27 November 2013 Polymer-embedded colloidal lead-sulfide nanocrystals integrated to vertically slotted silicon-based ring resonators for telecom applications
Author Affiliations +
The main drawback of the rapidly evolving field of silicon photonics lies in the absence of efficient monolithically integrated radiation sources as a consequence of the indirect bandgap of Si and Ge. Relevant alternatives based on the hybrid combination of Si with optically active materials have to be technologically simple, temporally stable, and provide efficient coupling to the Si waveguides. Lead-sulfide nanocrystals (NCs) were blended into a polymer resist suitable for deep-UV- and electron-beam lithography and integrated into Si-based vertically slotted waveguides and ring resonators. The polymer both stabilizes the NC’s photoluminescence emission against degradation under ambient conditions and allows lithographic patterning of this compound material. After integration into the optoelectronic structures and upon optical pumping, intense photoluminescence emission from ring resonators was recorded at the output of bus-waveguides. The resonator quality factors were investigated for polymer-NC compounds with NC concentrations in the range between 0.1 and 8 vol%. The spontaneous emission rate enhancement for vertically slotted resonators was estimated to be a factor of two higher as compared to unslotted ones. The stable integration of colloidal NCs as well as the improved light coupling to silicon circuits is an important step in the development of silicon-based hybrid photonics.



The field of integrated Si-based photonics has been emerging as a promising alternative to electronics over the last years, a trend that can be explained by the rapid advancements in terms of device design and compatibility with complementary metal-oxide semiconductor technology.1 However, although many low-loss devices like waveguides, filters, and optical switches, have been demonstrated in the past, the indirect bandgap of Si makes the realization of integrated emitters a demanding task still left to be solved.

One approach to overcome this problem is the development of hybrid structures that introduce semiconductor nanocrystal quantum dots (NCs) as emitters into Si-based photonics. The absorption and emission wavelengths of these NCs depend on the materials used during synthesis and on their size, and especially lead-sulfide (PbS) NCs are very attractive for applications in the telecom wavelength regime.23.4 Recent studies on NCs coupled to Si-based photonic crystal cavities have shown promising results toward the spectroscopy of single NCs5 as well as electrically pumped light-emitting devices.6

As the fabrication of such NCs is based on colloidal chemistry, their on-chip integration can be carried out after synthesis using well-established methods like drop casting, spin coating, or inkjet printing. Alternatively, the NCs can be blended into suitable polymers,7,8 which protect the NCs from degradation caused by ambient conditions and allow lithographic methods for locally defined on-chip integration. While with respect to fabrication simplicity it can be very advantageous to implement the NCs on a fully completed optoelectronic chip, the question remains how the light emitted by the NCs can be efficiently coupled to the Si structures on the device.

In this work, we experimentally demonstrate the integration of polymer-embedded PbS NCs into all-integrated Si-based vertically slotted ring resonators and waveguides as optically pumped emitters for room temperature applications. The novelty of this paper is in the significant increase of the spontaneous emission rate due to the vertical slot as compared to unslotted but otherwise similar structures that have been reported previously.9 Our method of integration allows the same device to be investigated as function of the NC concentration, using the negative electron-beam lithography (EBL) resist AR-7700.18 as polymer matrix. We demonstrate the full recovery of NC photoluminescence (PL) intensity after the polymer-NC blend is repeatedly heated up to 115°C and cooled back to room temperature, as required after exposure of the resist. Thus, spatial definition of a spin-cast polymer-NC film by EBL is possible without degrading the emission properties of the NCs. The compound additionally shows unaltered optical properties weeks after sample preparation, pointing out the high stability of this material and its suitability for device applications.


