16 February 2015 Polymer:fullerene solar cells: materials, processing issues, and cell layouts to reach power conversion efficiency over 10%, a review
Author Affiliations +
Abstract
In spite of the impressive development achieved by organic photovoltaics throughout the last decades, especially in terms of reported power conversion efficiencies, there are still important technological and fundamental obstacles to circumvent before they can be implemented into reliable and long-lasting applications. Regarding device processing, the synthesis of highly soluble polymeric semiconductors first, and then fullerene derivatives, was initially considered as an important breakthrough that would definitely change the fabrication of photovoltaics once and for all. The potential and the expectation raised by this technology is such that it is very difficult to keep track of the most significant progresses being now published in different and even monographic journals. In this paper, we review the development of polymeric solar cells from its origin to the most efficient devices published to date. We separate these achievements into three different categories traditionally followed by the scientific community to push devices over 10% power conversion efficiency: active materials, strategies—fabrication/processing procedures—that can mainly modify the active film morphology, and all the different cell layout/architectures that have been used in order to extract as high a photocurrent as possible from the Sun. The synthesis of new donors, the use of additives and postprocessing techniques, buffer interlayers, inverted and tandem designs are some of the most important aspects that are reviewed in detail in this paper. All have equally contributed to develop this technology and bring it at the doors of commercialization.

1.

Introduction

An abundance of raw materials, simplicity in device fabrication, and easy integration into different applications, thanks to their lightweight, semitransparency, flexibility, and color tunability, have made organic photovoltaics (OPV) an attractive source of green energy. Nowadays research on this technology is focused on understanding the physics behind the technology and on achieving an efficiency as high as possible.

Nelson calculated the limiting efficiency for an ideal single solar cell as a function of the semiconductor bandgap, obtaining a limiting efficiency of 33% at a bandgap of 1.4 eV (885 nm).1 In principle, all the assumptions made for this model are also perfectly valid for organic semiconductors. However, more accurate models explicitly developed for polymer:fullerene bulk heterojunction (BHJ) solar cells and that take into account their detailed working mechanisms predict maximum efficiencies of 15% (Ref. 2) and 21% (Ref. 3) for single and tandem cells, respectively. The main reasons why ideal performances are not achieved are incomplete absorption of the incident light, nonradiative recombination of photogenerated carriers, i.e., excited charges that are trapped at defect sites and recombine before being collected leading to transport losses, and voltage drop due to nonideal series and/or parallel resistance within the bulk and between the active film and the external circuit. All these aspects need to be tackled in order to overcome the current reported record efficiencies and take them closer to the theoretical limits. As we will show, this can be done by actuating on active materials, fabrication/processing procedures (strategies), and device layout/architectures.

The efficiency of a solar cell is defined as the ratio between the voltage at open circuit conditions (Voc), the output current at short circuit conditions (Isc), the fill factor (FF) of the device, and the incident light intensity (Pin) [see Eq. (1)].

(1)

η=Voc·Isc·FFPin.

It is clear that maximizing the efficiency is, thus, a matter of increasing Voc, Isc, and FF as much as possible.

Voc is ideally limited by the energy difference between the LUMO level of the acceptor and the HOMO level of the donor; therefore, it can be theoretically adjusted up to a certain extent by modifying the energy levels of the materials.45.6.7 However, Voc is not strictly an active material issue. Suboptimal contacts can lead to either resistive losses—series resistances—and/or current leakage—parallel resistance—that might cause a voltage drop. Therefore, device engineering and cell layout are also important to guarantee a large Voc. This is usually achieved with the use of interlayers, as we will describe in detail in Sec. 4.

A high photocurrent (Isc) can also be achieved by selecting materials with absorption spectra that overlap the photon flux density and, hence, the incident power spectrum from the Sun. The available power from these cells represents the best compromise between absorption and power delivery. As mentioned above, ideal bandgaps for photovoltaic conversion are in the red and near-infrared part of the electromagnetic spectrum. The so-called low-bandgap (LBG) polymers are synthesized for this purpose.8,9 However, as in the previous case, obtaining a high Isc is not only a matter of the active material. The morphology of the film is crucial in order to ensure efficient charge generation and transport processes.10 Different fabrication/processing procedures can lead to substantially different film morphologies even when the same active materials are used. These will be detailed in Sec. 3. Blends of solvents, the use of additives, manual manipulation of the deposition temperature, and the creation of a solvent saturated atmosphere are some of the strategies most commonly used in order to obtain better control of the film drying process and manipulate the resulting bulk-in morphology.1112.13.14.15.16.17.18

FF is the most meaningful and sensitive parameter in the characterization of solar cells since it contains information of all the processes involved in charge recombination, transport, and collection. The morphology of the film will, therefore, also have a direct effect on the measured FF. As commented above, deliberate manipulation of the film morphology also results in enhanced FF and device performance. Despite alternative fabrication/processing procedures, a spatial asymmetry that helps create a gradient in charge density can be beneficial to obtain selective charge injection/extraction, reduce leakage current and charge recombination, and improve charge transport. The use of buffer layers has been demonstrated to improve, in this way, contact selectivity and device rectification.

Finally, materials with complementary absorption spectra can be stacked together in the same tandem device. This is an alternative device layout/architecture approach in order to maximize the light harvesting and adjust the overall absorption of the cell to the solar irradiance spectrum.19,20

2.

Materials

Polythiophenes are one of the most widely used polymers in the fabrication of organic solar cells due to the good optical and electrical properties and good thermal and chemical stability that they present. Polythiophenes are based on repeating units of thiophenes [see Fig. 1(a)], where different side chains can be added in order to modify the resulting properties.21,22 Poly(3-hexylthiophene) (P3HT) [Fig. 1(b)] has an optical bandgap of 1.9 eV. In the literature, typical efficiency values of 3.5 to 4% have been achieved by several groups when combined with the fullerene derivative [6,6]-phenyl-C61-butyric acid methyl ester (PC60BM) as electron acceptor.23 However, higher efficiencies close to 4.5% have been reported when samples with higher regioregularity24 and/or [6,6]-phenyl C71-butyric acid methyl ester (PC70BM) instead of PC60BM are used.

Fig. 1

Molecular structure of (a) a polythiophene repeat unit and (b) poly(3-hexylthiophene) (P3HT).

JPE_5_1_057214_f001.png

P3HT has been, for many years, the standard absorber material used in OPV. In spite of its moderate power conversion efficiency, its acceptable hole mobility, long stability, processability, and scalability make it a potential candidate for the mass-fabrication of modules using roll-to-roll (R2R) compatible deposition techniques.25,26 However, their restricted absorption to <600nm limits their efficiency below 5%. Some of the most promising candidates that are being synthesized nowadays to enhance the light harvesting include carbazole-benzothiadiazole copolymers,27,28 diketopyrrolopyrrole (DPP) based copolymers,29,30 benzodithiophene (BDT) derivatives31,32 as well as indacenodithiophene (IDT) based copolymers.33 This new generation of semiconducting copolymers combine electron-rich segments with electron-deficient units, such as DPPs, along the polymer backbone. The selection of different electron-rich comonomers, such as thiophene, fluorine, or carbazole based units among others, determines the optical bandgap, the energy levels, and the carrier mobility of the resulting copolymer. These LBG donor-acceptor polymers present energy gaps in the range of 1.3 to 1.6 eV enabling light absorption in the near-infrared region, which combined with a fullerene derivative are able to extend the absorption of the organic solar cell to the UV/visible as well.

In the following, some promising copolymers based on previously mentioned units will be analyzed.

2.1.

Polymeric Donors

2.1.1.

Poly (2,7-carbazoles)

The electron-donating nitrogen unit of the central fused pyrrole ring makes carbazoles electron-rich compounds. The solubility of the polymer is ensured by functionalization of the central nitrogen with an alkyl chain (see molecular structure in Fig. 2). Since carbazole derivatives present good thermal and photochemical stability and high charge mobility, they are promising candidates to be incorporated in polymers for photovoltaic applications.22,34,35

Fig. 2

Molecular structure of 2,7-carbazole.

JPE_5_1_057214_f002.png

The conjugation of the carbazole unit to a benzothiadiazole moiety through a thiophene bridge gives rise to a material known as PCDTBT, see Fig. 3. In combination with PC70BM as an acceptor, organic solar cells with power conversion efficiencies >6% have been achieved by several groups.3637.38 These numbers can be improved to 7.2 to 7.5% by using advanced interface materials and antireflection coatings.27,39

Fig. 3

Highest reported efficiencies for different polymers in single devices.

JPE_5_1_057214_f003a.pngJPE_5_1_057214_f003b.png

A slightly different approach has been attempted by conjugating the benzothiadiazole moiety to a dithiophene unit instead of a carbazole one. The result is a polymer known as PCPDTBT (Fig. 3). Organic solar cells with efficiencies up to 5.5% are usually reported for this polymer when it is blended with PC70BM.40 Moreover, by introducing a fluor atom into this molecule (Fig. 3), which lowers the increase of the polymer HOMO level and, thus, the Voc, efficiencies of 6.16% have been also achieved.41

A further modification of this copolymer with two fluor atoms at the benzothiadiazole unit gives rise to a difluorobenzothiadiazole (DFBT) moiety that is further conjugated to a dithienopyran (DTP) segment instead of a single dithiophene. The result is a copolymer known as GPDTP-DFBT (Fig. 3) with efficiencies in single devices of >8% (Ref. 42) and also an outstanding performance in tandem configuration, as we will see in Sec. 4.3. A more developed semicrystalline version known as PPDT2FBT (Fig. 3) forms a well-distributed nanofibrillar networked morphology with the fullerene, which results in balanced hole and electron mobility, and tight interchain packing. Relatively thick films of 300nm yield record efficiencies of 9.4%.43

2.1.2.

Diketopyrrolopyrroles

Some other promising absorbers for OPV applications are copolymers based on electron-deficient diketopyrrolopyrrole units. The copolymerization of this electron-deficient unit with different electron-rich segments has resulted in solar cells with efficiencies up to 8%.29,4445.46.47.48.49.50.51.52

The most promising candidates consist of the conjugation of the DPP moiety to a thienothiophene fragment with a varying number of interconnecting thiophene units. For the simplest case, Meager et al. reported PDPP-TT-T based devices with efficiencies >7% for some particular alkyl chain branching position manipulation (Fig. 3).53 Hendriks et al. also reported efficiencies >7% by conjugating the DPP segment to different oligothiophenes (nT). The best material from this series (DT-PDPP3T, Fig. 3) uses terthiophene as a comonomer and reaches 7.1%. Higher efficiencies of 7.4% have also been achieved by alternating the DPP unit with thiophene-phenylene-thiophene (TPT) segments—PDPP-TPT—(Fig. 3) due to the improvement in the polymerization reaction. Finally, the highest reported efficiency of 8% for a DPP based polymer has been obtained by combining these segments with a terthiophene unit in order to produce a terpolymer called PDPP3TaltTPT (Fig. 3).52

2.1.3.

