4 February 2013 Photoluminescence of water-soluble NdF3 nanoparticles by codoping Li+ or Ba2+ ions
Author Affiliations +
Water-soluble NdF 3 , NdF 3 :Li + , and NdF 3 :Ba 2+ nanoparticles coated with polyvinylpyrrolidone were synthesized by a simple hydrothermal method. The products were characterized by x-ray diffraction, field-emission scanning electron microscopy, and photoluminescence spectra at room temperature. Codoping with Li + ions does not change the emission intensity of water-soluble NdF 3 nanoparticles, whereas codoping with Ba 2+ ions improves the near-infrared emissions.



In recent years, water-soluble fluorescent nanoparticles have been applied often in biological label applications.1,2 Among the fluorescent nanoparticles, rare-earth ion–doped nanoparticles have played an important role. They show superior chemical and optical properties, including low toxicity, large effective Stokes shifts, sharp emission band widths of 10–20 nm, and high resistance to photobleaching, blinking, and photochemical degradation.3 The problem with rare-earth ion-doped nanoparticles is their weak luminescence efficiency. Consequently, a great deal of research work has been devoted to improving luminescence efficiency of rare-earth ion–doped nanoparticles.4,5

NdF3 nanoparticles have been reported to lack the concentration quenching effect and have very low phonon energy.6 NdF3 nanoparticles coated with silica shells have been used in biological detection for near-infrared (NIR) luminescence.7 When NdF3 nanoparticles disperse in water, the luminescence intensity is weakened. Improving the photoluminescence (PL) of water-soluble NdF3 nanoparticles is urgent.

It is possible to tune the emission intensity of rare-earth ions by modifying neighboring network environment by introducing other atoms into the host lattice. Commonly, incorporation of metal atoms into host lattice can distort the lattice and modify the energy absorption and transfer behaviors, resulting in increased emission intensity of rare-earth ions. The reason is that the doped metal atoms distort the local symmetry around rare-earth ions and modify the selection rules of rare earth ions.89.10

In this study, water-soluble NdF3, NdF3:Li+, and NdF3:Ba2+ nanoparticles coated with polyvinylpyrrolidone (PVP) were synthesized by a facile hydrothermal method. Morphology and luminescence properties were studied. In comparison with NdF3 nanoparticles, codoping with Ba2+ ions improves the NIR emissions of NdF3, whereas codoping with Li+ ions does not appreciably change the emission intensity. The reason for the phenomena is discussed below.



NdF3 and NdF3/PVP nanoparticles were prepared via a hydrothermal method previously described.9 The NdF3:Li+/PVP nanoparticles were prepared by adding 0.3 g PVP and 5% LiNO3 into the solution, and NdF3:Ba2+/PVP nanoparticles were prepared by adding 0.3 g PVP and 5% BaCl2 into the solution.

The powder x-ray diffraction (XRD) patterns were tested by Philips PW1830 diffractometer using CuKα irradiation at 40 kV and 40 mA. The morphologies were imaged with field-emission scanning electron microscopy (FE-SEM) (Nova NanoSEM 430) operating at 10 Kv. The PL spectra were measured at room temperature through a spectrometer (Jobin-Yvon Triax320) with an 808-nm laser diode as excitation source recorded with a liquid nitrogen–cooled InGaAs detector.



Figure 1 shows the typical XRD patterns of the synthesized nanoparticles. All the diffraction peaks are well matched with theoretical data for hexagonal-phase structure of NdF3, with lattice constants a=0.7030nm and c=0.7199nm (Joint Committee on Powder Diffraction Standards no. 9-416). No other impurity peaks were detected. These results indicate that the coating of PVP does not change the hexagonal phase of NdF3 nanoparticles and the codoping Li+ and Ba2+ ions completely entered the host lattice without formation of any additional phase at codoped concentrations.

Fig. 1

XRD patterns of NdF3, NdF3/PVP, NdF3:Li+/PVP, and NdF3:Ba2+/PVP nanoparticles.


The FE-SEM images of NdF3, NdF3/PVP, NdF3:Li+/PVP, and NdF3:Ba2+/PVP nanoparticles are shown in Fig. 2. The NdF3 particles are monodisperse nanoplates, as shown in Fig. 2(a). The diameter of the plates is estimated to be in the range of 80–120 nm, whereas the thickness is about 30 nm. When coating with water-soluble PVP, the morphology of the nanoplates is nearly the same as that of the former particles, as shown in Fig. 2(b). Then codoped with Li+ ions, as shown in Fig. 2(c), the morphology does not have any distinct change compared to Fig. 2(b). When codoped with Ba2+, the morphology has changed, as shown in Fig. 2(d): the diameter of the nanoparticles became more uniform and decreased to about 60 nm, while the thickness has not changed, indicating that Ba2+ ions inhibit the growing of nanoplates in the direction of the plane. The smaller size of NdF3:Ba2+/PVP nanoparticles is of benefit for the use of biological labels.

Fig. 2

FE-SEM images of NdF3 (a), NdF3/PVP (b), NdF3:Li+/PVP (c), and NdF3:Ba2+/PVP (d) nanoparticles.


The PL spectra of the nanoparticles under 808-nm laser excitation at room temperature are shown in Fig. 3. The spectra represent the main transition of Nd3+ ions at 1060 nm corresponding to F3/24I11/24 channel. The coating of PVP layer increases the PL intensity of NdF3 at 1060 nm by 16%. The increase is perhaps due to the PVP layer, which prevents the energy losses from surface quenching of NdF3 nanoparticles.11

Fig. 3

Fluorescence spectra of NdF3, NdF3/PVP, NdF3:Li+/PVP, and NdF3:Ba2+/PVP nanoparticles under 808-nm laser excitation.