Polymer Nanocrystal Compound

As nanoemitters to be introduced into our photonic structures, colloidal PbS NCs from Evident Technologies (EviDot core LNR03LPB) suspended in toluene (40mg/ml) with a core diameter of 5.1nm are used. For an NC film drop cast onto a Si substrate, the room temperature PL spectrum under 532 nm continuous wave (cw) excitation is shown in Fig. 1(a) by the black dashed line. The PL signal shows a peak emission at 1375 nm and a full width at half maximum (FWHM) of 120nm, which is due to the inhomogeneous size distribution of the NCs. However, these NCs, when kept in an ambient environment, tend to bleach and oxidize quickly, which causes the PL signal to vanish or severely blue-shift, respectively.10 The incorporation of the NCs into a host material is one way to counteract these effects. From a device point of view, where the stability of the optical properties of the NCs over time is of great importance, poly(methyl-methacrylate) (PMMA), which is commonly used in research as a host material for NCs,11,12 is not suitable because a large shift on the PL peak emission can still be observed over the course of several days.13 On the other hand, novel epoxy-based photoresists like SU-8 or mr-L 6005 XP have been shown to also keep their lithographic processability after the incorporation of NCs emitting in the visible wavelength regime.14,15 A compound material suitable for device applications at telecom wavelengths should consequently ensure high stability over a long period of time while still preserving the sensitivity to lithographic patterning.

Fig. 1

(a) Normalized room temperature photoluminescence (PL) spectra of pure PbS nanocrystals (NCs) (black dashed line) and a Novolak-NC blend containing 4 vol% of PbS drop cast onto an Si substrate (full red line). (b) PL peak intensity of a defined number of NCs embedded into Novolak polymer under nominally equal optical excitation as function of the time under ambient conditions after drop casting. (c) Shift of the emission peak wavelength of the compound in function of the time under ambient conditions after drop casting.


In our case, the epoxy-based negative electron beam resist Novolak ARN 7700.18 from Allresist is used as a host material for the PbS NCs. Novolak-based polymer-NC blends containing different concentrations of NCs from 8 down to 0.1 vol% are mixed under nitrogen atmosphere to avoid any NC degradation throughout the compound fabrication process. In Fig. 1(a), the normalized PL spectrum of a polymer-NC blend containing 4 vol% of PbS drop cast onto a Si substrate is shown by the full red line. A perfect spectral agreement confront to the original pure PbS spectrum is found. The small intensity drops in both spectra of Fig. 1(a) at 1365 and 1385 nm correspond to atmospheric absorption.

The stability of intensity and spectral shape of the mixture over time is investigated and the results are presented in Figs. 1(b) and 1(c), respectively. In Fig. 1(b), the PL peak intensity of a fixed number of NCs embedded into Novolak polymer and coupled to a waveguide as discussed in a following paragraph is investigated over several weeks after drop casting. No degradation of the emission intensity is observed, showing that bleaching of the NCs in the polymer host is practically absent. Additionally, the spectral stability of the emission peak wavelength is shown in Fig. 1(c). As no spectral shift is observed after more than 40 days, we conclude that the NCs in the compound are also insensitive to oxidation. In between measurements, the samples were stored at ambient atmosphere.

Lithographic patterning imposes additional requirements on the compound, perhaps the most crucial one being the necessity to bake the material after exposure at 110°C for 2 min in order to crosslink the molecular chains of the negative resist so that the exposed areas are not removed during development. We thus examine the PL peak intensity of the polymer-NC blend while repeatedly heating the sample up to 115°C and cooling it back down to room temperature. Measurement results are presented in Fig. 2(a). By increasing the temperature of the sample, the observed PL peak intensity is lowered dramatically. This behavior can be a result of several effects discussed in the literature, such as the thermal activation between bright and dark excitonic states16 with subsequent nonradiative recombination or an increase of carrier-phonon interactions at elevated temperatures,17,18 although an exact mechanism is still under debate.19 By reducing again the temperature, however, the original PL peak intensity is restored. The heating and cooling steps were repeated several times on the same sample, thus confirming that the NCs do not experience temperature-induced permanent degradation up to 115°C.

Fig. 2

(a) PL peak intensity of the Novolak-NC mixture at various temperatures during heating (red open squares) and cooling (blue open squares). (b) PL spectra of the Novolak-NC mixture before electron-beam lithography (EBL) (black line with open squares) and after EBL (red line with open squares). (c) SEM image of a 10×10μm2 square of spin cast Novolak-NC mixture defined on ¼ of a photonic ring resonator by EBL.