Benzodithiophenes

Copolymers based on the alternation of BDT and thieno[3,4-b]thiophene units are also promising absorbers for organic solar cell applications. The thieno[3,4-b]thiophene units stabilize the quinoidal structure of the backbone, thus reducing the energy gap of the polymer to 1.6 eV estimated from the onset of the solid-state absorption (775 nm). The ester substituted thieno[3,4-b]thiophene, instead, makes the polymer soluble and oxidative stable while the rigid backbone ensures a good mobility of holes.54,55

Liang et al. developed several copolymers, known as poly thieno-thiophene benzodithiophenes (PTBs), for which efficiencies up to 7.4% have been achieved by using PTB7 as the absorber (Fig. 3) together with PC70BM as the electron acceptor for conventional configuration devices. This material is also a good example to illustrate that improving the efficiency of an organic solar cell is not only a matter of the active material. Different processing procedures and cell layouts/architectures, as those being described in this review, have taken the efficiency from 6.22 to 9.2%. Standard PTB7 was later modified by incorporating the 2-(2-ethylhexyl)-thienyl group into the BDT unit of PTB7 to produce PTB7-Th (Fig. 3). Incorporating deterministic aperiodic nanostructures (DANs) based on nanoimprint technology on PTB7-Th:PC71BM has resulted in the most efficient single device reported to date with a power conversion efficiency (PCE) of 10.1%.56

Huo et al. also designed and synthesized an interesting thiophene-substituted BDT copolymer with carboxyl-substituted thieno[3,4-b]thiophene, PBDTTT-C-T (Fig. 3), that exhibits good thermal stability and hole mobility. Devices based on PBDTTT-C-T:PCBM processed from orthodichlorobenzene (ODCB) and 3% 1,8-diiodooctane (DIO) resulted in efficiencies of 7.6%.57 This efficiency has been recently pushed up to 8.3% by Adhikary et al. when the cell was exposed to UV-ozone.58 Ye et al. introduced linear alkylthio chains in the BDT-T unit to produce another PBDTTT-based copolymer known as PBDT-TS1 (Table 1) from which record devices of up to 9.48% were obtained.59

Table 1

Device photovoltaic parameters of orthodichlorobenzene (ODCB) only, ODCB with 3% 1,8-diiodooctane (DIO), chlorobenzene (CB), and CB with 3% DIO as solvent.55

Voc (V)Jsc (mA cm−2)Fill factor (FF) (%)PCE (%)Jsc (calc.) (mA cm−2)Error (%)
DCB0.7413.9560.256.22
DCB + DIO0.7414.0968.857.1813.990.74
CB0.7610.2050.523.92
CB + DIO0.7414.5068.977.4014.162.34

A parallel approach conjugated the BDT fragment to thieno[3,4-c]pyrrole-4,6-dione (TPD) units to result in a copolymer known as PBDTTPD (Fig. 3). Devices based on this polymer in combination with PC70BM reached PCE values up to 8.5% and Voc values as high as 0.97 V.60

2.1.4.

Indacenodithiophenes

IDT based copolymers have also resulted in high-efficiency organic solar cells, reporting values >7%.33,61,62 Two cyclopentadiene rings are fused to a benzene in order to form the indaceno unit. This is later joined to a dithiophene fragment to make the IDT moiety, which can then be conjugated to different structures in order to obtain a new family of copolymers. These copolymers generally show high solar flux harvesting, high hole mobility, and deep HOMO energy levels, resulting in devices with Voc values up to 0.9.63,64 Guo et al. developed a copolymer by conjugation of the IDT unit to quinoxaline (Fig. 3), reporting efficiencies >7.5% for devices based on this copolymer (PIDTDTQx:PC70BM).33 Similarly, Fei et al. copolymerized the IDT segment to a benzothiadiazole structure. By heteroatom substitution at the cyclopentadiene rings by either silicon or germanium, they also published efficiencies >6.5% for C2C6GeIDT-BT (Fig. 3) based devices.65

2.2.

New Fullerene Derivatives

Nowadays, almost all reported cells with remarkable efficiencies employ soluble fullerene derivatives as an electron acceptor. Among them, PC60BM and PC70BM are the most widely used. Both of them have the same LUMO values, which considerably limit the Voc of operating devices.

A new n-type fullerene derivative, indene-C60 bis-adduct (ICBA) (see Fig. 4 for the molecular structure) was demonstrated to be a good alternative acceptor. ICBA has a higher LUMO level (3.74eV) in comparison to either PC60BM or PC70BM (4.2eV), which leads to a higher Voc. In this way, P3HT based devices with ICBA as an acceptor resulted in cells with Voc values of 0.84 V and enhanced PCE of 6.5%.66,67

Fig. 4

Molecular structure of indene-C60 bis-adduct.

JPE_5_1_057214_f004.png

Cheng et al. also reported P3HT based inverted solar cells using ICBA as an acceptor with a Voc of 0.82 V and a PCE of 4.8%. Further improvement was carried out by the incorporation of a cross-linked fullerene derivative interlayer, C-PCBSD, resulting in the following configuration: ITO/ZnO/C-PCBSD/ICBA:P3HT/PEDOT:PSS/Ag. The incorporation of C-PCBSD increased the photocurrent from 10.6 to 12.4mAcm2 and the FF from 55 to 60%, and, thus, pushed up the PCE to 6.2%.68

Many other fullerene derivatives such as bisadducts,5 diphenylmethano fullerenes,69 dimethylphenylmethano fullerene bisadducts,70 and endohedral fullerenes71,72 are also being synthesized and tested in the search for large Voc devices based on internal bulk polymer:fullerene heterojunction systems. In spite of these advances in the synthesis of new fullerenes, and even though soluble C70 derivatives, on average, yield a 10% increase in photocurrent in comparison to C60 ones thanks to a slightly increased absorption in the visible, the lack of a stronger absorption in the visible and in the infrared still hinders further developments in achieving higher conversion efficiencies. Non fullerene containing heterojunction thin films can overcome these shortcomings, since the energy levels (and, hence, absorption) can be modified through the choice of co-couple units due to the well-distributed frontier molecular orbitals.73,74

3.

Strategies: Fabrication/Processing Procedures

The morphology of the film in BHJ solar cells is a critical parameter to control the exciton dissociation rate, optimize charge transport, minimize bulk recombination, maximize the photocurrent, and, hence, enhance the efficiency of the device.75 On one hand, a large number of donor/acceptor interfaces is required in order to dissociate a large number of photogenerated excitons. On the other hand, the domain size of each material phase and the interconnection between them is also important for an efficient charge transport to the corresponding electrodes. Therefore, an optimum balance among the interface area, domain size, and interconnection is required to result in efficient BHJ solar cells.13 This is schematically represented in Fig. 5.

Fig. 5

Bulk heterojunction devices with different nanomorphologies. (a) Small domains with a large number of interfaces: large charge generation yield but nonefficient charge transport due to recombination. (b) Excessively large domains with a lower interface area between the donor and acceptor: low charge generation yield but good charge transport. (c) Intermediate domain size with an optimized interface area: large charge generation yield and good charge transport.

JPE_5_1_057214_f005.png

Solvent annealing, slow drying, and thermal annealing are few examples of how to deliberately influence the nanomorphology of the polymeric film.1112.13.14.15 Additionally, the use of additives and different solvent mixtures has also been recently demonstrated as an easy and efficient approach to modify and control the morphology of the photoactive layer.1617.18,44

3.1.

Use of Additives

Additives are used for the generation of a more favorable nanomorphology for the transport of electrons and holes, thereby enhancing the final efficiency of the device. Additives do not react with the polymer or with the fullerene; the only aim is to favor the bicontinuous percolation pathways for exciton dissociation and charge transport. Two basic requirements for the correct choice of an additive are (1) the boiling point of the additive has to be much higher than the primary solvent and (2) only one component will be selectively dissolved in the additive. For example, considering polymer:fullerene blends, only the fullerene is selectively dissolved in the selected additive.17

Some of the most studied additives are based on alkanedithiols. Due to the ability of alkanedithiols to selectively dissolve the fullerene component while the polymer is less soluble, an optimum nanomorphology is formed.17 Peet et al. compared the performance of P3HT and PCPDTBT devices processed from pristine solvents and with blends of the same primary solvent and different alkanedithiols. They reported improvements in the PCE from 2.8 to 5.5% when 1,8-octanedithiol was added to chlorobenzene (CB).40

1,8-di(R)octanes with different functional groups (R) are also often used as additives in order to favor the nanomorphology of the film, which improves device efficiency. Figure 6 represents the influence of DIO on the final morphology of the film. When no additives are used, there are big aggregates of fullerene and the penetration of the acceptor molecules in the polymer network is more difficult, resulting in large fullerene and polymer domains. On the contrary, DIO is a much better solvent for the fullerene than CB while the polymer has limited solubility in DIO and is very well dissolved in CB. With the addition of DIO in this case, the fullerene is selectively dissolved, facilitating the percolation of acceptor molecules in the polymer network, resulting in a more favorable nanomorphology of the film due to the optimization of the domain size and polymer:fullerene interface.18

Fig. 6

Graphical sketch of polymer and fullerene when using only chlorobenzene as a solvent (a) and with diiodooctane as an additive (b).18

JPE_5_1_057214_f006.png

The work carried out by Liang et al. for devices based on PTB7 show the influence of DIO on device performance when using it as additive.55 Preliminary studies showed that PTB7:PC70BM (11.5) films prepared from ODCB and DIO (97%:3% in volume) increased the FF from 60.25 to 68.9% and the PCE from 6.22 to 7.18%, in comparison to devices processed from pristine ODCB. In this case, the photocurrent remained constant. However, when CB was used as the primary solvent, a considerable increment was also observed in the photocurrent (from 10.2 to 14.5mAcm2). Also, the FF rose from 50.52 to 69%. In this way, it was possible to improve the efficiency from 3.92% (when CB was used as solvent) up to 7.4% when DIO was used as an additive. All these data are collected in Table 1. They also studied the influence of the additive on the morphology of the active layer by transmission electron microscopy. Images revealed that DIO promotes the formation of smaller domains. The film also showed a higher uniformity due to the good miscibility between PTB7 and PC70BM and the formation of an interpenetrating network. In this way, higher FF and photocurrent values were achieved, thus increasing the PCE.

Some other works have also shown the potential of DIO as an additive to improve the performance of devices made from different active materials. Lee et al. demonstrated an enhancement from 3.4 up to 5.1% by using DIO in BHJ organic solar cells based on PCPDTBT:PC70BM systems.16 Zhang et al. reported a PCE increment from 1.4 to 4.8% when DIO was used as the additive to process devices from an LBG polymer consisting of thieno-thiophene substituted BDT (PTTBDT-C8).76 Finally, Bijleveld et al. also documented the use of DIO for processing devices with DPPs.29 They also observed an enhancement in the PCE from 2 to 5.6% and substantial changes in the film morphology when DIO was added to chloroform.

3.2.