When codoping with Li+ ions into NdF3/PVP nanoparticles, the NIR emission intensity does not have any appreciable change, unlike the PL enhancement we reported in Y2O3 nanocrystals codoped with Li+ ions. But when divalent ions Ba2+ are codoped into NdF3/PVP nanoparticles, the NIR emission intensity increases further by 25% at 1060 nm.

Codoping of Li+ ions (5%) did not change the emission intensity of NdF3/PVP nanoparticles, whereas codoping of Ba2+ ions (5%) enhanced the NIR emission. The results could be due to the different ionic radius. The ionic radius for Li+, Ba2+, and Nd3+ ions are 76, 135, and 98.3 pm, respectively. Ba2+ ions have large ionic radii, which might distort the lattice network of Nd3+ ions in NdF3, resulting in the enhanced PL intensity. The smaller Li+ ions might be unable to distort the lattice network of Nd3+ ions in NdF3 enough to influence the PL intensity.



We have presented a simple synthesis method of water-soluble NdF3/PVP, NdF3:Li+/PVP, and NdF3:Ba2+/PVP nanoparticles by coating with a layer of hydrophilic polymer PVP via hydrothermal method. Codoping with Li+ ions does not change the emission intensity of water-soluble NdF3 nanoparticles, whereas codoping with Ba2+ ions improves the NIR emissions.


This work was supported by Foundation for Distinguished Young Talents in Higher Education of Guangdong Province, China (No. 2012LYM_0131) and National Natural Science Foundation of China (No. 61008063).


1. E. Schröcket al., “Multicolor spectral karyotyping of human chromosomes,” Science 273(5274), 494–497 (1996).SCIEAS0036-8075 http://dx.doi.org/10.1126/science.273.5274.494 Google Scholar

2. J. KimY. PiaoT. Hyeon, “Multifunctional nanostructured materials for multimodal imaging, and simultaneous imaging and therapy,” Chem. Soc. Rev. 38(2), 372–390 (2009).CSRVBR0306-0012 http://dx.doi.org/10.1039/b709883a Google Scholar

3. F. WangX. J. XueX. G. Liu, “Multicolor tuning of (Ln, P)-doped YVO4 nanoparticles by single-wavelength excitation,” Angew. Chem. Int. Ed. 47(2), 906–909 (2008).ACIEF51433-7851 http://dx.doi.org/10.1002/(ISSN)1521-3773 Google Scholar

4. G. Wanget al., “Enhanced photoluminescence of water soluble YVO4:Ln3+ (Ln=Eu, Dy, Sm, and Ce) nanocrystals by Ba2+ doping,” J. Phys. Chem. C 112(44), 17042–17045 (2008).1932-7447 http://dx.doi.org/10.1021/jp807577b Google Scholar

5. R. Balakrishnaiahet al., “Effect of Al3+ ions on fluorescence properties of YPO4:Eu3+ phosphors,” Mater. Lett. 63(23), 2063–2066 (2009).MLETDJ0167-577X http://dx.doi.org/10.1016/j.matlet.2009.06.053 Google Scholar

6. F. Baoet al., “Self-assembly of mono-crystalline NdF3 nanostructures during hydrothermal process,” Mater. Lett. 60(3), 389–392 (2006).MLETDJ0167-577X http://dx.doi.org/10.1016/j.matlet.2005.08.058 Google Scholar

7. X. Yuet al., “Highly efficient fluorescence of NdF3/SiO2 core/shell nanoparticles and the applications for in vivo NIR detection,” Adv. Mater. 20(21), 4118–4123 (2008).ADVMEW0935-9648 http://dx.doi.org/10.1002/adma.v20:21 Google Scholar

8. T. FanQ. ZhangZ. Jiang, “Enhancement of the 1.5 μm emission in Y2O3:Er3+ nanocrystals by codoping with Li+ ions,” J. Opt. 13(1), 015001 (2011).JOOPDB0150-536X http://dx.doi.org/10.1088/2040-8978/13/1/015001 Google Scholar

9. T. FanQ. ZhangZ. Jiang, “Enhanced near infrared emission in water-soluble NdF3 nanocrystals by Ba2+ doping,” Chin. Opt. Lett. 10(2), 021602 (2012).COLHBT1671-7694 http://dx.doi.org/10.3788/COL Google Scholar

10. Y. Baiet al., “The effect of Li on the spectrum of Er3+ in Li- and Er-codoped ZnO nanocrystals,” J. Phys. Chem. C 112(32), 12259–12263 (2008).1932-7447 http://dx.doi.org/10.1021/jp803373e Google Scholar

11. G. Ghoshet al., “Synthesis and characterization of PVP-encapsulated ZnS nanoparticles,” Opt. Mater. 28(8), 1047–1053 (2006).OMATET0925-3467 http://dx.doi.org/10.1016/j.optmat.2005.06.003 Google Scholar

© 2013 Society of Photo-Optical Instrumentation Engineers (SPIE)
Ting Fan, Ting Fan, Jiantao Lü, Jiantao Lü, Na Li, Na Li, Dingan Han, Dingan Han, } "Photoluminescence of water-soluble NdF3 nanoparticles by codoping Li+ or Ba2+ ions," Optical Engineering 52(2), 020503 (4 February 2013). https://doi.org/10.1117/1.OE.52.2.020503 . Submission:

Back to Top