Subsequently, the compound was spin coated on a photonic device and a 10×10μm2 square was defined on top of a ring resonator using EBL. A scanning electron microscopy picture of the final device is shown in Fig. 2(c). Even though practically any kind of structure could be realized with this method, the rather large-scale patterning allows a straightforward comparison of the emission intensity in a confocal μ-PL setup. The PL spectra of the polymer-NC layer before and after EBL are shown in Fig. 2(b). Neither a change of the PL intensity nor a shift of the emission peak wavelength is observed. Although the possibility for lithographic patterning without affecting the optical properties of the PbS NCs in the polymer is not essential for the work discussed in the following, this demonstrates the possibility to use this compound as an active material for on-chip applications and devices.

All this information indicates that the Novolak-based NC compound is a promising material for the fabrication of all-integrated hybrid photonic structures at telecom wavelengths, and in the rest of this article, it is used as the active medium.


Device Design and Fabrication

The first photonic devices for testing the integration of the PbS NCs are monomode waveguides coupled to ring resonators fabricated on a silicon on insulator wafer. All the processing of these samples was done by Amo Ltd. (Aachen, Germany) using EBL and inductively coupled plasma reactive ion etching (RIE). The 220-nm-high and 600-nm-wide Si waveguides are separated from the ring resonator (radius r=10μm) of the same cross-section by a gap of 150 nm.

In order to limit the interaction between the polymer-NC compound and the waveguide structures to a specific region on the device, the samples are passivated by spin casting a layer of Microchem SU-8 2000.5 negative resist with a thickness of 500 nm. The samples are then further processed using UV lithography in order to open 60×30μm interaction windows around the ring resonators. As a final step of the sample preparation, the SU-8 is cured on a hotplate at 150°C for 10 min. These windows are then filled by drop casting 0.5μl of the polymer-NC mixture and subsequent curing of the device at 75°C for 1 min. A scheme of the final device is shown in Fig. 3(b).

Fig. 3

Schematics of the vertically slotted (a) and unslotted (b) ring resonator—waveguide structure with the SU-8 interaction window. (c) to (e) show three-dimensional (3-D) beam propagation method (BPM) contour plots of the fundamental modes of the vertically slotted waveguide in TE (c) and TM (d) polarization and the unslotted waveguide in TE (e) and TM (f).


Due to the nearly equal refractive indices of SU-8 and the Novolak polymer (1.572 and 1.575, respectively, at 1500 nm wavelength),20,21 no significant mode distortion is experienced by the light travelling in the waveguide across the interface between SU-8 and the Novolak-NC compound. Another advantage of using SU-8 as a passivation layer in combination with the Novolak-based compound is the fact that the hard-baked SU-8 is only removable using piranha wet etching or RIE, whereas the polymer-NC blend can easily be cleaned off the device using the Allresist AR 300-70 remover. This allows a quick and efficient swapping of mixtures of different NC concentrations without affecting the device itself and in particular the waveguide facets. Additionally, this method enables an investigation of the same device for different NC concentrations of the compound.

Figures 3(e) and 3(f) show full-vector three-dimensional (3-D) beam propagation method (BPM) simulations of the fundamental modes of the Si waveguide at 1.45 μm wavelength for quasi transverse-electric (TE) and quasi transverse-magnetic (TM) polarization, respectively. The blue lines indicate the borders of the structures. In the TE case, most of the light is well confined inside the waveguide and the overlap factor Γ (defined as the partial power of the guided light within the active material with respect to the total guided power) is calculated to be only 0.1. Due to the waveguide cross-section dimensions, the TM mode is more weakly confined to the Si waveguide, and consequently Γ=0.25. The effective index of refraction neff is calculated to be 2.63 and 2.04 for TE and TM, respectively.

In order to further increase the overlap factor and thus the interaction of the NCs with the mode of the waveguide, a vertically slotted structure22 was also designed. This high-index contrast photonic structure with deep-submicron feature size consists of a thin layer of low-index material sandwiched between two high-index walls. Compared to conventional waveguides, where the main part of the optical field is confined within the high-index core, a larger fraction of the guided mode is within the low-index region, which in our case is the polymer-NC compound. This effect occurs only for the polarization mode whose electric field is perpendicular to the slot interfaces, which in the case of the vertically slotted structures discussed here is TE.