Solvent Mixtures

Similarly to additives, the combination of two or more solvents with different boiling points and limited solubility for one of the components can help control the nanomorphology of the polymeric blend. Janssen et al. reported the influence of adding ODCB to chloroform in a series of DPP based device performance.44,77 The analysis was based on a narrow bandgap polymer known as pBBTDPP2, in combination with PC60BM or PC70BM diluted in chloroform (CHCl3), ODCB, or a mixture of both solvents. When the polymer:fullerene was dissolved in chloroform, just 1.1% of PCE was achieved. This low performance was attributed to the amorphous nature of the deposited layer. When using ODCB instead, due to the limited solubility of pBBTDPP2 in this solvent, after spin-casting the solution, films with larger degrees of crystallinity were obtained, which resulted in devices with higher photocurrent values and, thus, higher PCEs, 2.9%. The PCE of pBBTDPP2 based devices was significantly improved by combining chloroform and ODCB. With the combination of these two solvents in a ratio of 41, a large amount of semicrystalline polymer film was obtained. In this way, PCE values of 3.2 and 4% were achieved when using PC60BM and PC70BM as electron acceptors, respectively. Due to the large difference in vapor pressure, the final film morphology was essentially determined by the slow evaporation of ODCB, leaving the polymer sufficient time to partly crystallize before precipitation. Cells from chloroform:ODCB, apart from higher photocurrent values, also provided higher FFs with respect to the other two options (see Table 2).

Table 2

Photovoltaic parameters of pBBTDPP2:PCBM solar cells.44

Jsc (SR)a (mA cm−2)Jscb (mA cm−2)FFVoc (V)PCE (%)
pBBTDPP2:[60]PCBM from chloroform2.42.40.410.781.1
pBBTDPP2:[60]PCBM from ODCB suspension9.29.40.470.662.9
pBBTDPP2:[60]PCBM from chloroform:ODCB9.09.40.540.633.2
pBBTDPP2:[70]PCBM from chloroform:ODCB11.511.30.580.614.0

a

Determined from convolution of the spectral response with the air mass (AM) 1.5G solar spectrum (1000  W/m2).

b

Determined from J−V measurements under simulated AM 1.5G illumination (1000  W/m2).

Zhang et al. also observed a significant enhancement in the photocurrent density for a polyfluorene copolymer/fullerene blend. When introducing a small amount of CB into the chloroform solvent, a uniform domain distribution was reached, resulting in more efficient devices.78 In further studies, 1-chloronaphthalene in ODCB or small amounts of nitrobenzene in CB have also been used as additives for P3HT:PCBM based devices in order to improve device performance with the aim of achieving a higher degree of crystallinity.79,80

3.3.

Postprocessing Treatments

The possibility to act on film morphology during and after the deposition process has also been thoughtfully studied. First, it is possible to quite accurately control the drying time of the films by using alternative depositing techniques to spin-coating, as, for example, Dr. Blading. Based on the work carried out by Li et al. about the slow drying for film nanomorphology control in conventional architecture devices,11 Ajuria also slowed down the drying process of the P3HT:PCBM photoactive film in inverted configuration devices [600-nm-thick photoactive layer, see Fig. 7(a)].81 Film drying times were delayed from 1 to 2 s to 10 and 30s for films dried directly in air, protecting the film with a Petri dish as a lid in order to limit the contact of the film with air and create a solvent atmosphere below the Petri plate to minimize the presence of air, respectively.

Fig. 7

(a) Field emission scanning electron microscopy cross-sectional view of an inverted ITO/ZnO/P3HT:PCBM/PEDOT:PSS/Au solar cell. Different layers and their thickness are depicted. (b) JV curves of different photoactive layer drying techniques.81

JPE_5_1_057214_f007.png

Results revealed that the slow drying of the film assists the growth of a photoactive self-ordered nanostructure, improving the PCE from 1.44 to 3.57% [see Fig. 7(b) and Table 3]. The self-organization of the polymer has been shown to improve field effect carrier mobilities by more than a factor of 100 in P3HT.82,83 On the contrary, the destruction of self-organized structures during fast drying (unordered growth) present unbalanced charge carriers and lower charge mobilities.11 Under these precisely controlled drying conditions, it is feasible to increase the thickness of the active film up to 600 nm, thus maximizing the light absorption without negatively affecting charge transport. Raising the Dr. Blade plate temperature from ambient conditions to 70°C had a similar effect.

Table 3

JV characteristics of different photoactive layer drying techniques.81

Lid typeVoc (V)Jsc (mA cm−2)FFPCE (%)
Dry in air0.575.260.481.44
Lid0.596.300.481.78
Lid + CB0.599.650.623.57

Alternatively, some other approaches to later manipulate the bulk morphology once the film has been already deposited from solution have been attempted with successful results. Zhou et al. spin-coated methanol on top of an already dry active layer comprising PTB7:PC70BM.84 They reported simultaneous improvements on device series resistance, charge mobility, charge recombination, and charge extraction mainly by means of surface modification. All these improvements gave rise to enhanced Jsc and FF, which lead to 7.9% PCE devices in comparison to 7.1% for nontreated films.

Finally, a novel approach explores the viability of vapor printing as a fast postprocessing technique.85,86 A carrier gas transporting the vapor solvent is delivered through a nozzle promoting local self-assembly of polymer chains. This enables finding an optimal nanostructure in promisingly short times. Changes in the degree of crystallinity led to a twofold increase in PCE with respect to as-cast samples.

4.

Device Layout/Architectures

All the layers that form an organic solar cell have a direct influence on the performance of the device. Buffer interlayers are of crucial interest in order to increase the efficiency of devices. The working principles behind these—sometimes insulating materials—are not yet totally understood. Some of them are used to smooth out the rough profile of underlying films and avoid shunts. Others are used to modify the work function of the metal and align it to some extent with the HOMO and LUMO levels of the semiconductor, thus favoring an ohmic contact. Last but not least, ionic compounds are believed to form interfacial dipoles that help charge injection/extraction and, at the same time, generate optimal optical interferences that improve the light harvesting of devices.87,88

The device architecture can also alter the efficiency of an organic cell. In some cases, inverting the polarity of the cell can also have a positive influence on device performance due to vertical segregation of the mixed compounds that generate a more favorable donor and acceptor material concentration gradient, leading to a more efficient charge-transport process through the film.89,90

Moreover, the processing of more complicated architectures, such as tandem cells that comprise two connected cells made of polymers with complementary absorption spectra, can also result in high efficiency devices due to enhanced light absorption.19

All these device layout/architecture aspects that have a direct influence on the PCE of devices, but are not strictly related to either absorbers’ intrinsic properties or the nanomorphology of the film, will be addressed in this section.

4.1.

Alternative Interlayers

An efficient charge extraction process following light absorption and charge generation requires the use of conducting electrodes wisely chosen in order to have energetic levels alignment and, hence, ideally ohmic contacts between the metal and the semiconductor, thus avoiding charge barriers and undesired losses. Depositing an extra buffer layer between the photoactive film and the metallic electrode has been demonstrated as an efficient way to improve the contact properties.

Indium tin oxide (ITO) is typically used as the bottom contact (anode) in conventional configuration organic solar cells. ITO has a high work function around 4.8 eV, which is very dependent on washing treatments.91,92 However, these variations and the roughness of the resulting films usually result in important contact losses.93 In order to improve the quality of this contact and favor the formation of an ohmic contact, a p-type PEDOT:PSS interlayer, which has a work function of 5 eV, has been traditionally used.94 Due to the acidic nature of PEDOT:PSS and its tendency of being easily degraded in contact with either air or moisture and negatively affecting the stability of the whole device, different transition metal oxides, such as V2O5, MoO3, WO3, and NiO, which are considered more stable, were introduced as alternative p-type interlayers in relatively highly efficient and stable devices.27,95,96 In the cathode side, instead, calcium was initially inherited from the organic light emitting diode (OLED) development as the hole blocking layer due to its low work function. In spite of the good results obtained for photovoltaic devices in combination with silver, it is, however, very reactive to oxygen and moisture and, thus, device stability is further jeopardized. Therefore, alternative inorganic low work function interlayers were introduced. On one side, inorganic salts, such as LiF,9798.99 CsF,100,101 and MgF,102 have been vacuum evaporated in combination with aluminum in order to enhance the contact selectivity and, hence, the PCE. It is believed that due to their high internal dipole moment, thin layers of these materials are able to alter the electrode work function by inducing a shift of the vacuum energy level. Regardless of the increase in efficiency obtained with the use of these materials, they are principally vacuum deposited, which hinders the way toward lower-cost devices based on R2R processing. Solution processable alternatives make use of salts like ZnS,103 LiAc,104 or Cs2CO3.105106.107 Furthermore, polymeric salt compounds, known as polyelectrolytes, have been used with promising results.108 Also, small molecules with opposing internal charges, zwitterions, have been demonstrated as interfacial layers in organic solar cells.109,110 Khan et al. demonstrated efficient conventional configuration P3HT:ICBA based solar cells substituting the Ca layer with a thin film of a hydrophilic polymer processed from a polyethylenimine, 80% ethoxylated solution, PEIE.111 As a result, devices with a Voc of 0.78 V, Jsc of 9.1mAcm2, FF of 65%, and PCE of 4.6% were achieved.

On the other side, as previously commented on for the anode, solution processable films of n-type inorganic semiconductors, such as TiOx and ZnO, processed from nanoparticle dispersions are typically used as n-type interlayers.112113.114.115 Nowadays, many research groups, mainly motivated by the improvement observed in the FF and the parallel resistance, have focused their investigation on alternative interlayers that can further enhance the device’s overall performance.

As it was shown in Sec. 3.1, Liang et al. improved the PCE of ITO/PEDOT:PSS/PTB7:PC70BM/Ca/Al based organic solar cells from 3.92 to 7.40% by adding 3% of DIO to the primary solvent CB.55 However, more specifically related to the use of effective interlayers, further improvement was carried out by He et al. when a thin polymeric film of poly [(9,9-bis(3´-(N , N—dimethylamino) propyl)-2,7-fluorene)- alt -2,7-(9,9–dioctylfluorene)] (PFN) was incorporated as the cathode interlayer, increasing the PCE to 8.22%. Significant and simultaneous enhancements in JSC, Voc, and FF were observed.116 PFN is an alcohol/water soluble conjugated polymer that creates an interfacial dipole between the PFN and the polymeric PTB7:PC70BM blend. Moreover, the incorporation of PFN is believed to exert a strong electric field at the active layer/cathode interface, which may strongly influence charge transport and extraction. Thus, the effects of the interlayer on the improvement of device performance were due to improved charge-transport properties, reduction of any possible space charge effect at the interface, and reduced surface recombination losses.117 Regarding dipole formation at this interface and related to morphology issues, which were previously addressed in Sec. 3.3, it has been recently suggested that vertical segregation of the fullerene content toward the cathode can also result in interfacial dipoles of varying strength, which affect the selectivity of the contact in a similar way as buffer interlayers.118,119

Alternatively, Martínez-Otero et al. incorporated bathocuproine (BCP) as the interlayer of the cathode to achieve an optimal optical interference for PBDTTT-C and PTB7 based devices. As a result, for devices processed with BCP as the interlayer instead of Ca, an increment in PCE from 6.3 to 7.5% was observed for PBDTTT-C based cells and from 7.4 to 8.1% for the PTB7 based ones.88 In the case of PTB7, the increment in PCE was related to the increase in photocurrent due to the enhanced reflectivity of the buffer layer/electrode back contact. For the PBDTTT-C instead, apart from the photocurrent improvement, the FF was also enhanced from 60.3 to 67.9%, which was related to the reduction of recombination at the interfaces.

4.2.

