 

C. Lu et al., “Highly tunable birefringent phase-matched second-harmonic generation in an angle-cut lithium niobate-on-insulator ridge waveguide,” Opt. Lett., 47 (5), 1081 –1084 (2022). https://doi.org/10.1364/OL.449634 OPLEDP 0146-9592 Google Scholar

60. 

R. Luo et al., “Optical parametric generation in a lithium niobate microring with modal phase matching,” Phys. Rev. Appl., 11 (3), 034026 (2019). https://doi.org/10.1103/PhysRevApplied.11.034026 PRAHB2 2331-7019 Google Scholar

61. 

A. Rao et al., “Second-harmonic generation in single-mode integrated waveguides based on mode-shape modulation,” Appl. Phys. Lett., 110 (11), 111109 (2017). https://doi.org/10.1063/1.4978696 APPLAB 0003-6951 Google Scholar

62. 

J. Lin et al., “Broadband quasi-phase-matched harmonic generation in an on-chip monocrystalline lithium niobate microdisk resonator,” Phys. Rev. Lett., 122 (17), 173903 (2019). https://doi.org/10.1103/PhysRevLett.122.173903 PRLTAO 0031-9007 Google Scholar

63. 

C. Wang et al., “Metasurface-assisted phase-matching-free second harmonic generation in lithium niobate waveguides,” Nat. Commun., 8 (1), 2098 (2017). https://doi.org/10.1038/s41467-017-02189-6 NCAOBW 2041-1723 Google Scholar

64. 

C. Wang et al., “Second harmonic generation in nano-structured thin-film lithium niobate waveguides,” Opt. Express, 25 (6), 6963 –6973 (2017). https://doi.org/10.1364/OE.25.006963 OPEXFF 1094-4087 Google Scholar

65. 

R. Luo et al., “Highly tunable efficient second-harmonic generation in a lithium niobate nanophotonic waveguide,” Optica, 5 (8), 1006 –1011 (2018). https://doi.org/10.1364/OPTICA.5.001006 Google Scholar

66. 

J.-Y. Chen et al., “Modal phase matched lithium niobate nanocircuits for integrated nonlinear photonics,” OSA Contin., 1 (1), 229 –242 (2018). https://doi.org/10.1364/OSAC.1.000229 Google Scholar

67. 

R. Luo et al., “Semi-nonlinear nanophotonic waveguides for highly efficient second-harmonic generation,” Laser Photonics Rev., 13 (3), 1800288 (2019). https://doi.org/10.1002/lpor.201800288 Google Scholar

68. 

C. Wang et al., “Integrated high quality factor lithium niobate microdisk resonators,” Opt. Express, 22 (25), 30924 –30933 (2014). https://doi.org/10.1364/OE.22.030924 OPEXFF 1094-4087 Google Scholar

69. 

S. Liu, Y. Zheng and X. Chen, “Cascading second-order nonlinear processes in a lithium niobate-on-insulator microdisk,” Opt. Lett., 42 (18), 3626 –3629 (2017). https://doi.org/10.1364/OL.42.003626 OPLEDP 0146-9592 Google Scholar

70. 

S. Liu et al., “Effective four-wave mixing in the lithium niobate on insulator microdisk by cascading quadratic processes,” Opt. Lett., 44 (6), 1456 –1459 (2019). https://doi.org/10.1364/OL.44.001456 OPLEDP 0146-9592 Google Scholar

71. 

E. Lim et al., “Blue light generation by frequency doubling in periodically poled lithium niobate channel waveguide,” Electron. Lett., 25 (11), 731 –732 (1989). https://doi.org/10.1049/el:19890495 ELLEAK 0013-5194 Google Scholar

72. 

L. E. Myers et al., “Quasi-phase-matched optical parametric oscillators in bulk periodically poled LiNbO3,” J. Opt. Soc. Am. B, 12 (11), 2102 –2116 (1995). https://doi.org/10.1364/JOSAB.12.002102 JOBPDE 0740-3224 Google Scholar

73. 

L. Chang et al., “Thin film wavelength converters for photonic integrated circuits,” Optica, 3 (5), 531 –535 (2016). https://doi.org/10.1364/OPTICA.3.000531 Google Scholar

74. 