The outer dimensions of the slot waveguides are similar to the ones already described above, but in addition, they feature 100-nm-wide vertical slots in the center. The gap between the (also slotted) ring resonator and the waveguide is 300 nm. Figure 3(a) shows a sketch of such a vertically slotted device. Figure 3(c) represents 3-D BPM simulations of the fundamental mode of the Si slot waveguide for TE polarization. The field is affected by a discontinuity at the slot-wall interfaces, which increases the maxima of the optical field evanescent tails within the slot, and Γ and neff are calculated to be 0.38 and 2.03, respectively. A decomposition of the overlap factor Γ=Γslot+Γout into contributions from inside (Γslot) and outside (Γout) the slot results in Γslot=0.15 and Γout=0.23. In TM polarization no such beneficial effect from the slot can be anticipated from the mode picture [Fig. 3(d)]. Although a slightly increased overlap factor Γ of 0.4 due to weaker confinement to the waveguide and thus a smaller neff=1.83 are calculated, the value for Γslot is only 0.06.


Transmission Measurements

The transmission spectra of the devices for different NC concentrations were measured using a tunable infrared cw laser source fiber-coupled to a polarization-maintaining (PM) lensed fiber mounted on a piezo stage. The excitation power of the laser was set to 1 mW for all measurements. Light at the output of the waveguide was collected by a second PM fiber and coupled to an InGaAs detector. The input and collection fiber polarization were controlled by rotatable fiber holders.

Figure 4(a) shows transmission spectra of the vertically slotted device in TE (red solid line) and TM (black solid line) polarization for an NC concentration of 2 vol%. Both the free spectral range (FSR) and the absolute spectral positions of the TE and TM resonances are very similar in the wavelength region investigated. For polarization-selective coupling of the PbS emission into the resonators, the spectral separation of TM and TE modes has to be controlled. One method to avoid the mode overlapping over a large spectral range is to increase the difference of the effective indices of refraction between TE and TM polarization Δneff=neff,TEneff,TM, resulting in a relative shift between the polarization-specific FSRs. For the vertically slotted structures, decreasing the width of the slot from 100 to 50 nm would cause an increase of Δneff from 0.175 to 0.315, as shown by the results of 3-D BPM simulations in Fig. 4(b). Thus, by a proper choice of the slot width, overlapping TE and TM resonances can be avoided for any spectral region of interest.

Fig. 4

(a) Transmission spectra of the vertically slotted ring resonators coupled to bus waveguides for an NC concentration of 2 vol% in the Novolak matrix, where the red and black solid lines correspond to TE and TM polarization, respectively. The excitation power was set to 1 mW. (b) 3-D BPM simulations of the difference in effective indices of refraction of the fundamental modes in TE and TM polarization Δneff=neff,TEneff,TM in function of the width of the vertical slot. The red dot indicates Δneff for the structure investigated in this work.


The total quality factors Qt (averaged over five central resonances) are 4200 and 1400 in TE and TM polarization, respectively. Qt denotes the as-measured Q factor of a resonator coupled to a waveguide. Depending on the gap separation between the bus-waveguide and the ring resonator, the coupling efficiency between them changes, which consequently modifies the associated loss channel seen by the resonator. Although this is generally inevitable for coupled structures as discussed in this work, we note that the waveguide-resonator separation can be tuned toward strong undercoupling in order to approach the intrinsic Q factor Qi of only the ring resonator, which is related to the losses caused by scattering, absorption, and radiative processes.23 Following Ref. 9, the Qi values of the different photonic structures are extracted from the obtained transmission measurements and represented in Fig. 5(a) for different NC concentrations.

Fig. 5

Intrinsic quality (Q) factors Qi (a) calculated from the measured transmission spectra and calculated Purcell factors Fp (b) as function of the NC concentrations of slotted ring resonator structures in TE (black squares) and TM (blue squares) polarization and unslotted devices in TE (red circles) and TM (green triangles).


By increasing the NC concentration in the active NC-polymer compound, it is clear that depending on the resonator type investigated, and above a certain concentration scattering, losses induced by the NCs coupled to the resonators start to degrade their Q factor. In the case of the nonslotted resonators, the effect of the NCs on the losses starts to appear between 4 and 6 vol%. On the other hand, as the slotted resonators have larger overlaps with the polymer-NC compound, the NC-induced scattering losses degrade the obtained Q values already beyond a concentration of 2 vol%. Below these critical concentrations, the resonators show similar Q factors as unloaded ones, which are covered only by pure Novolak polymer without any NCs. The replacement of the polymer-NC compound was repeated several times for different NC concentrations in order to verify that no residual NCs remain on the devices after the cleaning step.