Inverted Configuration

As previously commented on at the beginning of Sec. 4, inverting the polarity of the device and processing the electron collecting electrode onto the ITO and the hole collection electrode on top of the active layer has also been successfully used to increase the efficiency of devices made with the same active materials. Ajuria et al. documented this effect for P3HT:PCBM devices for which impressive FFs >70% were reported for inverted designs.120

In the case of PTB7 devices, further improvement in PCE was observed by He et al. when inverting the polarity of the device, reaching a very remarkable 9.2%.87 As it can be seen in Fig. 8 and Table 4, the efficiency improvement for inverted structure devices is mainly due to the larger Jsc with respect to the conventional one, 17.2mAcm2 in comparison to 15.4mAcm2, respectively. The drastically enhanced Jsc for inverted devices was assigned to an improved ohmic contact, which eases photogenerated charge carrier collection and an optimum photon harvesting of these devices.

Fig. 8

Performance for inverted configuration (red filled symbols) (ITO/PFN/PTB7:PC70BM/MoO3/Al) and conventional configuration (black open symbols) (ITO/PEDOT:PSS/PTB7:PC70BM/PFN/Ca) devices. (a) Current density-voltage measurements and (b) external quantum efficiency (EQE) graph.87

JPE_5_1_057214_f008.png

Table 4

Best device performance/parameters for PTB7:PC70BM based conventional and inverted solar cells with PFN as interlayer.87

Device typePCE (%)Jsc (mA cm−2)FF (%)Voc (V)
Conventional8.2415.470.60.759
Inverted9.1517.272.00.740
Inverted, tested by CPVT9.21417.4669.990.754

CPVT, National Center of Supervision and Inspection on Solar Photovoltaic Products Quality of China.

The interlayers used for inverted configurations can also be exposed to different treatments in order to modify their intrinsic properties and try to improve device efficiency. Adhikary et al. improved PBDTTT-CT:PC70BM based inverted configuration devices from 6.46 to 8.34% by exposing the cell to UV-ozone.58 This treatment modifies the wurtzite phase crystallinity of the ZnO films, leading to faster film mobilities and improved charge extraction properties. While exposure times around 5 min resulted in an ideal crystalline structure, longer exposure times induced the formation of p-type defects, pushing the ZnO Fermi-level further away from the vacuum level and decreasing the wurtzite crystallinity.

The work function of the materials can also be manipulated by surface modifiers. Zhou et al. demonstrated that compounds based on polymers containing simple aliphatic amine groups can substantially reduce the work function of conductors, including metals, transparent conductive metal oxides, conducting polymers, and graphene.121 Kyaw et al. incorporated PEIE on top of ZnO to enhance the efficiency of the cell by lowering the work function of ZnO (from 4.5 to 3.8 eV).122 With this surface modification, the PCE was enhanced from 6.29 to 7.88% thanks to simultaneous enhancements in Jsc, Voc, and FF.

4.3.

Tandem Cells

The main losses that occur in a solar cell are transmission and thermalization losses [see Fig. 9(a)]. Photons with lower energy than the energy bandgap will not be able to generate excited states, resulting in transmission losses. On the contrary, photons with energies larger than the energy bandgap will generate hot charge carriers that will relax down to the LUMO of the polymer, giving rise to thermalization losses.7,123124.125 By stacking together in the same device two cells with polymers that absorb at different wavelengths, i.e., wide- and low-bandgap polymers, these losses can be reduced. The reduction in thermalization losses can be carried out by conversion in the subcell with a wide-bandgap polymer. On the other hand, transmission losses are lowered by absorption of the low energy photons in the subcell with a small-bandgap polymer. This results in polymer solar cells with ideally enhanced power conversion efficiencies.

Fig. 9

(a) Thermodynamic losses related to light absorption. (b) Layout of an organic tandem cell with two devices stacked one on top of another.

JPE_5_1_057214_f009.png

Tandem solar cells basically consist of stacking two or more devices one on top the each other with an adequate interlayer between them [see Fig. 9(b)]. The first deposited subcell is usually referred to as the front cell, while the one that is deposited on top is referred as the back cell. The connection among the subcells can be performed either in series (two terminals) or in parallel (three terminals).125126.127 The front layer should ideally absorb only most of the light corresponding to wavelengths of its maximum absorption coefficient. On the contrary, the light that is not absorbed by the front cell, belonging to wavelengths of maximum absorption of the second layer, will be more efficiently absorbed by the polymer of the back cell. Thus, the solar irradiance is absorbed in a more efficient manner without the need of thick layers that can induce charge transport losses.

Simple models have been developed for organic tandem devices in order to predict the efficiency increase when going from single to tandem cells. These models are based on the energy bandgaps of the absorbers used in each subcell and efficiencies up to 15% are estimated with the appropriate combination of materials.128,129

One of the first reports about organic tandem solar cells with two identical small molecule subcells stacked together separated by a thin gold layer was published in 1990 by Hiramoto et al.130 However, due to the limited choice of small molecule materials with significantly different absorption spectra, they started exploring hybrid tandem cells combining polymer and small molecule subcells.131132.133.134.135 In 2005, Kawano et al. reported the first tandem cells composed of two identical polymer BHJ subcells stacked together with an interlayer comprising sputtered ITO and spin-coated PEDOT:PSS.136 One year later, Hadipour et al. showed a tandem cell consisting of subcells based on low- and wide-bandgap polymers with complementary absorptions.137 However, all these attempts resulted in efficiencies <5% and many times even below those efficiencies reported for single cells made with one of the same comprising materials. A major breakthrough in the area of polymeric tandem cells was the demonstration of all solution processable polymer tandem cells with efficiency >6% by Kim et al.138 More recently, in 2010, Gilot et al. studied the effect of current matching on the tandem device performance, which provides more insight in order to achieve high-performance tandem cells.139 It is worth saying that the performance of polymeric tandem cells during the last four years has been limited to 7% mainly due to the lack of high-performing low-bandgap polymers.139140.141.142 Nevertheless, in 2012, Dou et al. designed a new LBG polymer and achieved an inverted configuration tandem device with 8.6% PCE.143,144 Recently, Li et at. demonstrated tandem and triple-junction polymer solar cells with power conversion efficiencies of 8.9 and 9.6%, respectively, by combining an LBG polymer known as PMDPP3T (with absorption in the near-infrared region up to 960 nm) and the wide-bandgap polymer PCDTBT.20

Single cells based on PMDPP3T:PC60BM and PCDTBT:PC70BM result in devices of 6 and 4.7% PCE, respectively. However, using the same layer thicknesses and stacking the subcells in a tandem cell [see Fig. 10(a)], the PCE was enhanced to 8.9%. Further improvement in the efficiency of the organic solar cell was carried out by adding an additional layer of the same small-bandgap material, creating a triple-junction device, as the one depicted in Fig. 10(d). In a tandem cell, the Jsc is limited by the wide-bangap front cell. However, this limitation is circumvented by splitting the small-bandgap subcell into two separate cells (middle and back cell) with different thicknesses to ensure that both absorb the same number of photons. The increase in Voc of the triple junction (2.09 V with respect to 1.49 V) compensates the loss in Jsc [compare Figs. 10(b) and 10(c) with Figs. 10(e) and 10(f)]. In this way, the efficiency was enhanced up to 9.6%.20

Fig. 10

Tandem and triple junction device layout [(a) and (d)], JV characteristics [(b) and (e)], and EQE graph [(c) and (f)].20

JPE_5_1_057214_f010.png

Efficiencies up to 10.2% have been published by You et al. by stacking together in a tandem device two identical subcells based on PDTP-DFBT:PC70BM.145 It is worth mentioning that single PDTP-DFBT:PC70BM based devices provide efficiencies of 8.1%. The absorption in the visible part of the tandem cell was significantly increased from 70 to 90% with respect to that of the single cell, suggesting that the performance of single cells for this material is a difficult compromise between light absorption and charge transport. Films of 80 nm are not able to absorb all the light; thicker films of 120 nm yield higher photocurrents (19mAcm2) but smaller FF (58%) than those for thinner films of 80 nm (17mAcm2 and 65%, respectively). When implemented in a tandem configuration, however, it is preferred to have efficient charge transport since the lack of absorption of thinner films can be compensated by the extra absorption of the second cell that additionally offers a gain in Voc.

The best polymer-fullerene tandem solar cells have a reported certified efficiency of 10.6% [see Fig. 11(b)] and feature a response up to 900 nm.19 A wide-bandgap polymer, P3HT, was blended with ICBA in the front cell. As commented previously, this combination allows for a larger Voc in comparison to more standard fullerene derivatives. The LBP PDTP-DFBT was used with either PC60BM or PC70BM as the back cell [see Fig. 11(a)]. In Table 5, the detailed parameters of single and tandem cells are summarized. As can be seen, single cells provide efficiencies of 6.1 and 7.1% for P3HT:ICBA and PDTP-DFBT:PC60BM, respectively. It is remarkable that although the use of PC70BM with the LBG material shows higher efficiencies than PC60BM in single cells, thanks to the extended absorption of the former in comparison to the latter, this is not the case when implemented in tandem configuration. Either the front active film already absorbs at those wavelengths at which PC70BM can represent an improvement with respect to PC60BM and/or the extra current of the back cell breaks the current matching between the front and the back cell. The photocurrent of the tandem is obviously limited by the subcell with the lowest value. This is clearly the case for the tandem that makes use of PC60BM in the back cell, whose photocurrent is very similar to that measured for an equivalent single cell of the front cell. However, when PC70BM is used, the currents of both cells are unbalanced and penalize the overall performance of the tandem with additional losses that result in a photocurrent even lower than that of the limiting subcell. The Voc is the perfect summation of each subcell, resulting in the most efficient reported tandem device to date.

Fig. 11

(a) Device structure of the tandem solar cell. (b) JV characteristics of the tandem cell as measured by NREL.19

JPE_5_1_057214_f011.png

Table 5

Poly(3-hexylthiophene) (P3HT) and PDTP-difluorobenzothiadiazole (DFBT) single junction cell and tandem solar cell performance.19

DevicesVoc (V)Jsc (mA cm−2)FF (%)PCE (%)
P3HT:ICBA0.8410.371.16.1
PDTP-DFBT:PC61BM0.7015.466.27.1
PDTP-DFBT:PC71BM0.6817.865.07.9
P3HT:ICBA/PDTP-DFBT:PC61BM (Tandem 1)1.5310.168.510.6a
P3HT:ICBA/PDTP-DFBT:PC71BM (Tandem 2)1.519.869.210.2

Note: ICBA, indene-C60 bis-adduct.

a

Values are measured and certified by National Renewable Energy Laboratory.

Even though, as commented before, triple-junction devices can in some cases minimally improve the performance of tandem cells,20 they are very difficult and costly to implement. The enhancement obtained in terms of efficiency does not always compensate these two issues and one has to carefully analyze whether this approach is worth taking into account for a potential mass production. In any case, and considering only efficiency issues, an efficient triple-junction tandem organic solar cell with a record conversion efficiency of 11.5% has been recently published.146 Three complementary absorbers with bandgap energies from 1.4 to 1.9 eV are used to obtain balanced absorption rates and matched photocurrents among the three subcells. In similar terms, Yusoff et al. made use of a combination of a wide-bandgap, a medium-bandgap, and low-bandgap materials to report double-junction devices of 10.4% and a record efficiency of 11.83% for a triple-junction cell.147 The wide-bandgap material was a copolymer based on the alternation of dithienolsilole, thiophene, and thiazolothiazole segments (PSEHTT), whose bandgap lies at 1.82 eV, while the medium- and low-bandgap materials were the already introduced PTB7 (1.6 eV) and PMDPP3T (1.3 eV), respectively. Apart from the active materials, this work also makes use of all the other concepts mentioned in the other sections of this review, introducing, for example, new interlayers based on lithium zinc oxide and C60 self-assembled monolayers. The resulting devices show an impressive JSC of 10.30 and 7.83mAcm2, FF of 65.5 and 67.5, and Voc of 1.54 and 2.24 V for the tandem (PSEHTT:ICBA//PTB7:PC70BM) and triple device (PSEHTT:ICBA//PTB7:PC70BM//PMDPP3T:PC70BM), respectively.