J. T. Nagy and R. M. Reano, “Reducing leakage current during periodic poling of ion-sliced x-cut MgO doped lithium niobate thin films,” Opt. Mater. Express, 9 (7), 3146 –3155 (2019). https://doi.org/10.1364/OME.9.003146 Google Scholar

75. 

A. Boes et al., “Efficient second harmonic generation in lithium niobate on insulator waveguides and its pitfalls,” J. Phys.: Photonics, 3 (1), 012008 (2021). https://doi.org/10.1088/2515-7647/abd23a Google Scholar

76. 

J. Zhao et al., “Poling thin-film x-cut lithium niobate for quasi-phase matching with sub-micrometer periodicity,” J. Appl. Phys., 127 (19), 193104 (2020). https://doi.org/10.1063/1.5143266 JAPIAU 0021-8979 Google Scholar

77. 

B. Slautin et al., “Domain structure formation by local switching in the ion sliced lithium niobate thin films,” Appl. Phys. Lett., 116 (15), 152904 (2020). https://doi.org/10.1063/5.0005969 APPLAB 0003-6951 Google Scholar

78. 

J. T. Nagy and R. M. Reano, “Submicrometer periodic poling of lithium niobate thin films with bipolar preconditioning pulses,” Opt. Mater. Express, 10 (8), 1911 –1920 (2020). https://doi.org/10.1364/OME.394724 Google Scholar

79. 

S. Reitzig et al., ““Seeing is believing”—in-depth analysis by co-imaging of periodically-poled x-cut lithium niobate thin films,” Crystals, 11 (3), 288 (2021). https://doi.org/10.3390/cryst11030288 CRYSBC 2073-4352 Google Scholar

80. 

R. K. Prasath et al., “Measurement of the internal electric field in periodically poled congruent lithium niobate crystals by far-field diffraction,” Appl. Opt., 60 (13), 3791 –3796 (2021). https://doi.org/10.1364/AO.421735 APOPAI 0003-6935 Google Scholar

81. 

A. Boes et al., “Improved second harmonic performance in periodically poled LNOI waveguides through engineering of lateral leakage,” Opt. Express, 27 (17), 23919 –23928 (2019). https://doi.org/10.1364/OE.27.023919 OPEXFF 1094-4087 Google Scholar

82. 

A. Rao et al., “Actively-monitored periodic-poling in thin-film lithium niobate photonic waveguides with ultrahigh nonlinear conversion efficiency of 4600%W1cm2,” Opt. Express, 27 (18), 25920 –25930 (2019). https://doi.org/10.1364/OE.27.025920 OPEXFF 1094-4087 Google Scholar

83. 

J.-Y. Chen et al., “Ultra-efficient frequency conversion in quasi-phase-matched lithium niobate microrings,” Optica, 6 (9), 1244 –1245 (2019). https://doi.org/10.1364/OPTICA.6.001244 Google Scholar

84. 

J. Lu et al., “Toward 1% single-photon anharmonicity with periodically poled lithium niobate microring resonators,” Optica, 7 (12), 1654 –1659 (2020). https://doi.org/10.1364/OPTICA.403931 Google Scholar

85. 

Z. Hao et al., “Second-harmonic generation using d33 in periodically poled lithium niobate microdisk resonators,” Photonics Res., 8 (3), 311 –317 (2020). https://doi.org/10.1364/PRJ.382535 Google Scholar

86. 

C. Wang et al., “Ultrahigh-efficiency wavelength conversion in nanophotonic periodically poled lithium niobate waveguides,” Optica, 5 (11), 1438 –1441 (2018). https://doi.org/10.1364/OPTICA.5.001438 Google Scholar

87. 

J.-Y. Chen et al., “Efficient parametric frequency conversion in lithium niobate nanophotonic chips,” OSA Contin., 2 (10), 2914 –2924 (2019). https://doi.org/10.1364/OSAC.2.002914 Google Scholar

88. 

J. Zhao et al., “Shallow-etched thin-film lithium niobate waveguides for highly-efficient second-harmonic generation,” Opt. Express, 28 (13), 19669 –19682 (2020). https://doi.org/10.1364/OE.395545 OPEXFF 1094-4087 Google Scholar

89. 