Photoluminescence Measurements and Purcell Factor

The intrinsic Q factor is highest for nonslotted ring resonators for TE polarization, where the guided light experiences the highest confinement to the Si. However, more important than the Q factor for emitters coupled to resonators is the Purcell factor, which describes the enhancement of the spontaneous emission rate of an emitter into a resonator mode with respect to its integrated emission rate into all vacuum modes.24 According to Ref. 25, the Purcell factor of an optical resonator is defined as Fp=Γ/(4π2)(λ/neff)3(Qi/V), where V denotes the mode volume calculated using 3-D finite-difference time-domain simulations. For the nonslotted device, mode volumes of resonances around 1.45 μm wavelength in TE and TM are calculated to be 2.1 and 3.9μm3, respectively. For the slotted ring resonators, mode volumes in TE and TM of 2.2 and 4.4μm3 are calculated. Figure 5(b) shows the calculated Purcell factors of the different devices for varying NC concentrations, where the highest Fp of 20 is obtained for the slotted device in TE polarization, a factor of 2 higher than Fp for the unslotted device in TE, which is 10. This demonstrates that the slotted structure is more suitable as an active photonic building block with NCs acting as emitters.

It should be noted that the Purcell factor, which is by definition a property of a cavity independent of emitters coupled to it, only truly holds for perfect emitters with negligible homogeneous linewidth broadening and without any nonradiative decay channel. However, even though colloidal PbS NCs at room temperature are not considered to be perfect emitters, the improvement of Fp from introducing a vertical slot into the structure holds also for nonideal emitters. Consequently, PL measurements were performed on the slotted device.

For the experimental investigation of the PL performance of the slotted device for different NC concentrations, an AlGaInP cw laser with an emission wavelength of 657 nm was focused through a microscope objective onto the ring resonator, with a spot size only slightly larger than the diameter of the ring (20μm). The excitation intensity on the sample was kept constant at 1.64kW/cm2 for all measurements. The PL signal is collected at one output facet of the waveguide through a PM lensed fiber and a fiber-coupled polarizer, after which it is dispersed by a fiber-coupled monochromator connected to an InGaAs photodiode array detector (nominal resolution 0.2 nm). In Fig. 6(a), the PL spectra of the device covered with a polymer-NC compound containing 2 vol% of PbS are plotted in TE (black solid line) and TM polarization (blue dashed line), demonstrating that the PL signal can be investigated in one polarization while the other polarization is completely canceled in the spectrum.

Fig. 6

(a) Room temperature PL spectrum of the vertically slotted ring resonator device for an NC concentration of 2 vol% in the Novolak host with a pump excitation intensity of 1.64kW/cm2 measured at one output facet of the waveguide in TE (black solid line) and TM (blue dashed line). (b) Total Q factor Qt directly obtained from transmission (black squares, Qtr) and PL measurements (red open circles, Qpl) of the vertically slotted device in TE polarization for different NC concentrations. The dashed area indicates the limit of our PL measurement setup expressed in terms of Q factors. (c) Normalized transmission spectrum (red squares Qtr, solid red line corresponds to a Lorentzian fit) and PL spectrum (black squares, Qpl) of the same cavity resonance of the slotted ring resonator structure in TE polarization for an NC concentration of 2 vol%.


Figure 6(b) shows a comparison of Qt (averaged over five central resonances) obtained from transmission and PL measurements in TE polarization. Even though both curves still show the effect of NC-induced scattering losses at concentrations >2vol%, an approximately two times smaller Qt is observed in PL experiments as compared to transmission experiments. The resolution limit of the monochromator used for PL measurements expressed as Q factor is also indicated in Fig. 6(b). It was experimentally determined by measuring the FWHM of the tunable cw laser source (used for the transmission measurements), which was injected into the photonic device detuned from the ring resonances and spectrally resolved by the monochromator. Evidently, the resolution limit of the PL measurement setup does not limit the Qt values measured in PL experiments.