5.

Summary

In this paper, we have initially presented the fundamental limits of polymeric solar cells, the factors that limit their performance, and the different possible approaches to maximize this. We have then offered a comprehensive and detailed review of the most efficient attempts to overcome the long ambitioned 10% PCE in polymeric devices. We have divided the development of polymeric solar cells in three categories indicating the most efficient efficiencies achieved for every case:

  • Materials:

    • 10% PCE devices have been reported for a BDT device (PTB7-Th) incorporating DANs) for broad-angle light manipulation.

    • 9% PCE devices have been reported for BDT and dithienopyran- difluorobenzothiadiazole derivatives as PTB7, PBDT-TS1, and PPDT2FBT.

    • 8% PCE devices have been published for:

      • A fluorinated benzothiadiazole unit conjugated to a dithienopyran segment (PDTP-DFBT)

      • Complicated conjugations of the diketopyrrolopyrrole moiety to thiophene-phenylene-thiphene segments in combination to a terthiophene unit (PDPP3TaltTPT)

      • A fluorinated benzothiadiazole unit conjugated to a benzodithiophene unit (PBDT2FBT)

    • 7% PCE devices are already routinely achieved with the use of multiple diketopyrrolopyrrole and IDT derivatives

    • Traditional fullerene derivatives, such as PC60BM and PC70BM, are still used in all the most efficient reported devices.

  • Strategies (fabrication/processing procedures): With the use of additives, solvent mixtures, and postprocessing treatments, it is possible to obtain an accurate control of the bulk morphology that results in improved efficiencies for a large variety of different polymer families.

  • Device layout/architectures:

    • Alternative interlayers of polymeric films and/or inorganic semiconducting oxides have considerably improved the PCE of devices, reaching 9% for the most efficient donors.

    • Inverted configuration has also been demonstrated as an efficiency improvement for different polymeric donors, in particular for benzodithiophenes as PTB7 and PBDTTT with overall efficiencies >9% and 8%, respectively.

    • Tandem cells are the best approach to maximize light harvesting and device efficiency. The record reported polymeric device yields 10.6% and makes use of a single polythiophene, such as P3HT, as the wide-bandgap absorber and a fluorinated benzothiadiazole derivative (PDTP-DFBT) as the LBG absorber. Three complementary absorbers implemented in a triple-junction solar cell have taken the record efficiency of organic solar cells to 11.83%.

All these concepts and highlights are summarized in Fig. 12.

Fig. 12

List of most efficient polymer:fullerene solar cells published to date.

JPE_5_1_057214_f012.png

Acknowledgments

We thank the European Community’s Seventh Framework Programme (FP72007-2013) under Grant Nos. 287818 and 604397 of the X10D and ARTESUN projects, respectively, for providing financial support.

References

1. J. Nelson, The Physics of Solar Cells, Imperial College Press, Covent Garden, London (2003). Google Scholar

2. M. C. Scharber and N. S. Sariciftci, “Efficiency of bulk-heterojunction organic solar cells,” Prog. Polym. Sci. 38, 1929–1940 (2013).PRPSB80079-6700 http://dx.doi.org/10.1016/j.progpolymsci.2013.05.001 Google Scholar

3. N. Li et al., “Environmentally printing efficient organic tandem solar cells with high fill factors: a guideline towards 20% power conversion efficiency,” Adv. Energy Mater. 4(11), 1400084 (2014).ADEMBC1614-6832 http://dx.doi.org/10.1002/aenm.201400084 Google Scholar

4. C. J. Brabec et al., “Origin of the open circuit voltage of plastic solar cells,” Adv. Funct. Mater. 11, 374–380 (2001).AFMDC61616-3028 http://dx.doi.org/10.1002/(ISSN)1616-3028 Google Scholar

5. M. Lenes et al., “Fullerene bisadducts for enhanced open-circuit voltages and efficiencies in polymer solar cells,” Adv. Mater. 20, 2116–2119 (2008).ADVMEW0935-9648 http://dx.doi.org/10.1002/(ISSN)1521-4095 Google Scholar

6. F. B. Kooistra et al., “Increasing the open circuit voltage of bulk-heterojunction solar cells by raising the LUMO level of the acceptor,” Org. Lett. 9, 551–554 (2007).ORLEF71523-7060 http://dx.doi.org/10.1021/ol062666p Google Scholar

7. G. Dennler, M. C. Scharber and C. J. Brabec, “Polymer-fullerene bulk-heterojunction solar cells,” Adv. Mater. 21, 1323–1338 (2009).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.v21:13 Google Scholar

8. J. K. J. van Duren et al., “Low-bandgap polymer photovoltaic cells,” Synth. Met. 121, 1587–1588 (2001).SYMEDZ0379-6779 http://dx.doi.org/10.1016/S0379-6779(00)01307-2 Google Scholar

9. A. Dhanabalan et al., “Synthesis and characterization of a low bandgap conjugated polymer for bulk heterojunction photovoltaic cells,” Adv. Funct. Mater. 11, 255–262 (2001).AFMDC61616-3028 http://dx.doi.org/10.1002/(ISSN)1616-3028 Google Scholar

10. T. Stübinger and W. Brütting, “Exciton diffusion and optical interference in organic donor-acceptor photovoltaic cells,” J. Appl. Phys. 90, 3632–3641 (2001).JAPIAU0021-8979 http://dx.doi.org/10.1063/1.1394920 Google Scholar

11. G. Li et al., “High-efficiency solution processable polymer photovoltaic cells by self-organization of polymer blends,” Nat. Mater. 4, 864–868 (2005).NMAACR1476-1122 http://dx.doi.org/10.1038/nmat1500 Google Scholar

12. W. Ma et al., “Thermally stable, efficient polymer solar cells with nanoscale control of the interpenetrating network morphology,” Adv. Funct. Mater. 15, 1617–1622 (2005).AFMDC61616-3028 http://dx.doi.org/10.1002/(ISSN)1616-3028 Google Scholar

13. H. Hoppe and N. S. Sariciftci, “Morphology of polymer/fullerene bulk heterojunction solar cells,” J. Mater. Chem. 16, 45–61 (2006).JMACEP0959-9428 http://dx.doi.org/10.1039/b510618b Google Scholar

14. S. Sam-Shajing et al., “Photovoltaic enhancement of organic solar cells by a bridged donor-acceptor block copolymer approach,” Appl. Phys. Lett. 90, 043117 (2007).APPLAB0003-6951 http://dx.doi.org/10.1063/1.2437100 Google Scholar

15. S. Miller et al., “Investigation of nanoscale morphological changes in organic photovoltaics during solvent vapor annealing,” J. Mater. Chem. 18, 306–312 (2008).JMACEP0959-9428 http://dx.doi.org/10.1039/b713926h Google Scholar

16. J. K. Lee et al., “Processing additives for improved efficiency from bulk heterojunction solar cells,” J. Am. Chem. Soc. 130, 3619–3623 (2008).JACSAT0002-7863 http://dx.doi.org/10.1021/ja710079w Google Scholar

17. A. Pivrikas, H. Neugebauer and N. S. Sariciftci, “Influence of processing additives to nano-morphology and efficiency of bulk-heterojunction solar cells: a comparative review,” Sol. Energy 85, 1226–1237 (2011).SRENA40038-092X http://dx.doi.org/10.1016/j.solener.2010.10.012 Google Scholar

18. S. J. Lou et al., “Effects of additives on the morphology of solution phase aggregates formed by active layer components of high-efficiency organic solar cells,” J. Am. Chem. Soc. 133, 20661–20663 (2011).JACSAT0002-7863 http://dx.doi.org/10.1021/ja2085564 Google Scholar

19. J. You et al., “A polymer tandem solar cell with 10.6% power conversion efficiency,” Nat. Commun. 4, 1446 (2013).NCAOBW2041-1723 http://dx.doi.org/10.1038/ncomms2411 Google Scholar

20. W. Li et al., “Efficient tandem and triple-junction polymer solar cells,” J. Am. Chem. Soc. 135, 5529–5532 (2013).JACSAT0002-7863 http://dx.doi.org/10.1021/ja401434x Google Scholar

21. E. Bundgaard and F. C. Krebs, “Low band gap polymers for organic photovoltaics,” Sol. Energy Mater. Sol. Cells 91, 954–985 (2007).SEMCEQ0927-0248 http://dx.doi.org/10.1016/j.solmat.2007.01.015 Google Scholar

22. Y.-J. Cheng, S.-H. Yang and C.-S. Hsu, “Synthesis of conjugated polymers for organic solar cell applications,” Chem. Rev. 109, 5868–5923 (2009).CHREAY0009-2665 http://dx.doi.org/10.1021/cr900182s Google Scholar

23. M. T. Dang, L. Hirsch and G. Wantz, “P3HT:PCBM, best seller in polymer photovoltaic research,” Adv. Mater. 23, 3597–3602 (2011).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.201100792 Google Scholar

24. Y. Kim et al., “A strong regioregularity effect in self-organizing conjugated polymer films and high-efficiency polythiophene:fullerene solar cells,” Nat. Mater. 5, 197–203 (2006).NMAACR1476-1122 http://dx.doi.org/10.1038/nmat1574 Google Scholar

25. F. C. Krebs et al., “Large area plastic solar cell modules,” Mater. Sci. Eng. B 138, 106–111 (2007).MSBTEK0921-5107 http://dx.doi.org/10.1016/j.mseb.2006.06.008 Google Scholar

26. F. C. Krebs et al., “Strategies for incorporation of polymer photovoltaics into garments and textiles,” Sol. Energy Mater. Sol. Cells 90, 1058–1067 (2006).SEMCEQ0927-0248 http://dx.doi.org/10.1016/j.solmat.2005.06.003 Google Scholar

27. Y. Sun et al., “Efficient, air-stable bulk heterojunction polymer solar cells using MoOx as the anode interfacial layer,” Adv. Mater. 23, 2226–2230 (2011).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.v23.19 Google Scholar

28. S. Beaupre and M. Leclerc, “PCDTBT: en route for low cost plastic solar cells,” J. Mater. Chem. A 1, 11097–11105 (2013).JMACEP0959-9428 http://dx.doi.org/10.1039/c3ta12420g Google Scholar

29. J. C. Bijleveld et al., “Efficient solar cells based on an easily accessible diketopyrrolopyrrole polymer,” Adv. Mater. 22, E242–E246 (2010).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.201001449 Google Scholar