C. Lu et al., “Second and cascaded harmonic generation of pulsed laser in a lithium niobate on insulator ridge waveguide,” Opt. Express, 30 (2), 1381 –1387 (2022). https://doi.org/10.1364/OE.447958 OPEXFF 1094-4087 Google Scholar

90. 

J. Lu et al., “Periodically poled thin-film lithium niobate microring resonators with a second-harmonic generation efficiency of 250,000%/W,” Optica, 6 (12), 1455 –1460 (2019). https://doi.org/10.1364/OPTICA.6.001455 Google Scholar

91. 

J. Lin et al., “Phase-matched second-harmonic generation in an on-chip LiNbO3 microresonator,” Phys. Rev. Appl., 6 (1), 014002 (2016). https://doi.org/10.1103/PhysRevApplied.6.014002 PRAHB2 2331-7019 Google Scholar

92. 

M. Li et al., “Photon-photon quantum phase gate in a photonic molecule with χ(2) nonlinearity,” Phys. Rev. Appl., 13 (4), 044013 (2020). https://doi.org/10.1103/PhysRevApplied.13.044013 PRAHB2 2331-7019 Google Scholar

93. 

M. Heuck, K. Jacobs and D. R. Englund, “Controlled-phase gate using dynamically coupled cavities and optical nonlinearities,” Phys. Rev. Lett., 124 (16), 160501 (2020). https://doi.org/10.1103/PhysRevLett.124.160501 PRLTAO 0031-9007 Google Scholar

94. 

R. Wolf et al., “Quasi-phase-matched nonlinear optical frequency conversion in on-chip whispering galleries,” Optica, 5 (7), 872 –875 (2018). https://doi.org/10.1364/OPTICA.5.000872 Google Scholar

95. 

L. Zhang et al., “Dual-periodically poled lithium niobate microcavities supporting multiple coupled parametric processes,” Opt. Lett., 45 (12), 3353 –3356 (2020). https://doi.org/10.1364/OL.393244 OPLEDP 0146-9592 Google Scholar

96. 

G. Lin et al., “Wide-range cyclic phase matching and second harmonic generation in whispering gallery resonators,” Appl. Phys. Lett., 103 (18), 181107 (2013). https://doi.org/10.1063/1.4827538 APPLAB 0003-6951 Google Scholar

97. 

R. Luo et al., “On-chip second-harmonic generation and broadband parametric down-conversion in a lithium niobate microresonator,” Opt. Express, 25 (20), 24531 –24539 (2017). https://doi.org/10.1364/OE.25.024531 OPEXFF 1094-4087 Google Scholar

98. 

R. Wu et al., “Lithium niobate micro-disk resonators of quality factors above 107,” Opt. Lett., 43 (17), 4116 –4119 (2018). https://doi.org/10.1364/OL.43.004116 OPLEDP 0146-9592 Google Scholar

99. 

A. Fedotova et al., “Second-harmonic generation in resonant nonlinear metasurfaces based on lithium niobate,” Nano Lett., 20 (12), 8608 –8614 (2020). https://doi.org/10.1021/acs.nanolett.0c03290 NALEFD 1530-6984 Google Scholar

100. 

J. Ma et al., “Nonlinear lithium niobate metasurfaces for second harmonic generation,” Laser Photonics Rev., 15 (5), 2000521 (2021). https://doi.org/10.1002/lpor.202000521 Google Scholar

101. 

Y. Li et al., “Optical anapole mode in nanostructured lithium niobate for enhancing second harmonic generation,” Nanophotonics, 9 (11), 3575 –3585 (2020). https://doi.org/10.1515/nanoph-2020-0222 Google Scholar

102. 

F. Renaud et al., “Second-harmonic-generation enhancement in cavity resonator integrated grating filters,” Opt. Lett., 44 (21), 5198 –5201 (2019). https://doi.org/10.1364/OL.44.005198 OPLEDP 0146-9592 Google Scholar

103. 

S. Yuan et al., “Strongly enhanced second harmonic generation in a thin film lithium niobate heterostructure cavity,” Phys. Rev. Lett., 127 (15), 153901 (2021). https://doi.org/10.1103/PhysRevLett.127.153901 PRLTAO 0031-9007 Google Scholar

104. 