In Fig. 6(c), a spectrum of the same TE resonance is plotted from transmission and PL measurements. Since no shift in terms of resonance wavelength is observed, we assume that thermal effects are negligible, even more so because a polymer top cladding is known to reduce the resonance wavelength temperature dependence of Si microring resonators.26 Transmission measurements were also performed while the PL top excitation laser was illuminating the resonator in order to rule out any effects of the excitation laser on the different Qt factors observed in transmission and PL experiments. We tentatively assign this difference in Qt factors to the NC homogeneous emission linewidth being not significantly smaller than that of the cavity, thereby imposing an upper limit for the PL Q factors and the utilizable Purcell enhancement for these NCs.27 To estimate the homogeneous linewidth of PbS NCs emitting in the telecom wavelength regime and the magnitude of the Purcell factor in our ring resonators, time-resolved PL experiments will be performed.



In conclusion, we have demonstrated the functionalization of an epoxy-based negative photoresist with colloidal PbS NCs emitting at telecom wavelengths. We have investigated the intensity and spectral stability of this compound, which shows unaltered optical properties weeks after preparation. No permanent temperature-induced degradation of the PL signal is observed up to 115°C, thus enabling lithographic patterning of the polymer-NC mixture for on-chip applications. Our choice of materials allows for one and the same all-integrated Si-based ring resonator to investigate its performance as a function of the NC concentration in the polymer, which is coupled to the resonators via drop casting. A critical concentration beyond which NC-induced scattering losses start to degrade the Q factors of the devices was determined. Solid and vertically slotted cavities were compared in terms of Q factors and ideal Purcell factors. PL experiments on the vertically slotted resonators show high-intensity peaks at the facets of the output waveguide. Further investigations are needed to determine the origin of the different Q factors observed in the transmission and PL experiments for the slotted ring resonators.

Finally, the method presented in this work can also be applied for different NCs, enabling simple tuning of the working bandwidth of NC-based optoelectronic chips within the transparency region of Si photonics.


This work was supported by the Austrian Nanoinitiative within the PLATON project cluster under project numbers 819654, 819655, 819656, 834913, and 834924 as well as the Austrian Science Foundation FWF-F2521 (SFB025 IR-ON). We also acknowledge AMO GmbH in Aachen (Germany) for their support and the fabrication of the SOI waveguides and resonators.


1. B. JalaliS. Fathpour, “Silicon photonics,” J. Lightwave Technol. 24(12), 4600–4615 (2006),  http://dx.doi.org/10.1109/JLT.2006.885782.JLTEDG0733-8724 Google Scholar

2. D. V. Talapinet al., “Prospects of colloidal nanocrystals for electronic and optoelectronic applications,” Chem. Rev. 110(1), 389–458 (2010),  http://dx.doi.org/10.1021/cr900137k.CHREAY0009-2665 Google Scholar

3. P. Guyot-Sionnest, “Electrical transport in colloidal quantum dot films,” J. Phys. Chem. Lett. 3(9), 1169–1175 (2012),  http://dx.doi.org/10.1021/jz300048y.1948-7185 Google Scholar

4. A. Omariet al., “Role of interband and photoinduced absorption in the nonlinear reflection and absorption of resonantly excited PbS quantum dots around 1550 nm,” Phys. Rev. B. 85(11), 115318 (2012),  http://dx.doi.org/10.1103/PhysRevB.85.115318.PRBMDO1098-0121 Google Scholar

5. M. T. Rakheret al., “Spectroscopy of 1.55 μm PbS quantum dots on Si photonic crystal cavities with a fiber taper waveguide,” Appl. Phys. Lett. 96(16), 161108 (2010),  http://dx.doi.org/10.1063/1.3396988.APPLAB0003-6951 Google Scholar

6. J. Heoet al., “Electroluminescence from silicon-based photonic crystal microcavities with PbSe quantum dots,” Opt. Lett. 35(4), 547–549 (2010),  http://dx.doi.org/10.1364/OL.35.000547.OPLEDP0146-9592 Google Scholar

7. Y. Olssonet al., “Fabrication and optical properties of polymeric waveguides containing nanocrystalline quantum dots,” Appl. Phys. Lett. 85(19), 4469–4471 (2004),  http://dx.doi.org/10.1063/1.1818723.APPLAB0003-6951 Google Scholar

8. N. Tessleret al., “Efficient near-infrared polymer nanocrystal light-emitting diodes,” Science 295(5559), 1506–1508 (2002),  http://dx.doi.org/10.1126/science.1068153.SCIEAS0036-8075 Google Scholar