30. H. Bronstein et al., “Thieno[3,2-b]thiophene-diketopyrrolopyrrole-containing polymers for high-performance organic field-effect transistors and organic photovoltaic devices,” J. Am. Chem. Soc. 133, 3272–3275 (2011).JACSAT0002-7863 http://dx.doi.org/10.1021/ja110619k Google Scholar

31. Y. Liang et al., “Development of new semiconducting polymers for high performance solar cells,” J. Am. Chem. Soc. 131, 56–57 (2009).JACSAT0002-7863 http://dx.doi.org/10.1021/ja808373p Google Scholar

32. Y. Liang et al., “Highly efficient solar cell polymers developed via fine-tuning of structural and electronic properties,” J. Am. Chem. Soc. 131, 7792–7799 (2009).JACSAT0002-7863 http://dx.doi.org/10.1021/ja901545q Google Scholar

33. X. Guo et al., “Influence of D/A ratio on photovoltaic performance of a highly efficient polymer solar cell system,” Adv. Mater. 24, 6536–6541 (2012).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.v24.48 Google Scholar

34. N. Blouin, A. Michaud and M. Leclerc, “A low-bandgap poly(2,7-carbazole) derivative for use in high-performance solar cells,” Adv. Mater. 19, 2295–2300 (2007).ADVMEW0935-9648 http://dx.doi.org/10.1002/(ISSN)1521-4095 Google Scholar

35. N. Blouin et al., “Toward a rational design of poly(2,7-carbazole) derivatives for solar cells,” J. Am. Chem. Soc. 130, 732–742 (2008).JACSAT0002-7863 http://dx.doi.org/10.1021/ja0771989 Google Scholar

36. S. Alem et al., “Effect of mixed solvents on PCDTBT:PC70BM based solar cells,” Org. Electron. 12, 1788–1793 (2011).1566-1199 http://dx.doi.org/10.1016/j.orgel.2011.07.011 Google Scholar

37. S. H. Park et al., “Bulk heterojunction solar cells with internal quantum efficiency approaching 100%,” Nat. Photon. 3, 297–302 (2009).1749-4885 http://dx.doi.org/10.1038/nphoton.2009.69 Google Scholar

38. J. S. Moon, J. Jo and A. J. Heeger, “Nanomorphology of PCDTBT:PC70BM bulk heterojunction solar cells,” Adv. Energy Mater. 2, 304–308 (2012).ADEMBC1614-6832 http://dx.doi.org/10.1002/aenm.201100667 Google Scholar

39. D. H. Wang et al., “Transferable graphene oxide by stamping nanotechnology: electron-transport layer for efficient bulk-heterojunction solar cells,” Angew. Chem. Int. Ed. 52, 2874–2880 (2013).ACIEF51433-7851 http://dx.doi.org/10.1002/anie.201209999 Google Scholar

40. J. Peet et al., “Efficiency enhancement in low-bandgap polymer solar cells by processing with alkane dithiols,” Nat. Mater. 6, 497–500 (2007).NMAACR1476-1122 http://dx.doi.org/10.1038/nmat1928 Google Scholar

41. S. Albrecht et al., “Fluorinated copolymer PCPDTBT with enhanced open-circuit voltage and reduced recombination for highly efficient polymer solar cells,” J. Am. Chem. Soc. 134, 14932–14944 (2012).JACSAT0002-7863 http://dx.doi.org/10.1021/ja305039j Google Scholar

42. L. Dou et al., “Synthesis of 5H-dithieno[3,2-b:2’,3’-d]pyran as an electron-rich building block for donor-acceptor type low-bandgap polymers,” Macromolecules 46, 3384–3390 (2013).MAMOBX0024-9297 http://dx.doi.org/10.1021/ma400452j Google Scholar

43. T. L. Nguyen et al., “Semi-crystalline photovoltaic polymers with efficiency exceeding 9% in a [similar]300 nm thick conventional single-cell device,” Energy Environ. Sci. 7, 3040–3051 (2014).1754-5692 http://dx.doi.org/10.1039/C4EE01529K Google Scholar

44. M. M. Wienk et al., “Narrow-bandgap diketo-pyrrolo-pyrrole polymer solar cells: the effect of processing on the performance,” Adv. Mater. 20, 2556–2560 (2008).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.v20:13 Google Scholar

45. B. Walker et al., “Nanoscale phase separation and high photovoltaic efficiency in solution-processed, small-molecule bulk heterojunction solar cells,” Adv. Funct. Mater. 19, 3063–3069 (2009).AFMDC61616-3028 http://dx.doi.org/10.1002/adfm.v19:19 Google Scholar

46. L. Huo et al., “Bandgap and molecular level control of the low-bandgap polymers based on 3,6-dithiophen-2-yl-2,5-dihydropyrrolo[3,4-c]pyrrole-1,4-dione toward highly efficient polymer solar cells,” Macromolecules 42, 6564–6571 (2009).MAMOBX0024-9297 http://dx.doi.org/10.1021/ma9012972 Google Scholar

47. J. Jo et al., “Bulk heterojunction solar cells based on a low-bandgap carbazole-diketopyrrolopyrrole copolymer,” Appl. Phys. Lett. 97, 203303 (2010).APPLAB0003-6951 http://dx.doi.org/10.1063/1.3508951 Google Scholar

48. J. Ajuria et al., “Nanomorphology influence on the light conversion mechanisms in highly efficient diketopyrrolopyrrole based organic solar cells,” Org. Electron. 14, 326–334 (2013).1566-1199 http://dx.doi.org/10.1016/j.orgel.2012.11.010 Google Scholar

49. J. Li et al., “Design and modification of three-component randomly incorporated copolymers for high performance organic photovoltaic applications,” Polym. Chem. 4, 804–811 (2013).ACPPAY0032-3934 http://dx.doi.org/10.1039/c2py20763j Google Scholar

50. H. Bronstein et al., “Thieno[3,2-b]thiophene-diketopyrrolopyrrole containing polymers for inverted solar cells devices with high short circuit currents,” Adv. Funct. Mater. 23, 5647–5654 (2013).AFMDC61616-3028 http://dx.doi.org/10.1002/adfm.v23.45 Google Scholar

51. J. W. Jung et al., “A high mobility conjugated polymer based on dithienothiophene and diketopyrrolopyrrole for organic photovoltaics,” Energy Environ. Sci. 5, 6857–6861 (2012).1754-5692 http://dx.doi.org/10.1039/c2ee21149a Google Scholar

52. K. H. Hendriks et al., “High-molecular-weight regular alternating diketopyrrolopyrrole-based terpolymers for efficient organic solar cells,” Angew. Chem. Int. Ed. 52, 8341–8344 (2013).ACIEF51433-7851 http://dx.doi.org/10.1002/anie.v52.32 Google Scholar

53. I. Meager et al., “Photocurrent enhancement from diketopyrrolopyrrole polymer solar cells through alkyl-chain branching point manipulation,” J. Am. Chem. Soc. 135, 11537–11540 (2013).JACSAT0002-7863 http://dx.doi.org/10.1021/ja406934j Google Scholar

54. Y. Liang et al., “Development of new semiconducting polymers for high performance solar cells,” J. Am. Chem. Soc. 131, 56–57 (2009).JACSAT0002-7863 http://dx.doi.org/10.1021/ja808373p Google Scholar

55. Y. Liang et al., “For the bright future—bulk heterojunction polymer solar cells with power conversion efficiency of 7.4%,” Adv. Mater. 22, E135–E138 (2010).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.200903528 Google Scholar

56. J.-D. Chen et al., “Single-junction polymer solar cells exceeding 10% power conversion efficiency,” Adv. Mater. (2014).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.201404535 Google Scholar

57. L. Huo et al., “Replacing alkoxy groups with alkylthienyl groups: a feasible approach to improve the properties of photovoltaic polymers,” Angew. Chem. Int. Ed. 50, 9697–9702 (2011).ACIEF51433-7851 http://dx.doi.org/10.1002/anie.201103313 Google Scholar

58. P. Adhikary et al., “Enhanced charge transport and photovoltaic performance of PBDTTT-C-T/PC70BM solar cells via UV-ozone treatment,” Nanoscale 5, 10007–10013 (2013).1556-276X http://dx.doi.org/10.1039/c3nr03355d Google Scholar

59. L. Ye et al., “Highly efficient 2D-conjugated benzodithiophene-based photovoltaic polymer with linear alkylthio side chain,” Chem. Mater. 26, 3603–3605 (2014).CMATEX0897-4756 http://dx.doi.org/10.1021/cm501513n Google Scholar

60. C. Cabanetos et al., “Linear side chains in benzo[1,2-b:4,5-b’]dithiophene-thieno[3,4-c]pyrrole-4,6-dione polymers direct self-assembly and solar cell performance,” J. Am. Chem. Soc. 135, 4656–4659 (2013).JACSAT0002-7863 http://dx.doi.org/10.1021/ja400365b Google Scholar

61. Y.-C. Chen et al., “Low-bandgap conjugated polymer for high efficient photovoltaic applications,” Chem. Commun. 46, 6503–6505 (2010).CHCOFS1364-548X http://dx.doi.org/10.1039/c0cc01087a Google Scholar

62. Y. Zhang et al., “Indacenodithiophene and quinoxaline-based conjugated polymers for highly efficient polymer solar cells,” Chem. Mater. 23, 2289–2291 (2011).CMATEX0897-4756 http://dx.doi.org/10.1021/cm200316s Google Scholar

63. C.-P. Chen, Y.-C. Chen and C.-Y. Yu, “Increased open circuit voltage in a fluorinated quinoxaline-based alternating conjugated polymer,” Polym. Chem. 4, 1161–1166 (2013).ACPPAY0032-3934 http://dx.doi.org/10.1039/c2py20798b Google Scholar

64. C.-P. Chen and H.-L. Hsu, “Increasing the open-circuit voltage in high-performance organic photovoltaic devices through conformational twisting of an indacenodithiophene-based conjugated polymer,” Macromol. Rapid Commun. 34, 1623–1628 (2013).MRCOE31521-3927 http://dx.doi.org/10.1002/marc.v34.20 Google Scholar

65. Z. Fei et al., “Germaindacenodithiophene based low band gap polymers for organic solar cells,” Chem. Commun. 48, 2955–2957 (2012).CHCOFS1364-548X http://dx.doi.org/10.1039/c2cc17996b Google Scholar

66. Y. He et al., “Indene-C60 bisadduct: a new acceptor for high-performance polymer solar cells,” J. Am. Chem. Soc. 132, 1377–1382 (2010).JACSAT0002-7863 http://dx.doi.org/10.1021/ja908602j Google Scholar

67. G. Zhao, Y. He and Y. Li, “6.5% efficiency of polymer solar cells based on poly(3-hexylthiophene) and indene-C60 bisadduct by device optimization,” Adv. Mater. 22, 4355–4358 (2010).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.v22:39 Google Scholar

68. Y.-J. Cheng et al., “Combination of indene-C60 bis-adduct and cross-linked fullerene interlayer leading to highly efficient inverted polymer solar cells,” J. Am. Chem. Soc. 132, 17381–17383 (2010).JACSAT0002-7863 http://dx.doi.org/10.1021/ja108259n Google Scholar

69. H. J. Bolink et al., “Martin, polymer solar cells based on diphenylmethanofullerenes with reduced sidechain length,” J. Mater. Chem. 21, 1382–1386 (2011).JMACEP0959-9428 http://dx.doi.org/10.1039/c0jm01160f Google Scholar