Y. Li et al., “Recent progress of second harmonic generation based on thin film lithium niobate,” Chin. Opt. Lett., 19 (6), 060012 (2021). https://doi.org/10.3788/COL202119.060012 CJOEE3 1671-7694 Google Scholar

105. 

H. Jiang et al., “Nonlinear frequency conversion in one dimensional lithium niobate photonic crystal nanocavities,” Appl. Phys. Lett., 113 (2), 021104 (2018). https://doi.org/10.1063/1.5039948 APPLAB 0003-6951 Google Scholar

106. 

M. Li et al., “High-Q 2D lithium niobate photonic crystal slab nanoresonators,” Laser Photonics Rev., 13 (5), 1800228 (2019). https://doi.org/10.1002/lpor.201800228 Google Scholar

107. 

J. S. Dam, P. Tidemand-Lichtenberg and C. Pedersen, “Room-temperature mid-infrared single-photon spectral imaging,” Nat. Photonics, 6 (11), 788 –793 (2012). https://doi.org/10.1038/nphoton.2012.231 NPAHBY 1749-4885 Google Scholar

108. 

G. Li et al., “Broadband sum-frequency generation using d33 in periodically poled LiNbO3 thin film in the telecommunications band,” Opt. Lett., 42 (5), 939 –942 (2017). https://doi.org/10.1364/OL.42.000939 OPLEDP 0146-9592 Google Scholar

109. 

Z. Hao et al., “Sum-frequency generation in on-chip lithium niobate microdisk resonators,” Photonics Res., 5 (6), 623 –628 (2017). https://doi.org/10.1364/PRJ.5.000623 Google Scholar

110. 

X. Ye et al., “Sum-frequency generation in lithium-niobate-on-insulator microdisk via modal phase matching,” Opt. Lett., 45 (2), 523 –526 (2020). https://doi.org/10.1364/OL.383450 OPLEDP 0146-9592 Google Scholar

111. 

A. K. Hansen et al., “Highly efficient single-pass sum frequency generation by cascaded nonlinear crystals,” Opt. Lett., 40 (23), 5526 –5529 (2015). https://doi.org/10.1364/OL.40.005526 OPLEDP 0146-9592 Google Scholar

112. 

T. Sjaardema, A. Rao and S. Fathpour, “Third-and fourth-harmonic generation in cascaded periodically-poled lithium niobate ultracompact waveguides on silicon,” in CLEO: Sci. and Innov., STh1J-1 (2019). Google Scholar

113. 

S. Lauria and M. F. Saleh, “Mixing second- and third-order nonlinear interactions in nanophotonic lithium-niobate waveguides,” Phys. Rev. A, 105 (4), 043511 (2021). https://doi.org/10.1103/PhysRevA.105.043511 Google Scholar

114. 

R. Wolf et al., “Cascaded second-order optical nonlinearities in on-chip micro rings,” Opt. Express, 25 (24), 29927 –29933 (2017). https://doi.org/10.1364/OE.25.029927 OPEXFF 1094-4087 Google Scholar

115. 

D. D. Hickstein et al., “High-harmonic generation in periodically poled waveguides,” Optica, 4 (12), 1538 –1544 (2017). https://doi.org/10.1364/OPTICA.4.001538 Google Scholar

116. 

D. Wang et al., “Cascaded sum-frequency generation and electro-optic polarization coupling in the PPLNOI ridge waveguide,” Opt. Express, 27 (11), 15283 –15288 (2019). https://doi.org/10.1364/OE.27.015283 OPEXFF 1094-4087 Google Scholar

117. 

Y. J. Ding, “Progress in terahertz sources based on difference-frequency generation,” J. Opt. Soc. Am. B, 31 (11), 2696 –2711 (2014). https://doi.org/10.1364/JOSAB.31.002696 JOBPDE 0740-3224 Google Scholar

118. 

C. Erny et al., “Mid-infrared difference-frequency generation of ultrashort pulses tunable between 3.2 and 4.8  μm from a compact fiber source,” Opt. Lett., 32 (9), 1138 –1140 (2007). https://doi.org/10.1364/OL.32.001138 OPLEDP 0146-9592 Google Scholar

119. 