9. M. Humeret al., “Integration, photostability and spontaneous emission rate enhancement of colloidal PbS nanocrystals for Si-based photonics at telecom wavelengths,” Opt. Express 21(16), 18680–18688 (2013),  http://dx.doi.org/10.1364/OE.21.018680.OPEXFF1094-4087 Google Scholar

10. J. J. PetersonT. D. Krauss, “Fluorescence spectroscopy of single lead sulfide quantum dots,” Nano Lett. 6(3), 510–514 (2006),  http://dx.doi.org/10.1021/nl0525756.NALEFD1530-6984 Google Scholar

11. D. F. Dorfneret al., “Optical characterization of silicon on insulator photonic crystal nanocavities infiltrated with colloidal PbS quantum dots,” Appl. Phys. Lett. 91(23), 233111 (2007),  http://dx.doi.org/10.1063/1.2822441.APPLAB0003-6951 Google Scholar

12. R. Boseet al., “Weak coupling interactions of colloidal lead sulfide nanocrystals with silicon photonic crystal nanocavities near 1.55 μm at room temperature,” Appl. Phys. Lett. 90(11), 111117 (2007),  http://dx.doi.org/10.1063/1.2714097.APPLAB0003-6951 Google Scholar

13. D. W. GrundB. OlbrichtD. W. Prather, “Quantum dot composite light sources,” Proc. SPIE 7953, 795302 (2011),  http://dx.doi.org/10.1117/12.875227.PSISDG0277-786X Google Scholar

14. C. Ingrossoet al., “An epoxy photoresist modified by luminescent nanocrystals for the fabrication of 3D high-aspect-ratio microstructures,” Adv. Funct. Mater. 17(13), 2009–2017 (2007),  http://dx.doi.org/10.1002/(ISSN)1616-3028.AFMDC61616-3028 Google Scholar

15. A. Qualtieriet al., “Advances in resist materials and processing technology: photonic devices fabricated by direct lithography of resist/colloidal nanocrystals blend,” Chapter 7 in Lithography, M. Wang, Ed., pp. 115–130, InTech Publishing, Rijeka, Croatia (2010). Google Scholar

16. V. I. Klimov, “Mechanisms for photogeneration and recombination of multiexcitons in semiconductor nanocrystals: implications for lasing and solar energy conversion,” J. Phys. Chem. B 110(34), 16827–16845 (2006),  http://dx.doi.org/10.1021/jp0615959.JPCBFK1520-6106 Google Scholar

17. K. Szendreiet al., “Exploring the origin of the temperature-dependent behavior of PbS nanocrystal thin films and solar cells,” Adv. Funct. Mater. 22(8), 1598–1605 (2012),  http://dx.doi.org/10.1002/adfm.v22.8.AFMDC61616-3028 Google Scholar

18. L. Turyanskaet al., “Temperature dependence of the photoluminescence emission from thiol-capped PbS quantum dots,” Appl. Phys. Lett. 90(10), 101913 (2007),  http://dx.doi.org/10.1063/1.2711529.APPLAB0003-6951 Google Scholar

19. B. UllrichJ. S. WangG. J. Brown, “Comment on ‘temperature dependent optical properties of PbS nanocrystals’,” Nanotechnology 24(28), 288001 (2013),  http://dx.doi.org/10.1088/0957-4484/24/28/288001.NNOTER0957-4484 Google Scholar

20. W. H. WongJ. ZhouE. Y. B. Pun, “Low-loss polymeric waveguides using electron-beam direct writing,” Appl. Phys. Lett. 78(15), 2110–2112 (2001),  http://dx.doi.org/10.1063/1.1361287.APPLAB0003-6951 Google Scholar

21. C. S. HuangW. C. Wang, “Large-core single-mode SU8 rib waveguide using solvent-assisted microcontact molding,” Appl. Opt. 47(25), 4540–4547 (2008),  http://dx.doi.org/10.1364/AO.47.004540.APOPAI0003-6935 Google Scholar

22. V. R. Almeidaet al., “Guiding and confining light in void nanostructure,” Opt. Lett. 29(11), 1209–1211 (2004),  http://dx.doi.org/10.1364/OL.29.001209.OPLEDP0146-9592 Google Scholar