70. Y.-J. Cheng et al., “Di(4-methylphenyl)methano-C60 bis-adduct for efficient and stable organic photovoltaics with enhanced open-circuit voltage,” Chem. Mater. 23, 4056–4062 (2011).CMATEX0897-4756 http://dx.doi.org/10.1021/cm201784w Google Scholar

71. R. B. Ross et al., “Endohedral fullerenes for organic photovoltaic devices,” Nat. Mater. 8, 208–212 (2009).NMAACR1476-1122 http://dx.doi.org/10.1038/nmat2379 Google Scholar

72. R. B. Ross et al., “Tuning conversion efficiency in metallo endohedral fullerene-based organic photovoltaic devices,” Adv. Funct. Mater. 19, 2332–2337 (2009).AFMDC61616-3028 http://dx.doi.org/10.1002/adfm.v19:14 Google Scholar

73. Y. Zhou et al., “High performance all-polymer solar cell via polymer side-chain engineering,” Adv. Mater. 26, 3767–3772 (2014).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.v26.22 Google Scholar

74. Y. Kim and E. Lim, “Development of polymer acceptors for organic photovoltaic cells,” Polymers 6, 382–407 (2014).2073-4360 http://dx.doi.org/10.3390/polym6020382 Google Scholar

75. H. Hoppe et al., “Nanoscale morphology of conjugated polymer/fullerene-based bulk-heterojunction solar cells,” Adv. Funct. Mater. 14, 1005–1011 (2004).AFMDC61616-3028 http://dx.doi.org/10.1002/(ISSN)1616-3028 Google Scholar

76. Y. Zhang et al., “Bulk heterojunction solar cells based on a new low-band-gap polymer: morphology and performance,” Org. Electron. 12, 1211–1215 (2011).1566-1199 http://dx.doi.org/10.1016/j.orgel.2011.04.001 Google Scholar

77. W. Li et al., “Efficient small bandgap polymer solar cells with high fill factors for 300 nm thick films,” Adv. Mater. 25, 3182–3186 (2013).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.201300017 Google Scholar

78. F. Zhang et al., “Influence of solvent mixing on the morphology and performance of solar cells based on polyfluorene copolymer/fullerene blends,” Adv. Funct. Mater. 16, 667–674 (2006).AFMDC61616-3028 http://dx.doi.org/10.1002/(ISSN)1616-3028 Google Scholar

79. F.-C. Chen, H.-C. Tseng and C.-J. Ko, “Solvent mixtures for improving device efficiency of polymer photovoltaic devices,” Appl. Phys. Lett. 92, 103316 (2008).APPLAB0003-6951 http://dx.doi.org/10.1063/1.2898153 Google Scholar

80. A. J. Moulé and K. Meerholz, “Controlling morphology in polymer–fullerene mixtures,” Adv. Mater. 20, 240–245 (2008).ADVMEW0935-9648 http://dx.doi.org/10.1002/(ISSN)1521-4095 Google Scholar

81. J. Ajuria, “Hybrid photovoltaic devices based on organic semiconducting polymers and inorganic nanostructured electrodes,” PhD Thesis, Euskal Herriko Unibertsitatea (UPV/EHU) (2012). Google Scholar

82. Z. Bao, A. Dodabalapur and A. J. Lovinger, “Soluble and processable regioregular poly(3-hexylthiophene) for thin film field-effect transistor applications with high mobility,” Appl. Phys. Lett. 69, 4108–4110 (1996).APPLAB0003-6951 http://dx.doi.org/10.1063/1.117834 Google Scholar

83. H. Sirringhaus et al., “Two-dimensional charge transport in self-organized, high-mobility conjugated polymers,” Nature 401, 685–688 (1999).0028-0836 http://dx.doi.org/10.1038/44359 Google Scholar

84. H. Zhou et al., “High-efficiency polymer solar cells enhanced by solvent treatment,” Adv. Mater. 25, 1646–1652 (2013).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.201204306 Google Scholar

85. I. Burgués-Ceballos et al., “Fast annealing and patterning of polymer solar cells by means of vapor printing,” J. Polym. Sci. B Polym. Phys. 50, 1245–1252 (2012).JPLPAY0887-6266 http://dx.doi.org/10.1002/polb.v50.17 Google Scholar

86. D. Nassyrov et al., “Vapour printing: patterning of the optical and electrical properties of organic semiconductors in one simple step,” J. Mater. Chem. 22, 4519–4526 (2012).JMACEP0959-9428 http://dx.doi.org/10.1039/c2jm15190a Google Scholar

87. Z. He et al., “Enhanced power-conversion efficiency in polymer solar cells using an inverted device structure,” Nat. Photon. 6, 591–595 (2012).1749-4885 http://dx.doi.org/10.1038/nphoton.2012.190 Google Scholar

88. A. Martínez-Otero et al., “High-performance polymer solar cells using an optically enhanced architecture,” Adv. Opt. Mater. 1, 37–42 (2013).AOMDAX2195-1071 http://dx.doi.org/10.1002/adom.201200027 Google Scholar

89. M. Campoy-Quiles et al., “Morphology evolution via self-organization and lateral and vertical diffusion in polymer:fullerene solar cell blends,” Nat. Mater. 7, 158–164 (2008).NMAACR1476-1122 http://dx.doi.org/10.1038/nmat2102 Google Scholar

90. L. M. Chen et al., “Recent progress in polymer solar cells: manipulation of polymer:fullerene morphology and the formation of efficient inverted polymer solar cells,” Adv. Mater. 21, 1434–1449 (2009).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.v21:14/15 Google Scholar

91. K. Sugiyama et al., “Dependence of indium-tin-oxide work function on surface cleaning method as studied by ultraviolet and x-ray photoemission spectroscopies,” J. Appl. Phys. 87, 295–298 (2000).JAPIAU0021-8979 http://dx.doi.org/10.1063/1.371859 Google Scholar

92. T. M. Brown et al., “Built-in field electroabsorption spectroscopy of polymer light-emitting diodes incorporating a doped poly(3,4-ethylene dioxythiophene) hole injection layer,” Appl. Phys. Lett. 75, 1679–1681 (1999).APPLAB0003-6951 http://dx.doi.org/10.1063/1.124789 Google Scholar

93. A. C. Arias et al., “Doped conducting-polymer-semiconducting-polymer interfaces: their use in organic photovoltaic devices,” Phys. Rev. B 60, 1854–1860 (1999).PRBMDO0163-1829 http://dx.doi.org/10.1103/PhysRevB.60.1854 Google Scholar

94. A. J. Campbell et al., “Transient and steady-state space-charge-limited currents in polyfluorene copolymer diode structures with ohmic hole injecting contacts,” Appl. Phys. Lett. 76, 1734–1736 (2000).APPLAB0003-6951 http://dx.doi.org/10.1063/1.126182 Google Scholar

95. V. Shrotriya et al., “Transition metal oxides as the buffer layer for polymer photovoltaic cells,” Appl. Phys. Lett. 88, 073508 (2006).APPLAB0003-6951 http://dx.doi.org/10.1063/1.2174093 Google Scholar

96. M. D. Irwin et al., “p-type semiconducting nickel oxide as an efficiency-enhancing anode interfacial layer in polymer bulk-heterojunction solar cells,” Proc. Natl. Acad. Sci. 105, 2783–2787 (2008).PMASAX0096-9206 http://dx.doi.org/10.1073/pnas.0711990105 Google Scholar

97. E. I. Haskal et al., “Lithium-aluminum contacts for organic light-emitting devices,” Appl. Phys. Lett. 71, 1151–1153 (1997).APPLAB0003-6951 http://dx.doi.org/10.1063/1.119850 Google Scholar

98. L. S. Hung, C. W. Tang and M. G. Mason, “Enhanced electron injection in organic electroluminescence devices using an Al/LiF electrode,” Appl. Phys. Lett. 70, 152–154 (1997).APPLAB0003-6951 http://dx.doi.org/10.1063/1.118344 Google Scholar

99. J. Zhi-Qiang et al., “Improving efficiency of organic light-emitting devices by optimizing the LiF interlayer in the hole transport layer,” Chin. Phys. B 20, 107803 (2011).1674-1056 http://dx.doi.org/10.1088/1674-1056/20/10/107803 Google Scholar

100. X. Jiang et al., “Effect of CsF interlayer on the performance of polymer bulk heterojunction solar cells,” Sol. Energy Mater. Sol. Cells 93, 650–653 (2009).SEMCEQ0927-0248 http://dx.doi.org/10.1016/j.solmat.2009.01.005 Google Scholar

101. M. Reinhard et al., “Inverted organic solar cells comprising a solution-processed cesium fluoride interlayer,” Appl. Phys. Lett. 98, 053303 (2011).APPLAB0003-6951 http://dx.doi.org/10.1063/1.3548860 Google Scholar

102. L. Ke et al., “Magnesium fluoride modified interfaces for organic light-emitting diode,” Thin Solid Films 515, 3881–3886 (2007).THSFAP0040-6090 http://dx.doi.org/10.1016/j.tsf.2006.10.129 Google Scholar

103. T. Kuwabara et al., “Characterization of ZnS-layer-inserted bulk-heterojunction organic solar cells by ac impedance spectroscopy,” J. Appl. Phys. 105, 124513 (2009).JAPIAU0021-8979 http://dx.doi.org/10.1063/1.3153970 Google Scholar

104. L. Jiang et al., “Effects of cathode modification using spin-coated lithium acetate on the performances of polymer bulk-heterojunction solar cells,” Appl. Phys. Lett. 102, 013303 (2013).APPLAB0003-6951 http://dx.doi.org/10.1063/1.4773570 Google Scholar

105. F.-C. Chen et al., “Cesium carbonate as a functional interlayer for polymer photovoltaic devices,” J. Appl. Phys. 103, 103721 (2008).JAPIAU0021-8979 http://dx.doi.org/10.1063/1.2937202 Google Scholar

106. H.-H. Liao et al., “Highly efficient inverted polymer solar cell by low temperature annealing of Cs2CO3 interlayer,” Appl. Phys. Lett. 92, 173303 (2008).APPLAB0003-6951 http://dx.doi.org/10.1063/1.2918983 Google Scholar

107. Y. Park et al., “Study of the cesium carbonate (Cs2CO3) inter layer fabricated by solution process on P3HT:PCBM solar cells,” Mol. Cryst. Liq. Cryst. 538, 20–27 (2011).MCLCA50026-8941 http://dx.doi.org/10.1080/15421406.2011.563221 Google Scholar

108. F. Huang, H. Wu and Y. Cao, “Water/alcohol soluble conjugated polymers as highly efficient electron transporting/injection layer in optoelectronic devices,” Chem. Soc. Rev. 39, 2500–2521 (2010).CSRVBR0306-0012 http://dx.doi.org/10.1039/b907991m Google Scholar

109. K. Sun et al., “Highly efficient, inverted polymer solar cells with indium tin oxide modified with solution-processed zwitterions as the transparent cathode,” ACS Appl. Mater. Interfaces 4, 2009–2017 (2012).AAMICK1944-8244 http://dx.doi.org/10.1021/am201844q Google Scholar