J. Mishra et al., “Mid-infrared nonlinear optics in thin-film lithium niobate on sapphire,” Optica, 8 (6), 921 –924 (2021). https://doi.org/10.1364/OPTICA.427428 Google Scholar

120. 

J. Yang and C. Wang, “Efficient terahertz generation scheme in a thin-film lithium niobate-silicon hybrid platform,” Opt. Express, 29 (11), 16477 –16486 (2021). https://doi.org/10.1364/OE.419965 OPEXFF 1094-4087 Google Scholar

121. 

F. Kaufmann et al., “On-chip optical parametric amplification in subwavelength lithium niobate nanowaveguides,” in Integr. Photonics Res., Silicon and Nanophotonics, JTu5A-52 (2018). Google Scholar

122. 

J.-Y. Chen et al., “Phase-sensitive amplification in nanophotonic periodically poled lithium niobate waveguides,” in CLEO: Sci. and Innov., SM3L-5 (2020). Google Scholar

123. 

L. Ledezma et al., “Intense optical parametric amplification in dispersion engineered nanophotonic lithium niobate waveguides,” (2021). Google Scholar

124. 

M. Jankowski et al., “Quasi-static optical parametric amplification,” Optica, 9 (3), 273 –279 (2022). https://doi.org/10.1364/OPTICA.442550 Google Scholar

125. 

J. Lu et al., “Ultralow-threshold thin-film lithium niobate optical parametric oscillator,” Optica, 8 (4), 539 –544 (2021). https://doi.org/10.1364/OPTICA.418984 Google Scholar

126. 

D. C. Burnham and D. L. Weinberg, “Observation of simultaneity in parametric production of optical photon pairs,” Phys. Rev. Lett., 25 (2), 84 –87 (1970). https://doi.org/10.1103/PhysRevLett.25.84 PRLTAO 0031-9007 Google Scholar

127. 

T. Jennewein et al., “Quantum cryptography with entangled photons,” Phys. Rev. Lett., 84 (20), 4729 –4732 (2000). https://doi.org/10.1103/PhysRevLett.84.4729 PRLTAO 0031-9007 Google Scholar

128. 

D. Bouwmeester et al., “Experimental quantum teleportation,” Nature, 390 (6660), 575 –579 (1997). https://doi.org/10.1038/37539 Google Scholar

129. 

B. S. Elkus et al., “Generation of broadband correlated photon-pairs in short thin-film lithium-niobate waveguides,” Opt. Express, 27 (26), 38521 –38531 (2019). https://doi.org/10.1364/OE.27.038521 OPEXFF 1094-4087 Google Scholar

130. 

B. S. Elkus et al., “Quantum-correlated photon-pair generation via cascaded nonlinearity in an ultra-compact lithium-niobate nano-waveguide,” Opt. Express, 28 (26), 39963 –39975 (2020). https://doi.org/10.1364/OE.411575 OPEXFF 1094-4087 Google Scholar

131. 

G.-T. Xue et al., “Ultrabright multiplexed energy-time-entangled photon generation from lithium niobate on insulator chip,” Phys. Rev. Appl., 15 (6), 064059 (2021). https://doi.org/10.1103/PhysRevApplied.15.064059 PRAHB2 2331-7019 Google Scholar

132. 

J. Zhao et al., “High quality entangled photon pair generation in periodically poled thin-film lithium niobate waveguides,” Phys. Rev. Lett., 124 (16), 163603 (2020). https://doi.org/10.1103/PhysRevLett.124.163603 PRLTAO 0031-9007 Google Scholar

133. 

U. A. Javid et al., “Ultrabroadband entangled photons on a nanophotonic chip,” Phys. Rev. Lett., 127 (18), 183601 (2021). https://doi.org/10.1103/PhysRevLett.127.183601 PRLTAO 0031-9007 Google Scholar

134. 

Z. Ma et al., “Ultrabright quantum photon sources on chip,” Phys. Rev. Lett., 125 (26), 263602 (2020). https://doi.org/10.1103/PhysRevLett.125.263602 PRLTAO 0031-9007 Google Scholar

135. 

S. Saravi, T. Pertsch and F. Setzpfandt, “Lithium niobate on insulator: an emerging platform for integrated quantum photonics,” Adv. Opt. Mater., 9 (22), 2100789 (2021). https://doi.org/10.1002/adom.202100789 2195-1071 Google Scholar

136. 

G. I. Stegeman, D. J. Hagan and L. Torner, “χ(2) cascading phenomena and their applications to all-optical signal processing, mode-locking, pulse compression and solitons,” Opt. Quantum Electron., 28 (12), 1691 –1740 (1996). https://doi.org/10.1007/BF00698538 OQELDI 0306-8919 Google Scholar

137. 

T. Sjaardema et al., “Low-harmonic generation in cascaded thin-film lithium niobate waveguides,” Adv. Photonics Res., 2022 2100262 (2022). https://doi.org/10.1002/adpr.202100262 Google Scholar

138. 

M. Wang et al., “Strong nonlinear optics in on-chip coupled lithium niobate microdisk photonic molecules,” New J. Phys., 22 (7), 073030 (2020). https://doi.org/10.1088/1367-2630/ab97ea NJOPFM 1367-2630 Google Scholar

139. 

M. Jankowski et al., “Ultrabroadband nonlinear optics in nanophotonic periodically poled lithium niobate waveguides,” Optica, 7 (1), 40 –46 (2020). https://doi.org/10.1364/OPTICA.7.000040 Google Scholar

140. 

M. Malinowski et al., “Towards on-chip self-referenced frequency-comb sources based on semiconductor mode-locked lasers,” Micromachines, 10 (6), 391 (2019). https://doi.org/10.3390/mi10060391 Google Scholar

141. 

S. Mosca et al., “Modulation instability induced frequency comb generation in a continuously pumped optical parametric oscillator,” Phys. Rev. Lett., 121 (9), 093903 (2018). https://doi.org/10.1103/PhysRevLett.121.093903 PRLTAO 0031-9007 Google Scholar

142. 

A. W. Bruch et al., “Pockels soliton microcomb,” Nat. Photonics, 15 (1), 21 –27 (2021). https://doi.org/10.1038/s41566-020-00704-8 NPAHBY 1749-4885 Google Scholar

143. 

R. Ikuta et al., “Frequency comb generation in a quadratic nonlinear waveguide resonator,” Opt. Express, 26 (12), 15551 –15558 (2018). https://doi.org/10.1364/OE.26.015551 OPEXFF 1094-4087 Google Scholar

144. 

X. Wang et al., “2  μm optical frequency comb generation via optical parametric oscillation from a lithium niobate optical superlattice box resonator,” Photonics Res., 10 (2), 509 –515 (2022). https://doi.org/10.1364/PRJ.432076 Google Scholar

145. 

N. Amiune et al., “Optical-parametric-oscillation-based χ(2) frequency comb in a lithium niobate microresonator,” Opt. Express, 29 (25), 41378 –41387 (2021). https://doi.org/10.1364/OE.440206 OPEXFF 1094-4087 Google Scholar

146. 

I. Hendry et al., “Experimental observation of internally pumped parametric oscillation and quadratic comb generation in a χ(2) whispering-gallery-mode microresonator,” Opt. Lett., 45 (5), 1204 –1207 (2020). https://doi.org/10.1364/OL.385751 OPLEDP 0146-9592 Google Scholar

147. 

J. Szabados et al., “Frequency comb generation via cascaded second-order nonlinearities in microresonators,” Phys. Rev. Lett., 124 (20), 203902 (2020). https://doi.org/10.1103/PhysRevLett.124.203902 PRLTAO 0031-9007 Google Scholar

148. 

Y. Hu et al., “High-efficiency and broadband electro-optic frequency combs enabled by coupled micro-resonators,” (2021). Google Scholar

149. 

T. Ren et al., “An integrated low-voltage broadband lithium niobate phase modulator,” IEEE Photonics Technol. Lett., 31 (11), 889 –892 (2019). https://doi.org/10.1109/LPT.2019.2911876 IPTLEL 1041-1135 Google Scholar

150. 

M. Xu et al., “Integrated lithium niobate modulator and frequency comb generator based on Fabry-Perot resonators,” in CLEO: Appl. and Technol., JTh2B-27 (2020). Google Scholar

151. 

M. Zhang et al., “Broadband electro-optic frequency comb generation in a lithium niobate microring resonator,” Nature, 568 (7752), 373 –377 (2019). https://doi.org/10.1038/s41586-019-1008-7 Google Scholar

152. 

H. Sun et al., “Recent progress in integrated electro-optic frequency comb generation,” J. Semicond., 42 (4), 041301 (2021). https://doi.org/10.1088/1674-4926/42/4/041301 Google Scholar

153. 

R. Normandin and G. I. Stegeman, “Nondegenerate four-wave mixing in integrated optics,” Opt. Lett., 4 (2), 58 –59 (1979). https://doi.org/10.1364/OL.4.000058 OPLEDP 0146-9592 Google Scholar

154. 

B. J. Eggleton et al., “Brillouin integrated photonics,” Nat. Photonics, 13 (10), 664 –677 (2019). https://doi.org/10.1038/s41566-019-0498-z NPAHBY 1749-4885 Google Scholar

155. 

R. Loudon, “The Raman effect in crystals,” Adv. Phys., 13 (52), 423 –482 (1964). https://doi.org/10.1080/00018736400101051 ADPHAH 0001-8732 Google Scholar

156. 

L. Cai et al., “Acousto-optical modulation of thin film lithium niobate waveguide devices,” Photonics Res., 7 (9), 1003 –1013 (2019). https://doi.org/10.1364/PRJ.7.001003 Google Scholar

157. 

A. L. Gaeta, M. Lipson and T. J. Kippenberg, “Photonic-chip-based frequency combs,” Nat. Photonics, 13 (3), 158 –169 (2019). https://doi.org/10.1038/s41566-019-0358-x NPAHBY 1749-4885 Google Scholar

158. 

Y. Okawachi et al., “Chip-based self-referencing using integrated lithium niobate waveguides,” Optica, 7 (6), 702 –707 (2020). https://doi.org/10.1364/OPTICA.392363 Google Scholar

159. 

M. Yu et al., “Coherent two-octave-spanning supercontinuum generation in lithium-niobate waveguides,” Opt. Lett., 44 (5), 1222 –1225 (2019). https://doi.org/10.1364/OL.44.001222 OPLEDP 0146-9592 Google Scholar

160. 

J. Lu et al., “Octave-spanning supercontinuum generation in nanoscale lithium niobate waveguides,” Opt. Lett., 44 (6), 1492 –1495 (2019). https://doi.org/10.1364/OL.44.001492 OPLEDP 0146-9592 Google Scholar

161. 

Y. He et al., “Self-starting bi-chromatic LiNbO3 soliton microcomb,” Optica, 6 (9), 1138 –1144 (2019). https://doi.org/10.1364/OPTICA.6.001138 Google Scholar

162. 

Z. Gong et al., “Near-octave lithium niobate soliton microcomb,” Optica, 7 (10), 1275 –1278 (2020). https://doi.org/10.1364/OPTICA.400994 Google Scholar

163. 

Z. Gong et al., “Monolithic Kerr and electro-optic hybrid microcombs,” (2022). Google Scholar

164. 

Z. Gong et al., “Soliton microcomb generation at 2  μm in z-cut lithium niobate microring resonators,” Opt. Lett., 44 (12), 3182 –3185 (2019). https://doi.org/10.1364/OL.44.003182 OPLEDP 0146-9592 Google Scholar

165. 

C. Wang et al., “Monolithic lithium niobate photonic circuits for Kerr frequency comb generation and modulation,” Nat. Commun., 10 (1), 978 (2019). https://doi.org/10.1038/s41467-019-08969-6 NCAOBW 2041-1723 Google Scholar

166. 

A. Honardoost et al., “Cascaded integration of optical waveguides with third-order nonlinearity with lithium niobate waveguides on silicon substrates,” IEEE Photonics J., 10 (3), 4500909 (2018). https://doi.org/10.1109/JPHOT.2018.2827995 Google Scholar

167. 

G. F. C. Gonzalez et al., “Design of a hybrid chalcogenide-glass on lithium-niobate waveguide structure for high-performance cascaded third-and second-order optical nonlinearities,” Appl. Opt., 58 (13), D1 –D6 (2019). https://doi.org/10.1364/AO.58.0000D1 APOPAI 0003-6935 Google Scholar

168. 

Y. Zhao et al., “Compact lithium-niobate-on-insulator polarization rotator based on asymmetric hybrid plasmonics waveguide,” IEEE Photonics J., 13 (4), 4800105 (2021). https://doi.org/10.1109/JPHOT.2021.3094797 Google Scholar

169. 

Z. Chen et al., “Broadband adiabatic polarization rotator-splitter based on a lithium niobate on insulator platform,” Photonics Res., 9 (12), 2319 –2324 (2021). https://doi.org/10.1364/PRJ.432906 Google Scholar

170. 

X. Wang et al., “Efficient polarization splitter-rotator on thin-film lithium niobate,” Opt. Express, 29 (23), 38044 –38052 (2021). https://doi.org/10.1364/OE.443798 OPEXFF 1094-4087 Google Scholar

171. 

M. Cai et al., “Erbium-doped lithium niobate thin film waveguide amplifier with 16 dB internal net gain,” IEEE J. Sel. Top. Quantum Electron., 28 (3), 8200608 (2021). https://doi.org/10.1109/JSTQE.2021.3137192 IJSQEN 1077-260X Google Scholar

172. 

Q. Luo et al., “On-chip erbium-doped lithium niobate waveguide amplifiers,” Chin. Opt. Lett., 19 (6), 060008 (2021). https://doi.org/10.3788/COL202119.060008 CJOEE3 1671-7694 Google Scholar

173. 

J. Zhou et al., “On-chip integrated waveguide amplifiers on erbium-doped thin-film lithium niobate on insulator,” Laser Photonics Rev., 15 (8), 2100030 (2021). https://doi.org/10.1002/lpor.202100030 Google Scholar

Biography

Milad Gholipour Vazimali is a PhD candidate at CREOL, the College of Optics and Photonics at the University of Central Florida (UCF). He received his BS degree in electrical engineering from Sharif University of Technology in 2014. He received his first MS degree in semiconductor devices from the University of Tehran in 2017 and his second MS degree in optics from UCF in 2020. His current research interests include photonic integrated circuits, nonlinear optics, and optoelectronic devices.

Sasan Fathpour is a professor at CREOL, the College of Optics and Photonics at UCF with a secondary joint appointment at the Department of Electrical and Computer Engineering. He received his PhD in electrical engineering from the University of Michigan, Ann Arbor, in 2005. His current research interests include heterogeneous integrated photonics, nonlinear integrated optics, silicon photonics, and unconventional photonic platforms operating in the mid-wave- and near-infrared and visible wavelength ranges. He has received the US National Science Foundation CAREER Award (2012) and the Office of Naval Research Young Investigator Program Award (2013). He is a coauthor of over 190 publications, including about 80 journal papers, 6 book chapters, and 3 patents. He coedited the book Silicon Photonics for Telecommunications and Biomedicine, CRC Press (2012). He is the cofounder of Partow Technologies, LLC. He is an associate editor of Optica and has been a guest editor for the SPIE Journal of Nanophotonics. He is a fellow of Optica, a senior member of SPIE and IEEE, and a member of MRS.

CC BY: © The Authors. Published by SPIE under a Creative Commons Attribution 4.0 Unported License. Distribution or reproduction of this work in whole or in part requires full attribution of the original publication, including its DOI.
Milad Gholipour Vazimali and Sasan Fathpour "Applications of thin-film lithium niobate in nonlinear integrated photonics," Advanced Photonics 4(3), 034001 (30 May 2022). https://doi.org/10.1117/1.AP.4.3.034001
Received: 15 March 2022; Accepted: 3 May 2022; Published: 30 May 2022
Lens.org Logo
CITATIONS
Cited by 80 scholarly publications.
Advertisement
Advertisement
KEYWORDS
Waveguides

Second-harmonic generation

Lithium niobate

Nonlinear optics

Photonics

Integrated photonics

Thin films

Back to Top