23. R. Guideret al., “NanoSi low loss horizontal slot waveguides coupled to high Q ring resonators,” Opt. Express 17(23), 20762–20770 (2009),  http://dx.doi.org/10.1364/OE.17.020762.OPEXFF1094-4087 Google Scholar

24. E. M. Purcell, “Spontaneous emission probabilities at radio frequencies,” Phys. Rev. 69, 681 (1946),  http://dx.doi.org/10.1103/PhysRev.69.37.PHRVAO0031-899X Google Scholar

25. T. BabaD. Sano, “Low-threshold lasing and Purcell effect in microdisk lasers at room temperature,” IEEE J. Sel. Topics Quantum Electron. 9(5), 1340–1346 (2003),  http://dx.doi.org/10.1109/JSTQE.2003.819464.IJSQEN1077-260X Google Scholar

26. J. Tenget al., “Athermal silicon-on-insulator ring resonators by overlaying a polymer cladding on narrowed waveguides,” Opt. Express 17(17), 14627–14633 (2009),  http://dx.doi.org/10.1364/OE.17.014627.OPEXFF1094-4087 Google Scholar

27. A. Pitantiet al., “Probing the spontaneous emission dynamics in Si-nanocrystals-based microdisk resonators” Phys. Rev. Lett. 104(10), 103901 (2010),  http://dx.doi.org/10.1103/PhysRevLett.104.103901.PRLTAO0031-9007 Google Scholar



Markus Humer is a graduate student at the Johannes Kepler University (JKU) of Linz. He received his diploma in technical physics in 2008 in the nano-MIR research group of Professor Dr. Wolfgang Heiß at the Institute of Solid-State Physics at JKU. He is currently working toward his PhD degree in the Nanostructures4Optoelectronics research group of Dr. Thomas Fromherz at the Institute of Semiconductor Physics. His current research interests include colloidal nanocrystal-based photonic devices, nanoplasmonics, cavity quantum electrodynamics, slow light, and graphene.


Romain Guider received his degree in optoelectronics engineering from the École Nationale Supérieure de Sciences Appliquées et de Technologie, Lannion, France, in 2006, and his PhD degree from the University of Trento, Trento, Italy, in 2009. His doctoral research focused on the study of new nanosilicon waveguides and nanophotonics structures, more particularly on slot waveguides, ring and disk resonators. In January 2011, he joined the Institut für Halbleiter und Festkörperphysik, Linz University, Austria, as a postdoctoral fellow. His research interests include design, fabrication, and characterization of new Si-based photonic structures for on-chip applications.


Florian Hackl is a graduate student at the JKU of Linz and received his diploma in technical physics in 2012 in the research group of Professor Dr. Günther Bauer at the Institute of Semiconductor Physics at the JKU. He is currently working on his PhD within the Infra Red Optical Nanostructures project in the research group of Dr. Thomas Fromherz at the Institute of Semiconductor Physics. His current research interests include Si-based optical nanostructures, μ-photoluminescence, and time-resolved spectroscopy in the telecom spectral range.


Thomas Fromherz received his PhD degree in technical sciences from JKU, Linz, Austria, in 1994. He was an Erwin Schrödinger fellow at the Quantum Institute of the University of California, Santa Barbara, in 1996 and worked as a research engineer in the Si Foundry Austria Microsystems International AG, Styria, Austria, from 1997 to 1998, and in the organic solar cell start-up company Quantum Solar Energy Linz, Austria, from 1998 to 2000. In 2000, he rejoined JKU as a research assistant at the Institute of Semiconductor and Solid State Physics and became an assistant professor in 2006. His current research interests include Si-based optoelectronics for the infrared and telecom spectral region.

© The Authors. Published by SPIE under a Creative Commons Attribution 3.0 Unported License. Distribution or reproduction of this work in whole or in part requires full attribution of the original publication, including its DOI.
Markus Humer, Markus Humer, Romain Guider, Romain Guider, Florian Hackl, Florian Hackl, Thomas Fromherz, Thomas Fromherz, } "Polymer-embedded colloidal lead-sulfide nanocrystals integrated to vertically slotted silicon-based ring resonators for telecom applications," Journal of Nanophotonics 7(1), 073076 (27 November 2013). https://doi.org/10.1117/1.JNP.7.073076 . Submission:

Back to Top