110. K. Sun et al., “High-performance polymer solar cells with a conjugated zwitterion by solution processing or thermal deposition as the electron-collection interlayer,” J. Mater. Chem. 22, 24155–24165 (2012).JMACEP0959-9428 http://dx.doi.org/10.1039/c2jm35221d Google Scholar

111. T. M. Khan et al., “Organic photovoltaic cells with stable top metal electrodes modified with polyethylenimine,” ACS Appl. Mater. Interfaces 6, 6202–6207 (2014).AAMICK1944-8244 http://dx.doi.org/10.1021/am501236z Google Scholar

112. C. J. Brabec et al., “Effect of LiF/metal electrodes on the performance of plastic solar cells,” Appl. Phys. Lett. 80, 1288–1290 (2002).APPLAB0003-6951 http://dx.doi.org/10.1063/1.1446988 Google Scholar

113. J. Y. Kim et al., “New architecture for high-efficiency polymer photovoltaic cells using solution-based titanium oxide as an optical spacer,” Adv. Mater. 18, 572–576 (2006).ADVMEW0935-9648 http://dx.doi.org/10.1002/(ISSN)1521-4095 Google Scholar

114. M.-H. Park et al., “Doping of the metal oxide nanostructure and its influence in organic electronics,” Adv. Funct. Mater. 19, 1241–1246 (2009).AFMDC61616-3028 http://dx.doi.org/10.1002/adfm.v19:8 Google Scholar

115. J. Gilot et al., “The use of ZnO as optical spacer in polymer solar cells: theoretical and experimental study,” Appl. Phys. Lett. 91, 113520 (2007).APPLAB0003-6951 http://dx.doi.org/10.1063/1.2784961 Google Scholar

116. Z. He et al., “Simultaneous enhancement of open-circuit voltage, short-circuit current density, and fill factor in polymer solar cells,” Adv. Mater. 23, 4636–4643 (2011).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.201103006 Google Scholar

117. J. Reinhardt et al., “Identifying the impact of surface recombination at electrodes in organic solar cells by means of electroluminescence and modeling,” Adv. Energy Mater. 4(11), 1400081 (2014).ADEMBC1614-6832 http://dx.doi.org/10.1002/aenm.201400081 Google Scholar

118. A. Guerrero et al., “Charge carrier transport and contact selectivity limit the operation of PTB7-based organic solar cells of varying active layer thickness,” J. Mater. Chem. A 1, 12345–12354 (2013).JMACEP0959-9428 http://dx.doi.org/10.1039/c3ta12358h Google Scholar

119. A. Guerrero et al., “Interplay between fullerene surface coverage and contact selectivity of cathode interfaces in organic solar cells,” ACS Nano 7, 4637–4646 (2013).1936-0851 http://dx.doi.org/10.1021/nn4014593 Google Scholar

120. J. Ajuria et al., “Inverted ITO-free organic solar cells based on p and n semiconducting oxides. New designs for integration in tandem cells, top or bottom detecting devices, and photovoltaic windows,” Energy Environ. Sci. 4, 453–458 (2011).1754-5692 http://dx.doi.org/10.1039/c0ee00318b Google Scholar

121. Y. Zhou et al., “A universal method to produce low-work function electrodes for organic electronics,” Science 336, 327–332 (2012).SCIEAS0036-8075 http://dx.doi.org/10.1126/science.1218829 Google Scholar

122. A. K. K. Kyaw et al., “Efficient solution-processed small-molecule solar cells with inverted structure,” Adv. Mater. 25, 2397–2402 (2013).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.v25.17 Google Scholar

123. W. Shockley and H. J. Queisser, “Detailed balance limit of efficiency of p-n junction solar cells,” J. Appl. Phys. 32, 510–519 (1961).JAPIAU0021-8979 http://dx.doi.org/10.1063/1.1736034 Google Scholar

124. T. Ameri et al., “Organic tandem solar cells: a review,” Energy Environ. Sci. 2, 347–363 (2009).1754-5692 http://dx.doi.org/10.1039/b817952b Google Scholar

125. S. Sista et al., “Tandem polymer photovoltaic cells-current status, challenges and future outlook,” Energy Environ. Sci. 4, 1606–1620 (2011).1754-5692 http://dx.doi.org/10.1039/c0ee00754d Google Scholar

126. S. Sista et al., “High-efficiency polymer tandem solar cells with three-terminal structure,” Adv. Mater. 22, E77–E80 (2010).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.v22:8 Google Scholar

127. I. Etxebarria et al., “Series vs parallel connected organic tandem solar cells: cell performance and impact on the design and operation of functional modules,” Sol. Energy Mater. Sol. Cells 130, 495–504.(2014).SEMCEQ0927-0248 http://dx.doi.org/10.1016/j.solmat.2014.07.047 Google Scholar

128. M. C. Scharber et al., “Design rules for donors in bulk-heterojunction solar cells—towards 10% energy-conversion efficiency,” Adv. Mater. 18, 789–794 (2006).ADVMEW0935-9648 http://dx.doi.org/10.1002/(ISSN)1521-4095 Google Scholar

129. G. Dennler et al., “Design rules for donors in bulk-heterojunction tandem solar cells—towards 15% energy-conversion efficiency,” Adv. Mater. 20, 579–583 (2008).ADVMEW0935-9648 http://dx.doi.org/10.1002/(ISSN)1521-4095 Google Scholar

130. M. Hiramoto, M. Suezaki and M. Yokoyama, “Effect of thin gold interstitial-layer on the photovoltaic properties of tandem organic solar cell,” Chem. Lett. 19, 327–330 (1990).CMLTAG0366-7022 http://dx.doi.org/10.1246/cl.1990.327 Google Scholar

131. G. Dennler et al., “Enhanced spectral coverage in tandem organic solar cells,” Appl. Phys. Lett. 89, 073502 (2006).APPLAB0003-6951 http://dx.doi.org/10.1063/1.2336593 Google Scholar

132. A. Colsmann et al., “Organic tandem solar cells comprising polymer and small-molecule subcells,” Appl. Phys. Lett. 89, 203506 (2006).APPLAB0003-6951 http://dx.doi.org/10.1063/1.2388938 Google Scholar

133. A. G. F. Janssen et al., “Highly efficient organic tandem solar cells using an improved connecting architecture,” Appl. Phys. Lett. 91, 073519 (2007).APPLAB0003-6951 http://dx.doi.org/10.1063/1.2772208 Google Scholar

134. D. W. Zhao et al., “Efficient tandem organic solar cells with an Al/MoO3 intermediate layer,” Appl. Phys. Lett. 93, 083305 (2008).APPLAB0003-6951 http://dx.doi.org/10.1063/1.2976126 Google Scholar

135. B. J. Lee et al., “A transparent conducting oxide as an efficient middle electrode for flexible organic tandem solar cells,” Sol. Energy Mater. Sol. Cells 94, 542–546 (2010).SEMCEQ0927-0248 http://dx.doi.org/10.1016/j.solmat.2009.11.021 Google Scholar

136. K. Kawano et al., “Open circuit voltage of stacked bulk heterojunction organic solar cells,” Appl. Phys. Lett. 88, 073514 (2006).APPLAB0003-6951 http://dx.doi.org/10.1063/1.2177633 Google Scholar

137. A. Hadipour et al., “Solution-processed organic tandem solar cells,” Adv. Funct. Mater. 16, 1897–1903 (2006).AFMDC61616-3028 http://dx.doi.org/10.1002/(ISSN)1616-3028 Google Scholar

138. J. Y. Kim et al., “Efficient tandem polymer solar cells fabricated by all-solution processing,” Science 317, 222–225 (2007).SCIEAS0036-8075 http://dx.doi.org/10.1126/science.1141711 Google Scholar

139. J. Gilot, M. M. Wienk and R. A. J. Janssen, “Optimizing polymer tandem solar cells,” Adv. Mater. 22, E67–E71 (2010).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.v22:8 Google Scholar

140. S. Sista et al., “Highly efficient tandem polymer photovoltaic cells,” Adv. Mater. 22, 380–383 (2010).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.v22:3 Google Scholar

141. J. Yang et al., “A robust inter-connecting layer for achieving high performance tandem polymer solar cells,” Adv. Mater. 23, 3465–3470 (2011).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.201100221 Google Scholar

142. C.-H. Chou et al., “A metal-oxide interconnection layer for polymer tandem solar cells with an inverted architecture,” Adv. Mater. 23, 1282–1286 (2011).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.201001033 Google Scholar

143. L. Dou et al., “Tandem polymer solar cells featuring a spectrally matched low-bandgap polymer,” Nat. Photon. 6, 180–185 (2012).1749-4885 http://dx.doi.org/10.1038/nphoton.2011.356 Google Scholar

144. L. Dou et al., “Systematic investigation of benzodithiophene- and diketopyrrolopyrrole-based low-bandgap polymers designed for single junction and tandem polymer solar cells,” J. Am. Chem. Soc. 134, 10071–10079 (2012).JACSAT0002-7863 http://dx.doi.org/10.1021/ja301460s Google Scholar

145. J. You et al., “10.2% power conversion efficiency polymer tandem solar cells consisting of two identical sub-cells,” Adv. Mater. 25, 3973–3978 (2013).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.v25.29 Google Scholar

146. C.-C. Chen et al., “An efficient triple-junction polymer solar cell having a power conversion efficiency exceeding 11%,” Adv. Mater. 26, 5670–5677 (2014).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.201402072 Google Scholar

147. A. R. b. M. Yusoff et al., “A high efficiency solution processed polymer inverted triple-junction solar cell exhibiting a power conversion efficiency of 11.83%,” Energy Environ. Sci. 8, 303–316 (2015).1754-5692 http://dx.doi.org/10.1039/C4EE03048F Google Scholar

Biography

Ikerne Etxebarria received her BSc degree in chemical engineering in 2009 and a master’s degree in new materials in 2010 from the University of the Basque Country. In 2014, she was awarded her PhD degree by the same university. At present, her main research activity is focused on surface functionalization by means of inkjet printing, on the one hand for photoactive layer patterning for OPV module fabrication and on the other for sensor applications.

Jon Ajuria received his chemistry degree in 2003 from the University of the Basque Country. In 2007, he moved to IKERLAN to carry out his PhD thesis on hybrid organic-inorganic solar cells. He was awarded his PhD degree by the University of the Basque Country in 2012. At present, his main research focus in the development of inverted single and tandem solar cells based on new generation low band gap materials and inorganic nanostructured electrodes.

Roberto Pacios graduated in physics from the University of the Basque Country, Spain, in 1999. He was awarded his PhD degree by Imperial College London in 2003. After a postdoctoral stay, he moved to Siemens in Erlangen, Germany. In 2006 he moved to the Microsystems Department of IK4-IKERLAN, where he leads activities in plastics electronics and organic photovoltaics. His research career has been focused on material characterization, device integration, and module development of polymer solar cells.

© 2015 Society of Photo-Optical Instrumentation Engineers (SPIE)
Ikerne Etxebarria, Ikerne Etxebarria, Jon Ajuria, Jon Ajuria, Roberto Pacios, Roberto Pacios, } "Polymer:fullerene solar cells: materials, processing issues, and cell layouts to reach power conversion efficiency over 10%, a review," Journal of Photonics for Energy 5(1), 057214 (16 February 2015). https://doi.org/10.1117/1.JPE.5.057214 . Submission: