The manufacturing methods and materials for diffractive optical elements are actively developed due to the prospects of their use in various components of the microsystem technology. Photolithography occupies a central place in modern manufacturing technology for such components. The photoresists used in it can be exposed to high (100-150 degrees) temperatures, treated in a liquid environment, aggressive (alkaline, acidic) fluids, reactive ion etching (RIE), and electrolyte exposed to electrochemical deposition of metals. Therefore, the development of photoresist materials with thermo-, plasma-, chemo- and moisture resistance is relevant and of the high interest at this time. One of the promising classes of organic compounds with photoresistive properties is the chalcones. It is shown that polyfluorochalcones are capable of providing the holographic recording of transmission gratings with diffraction efficiency up to 59% and angular selectivity up to 54.5°. The masking and thermal properties of triacrylamide polyfluorochalcon (TAPCh), its triaryl pyrazoline modification (TAP), as well as modifications by prepolymerized triaryl pyrazoline (polyTAP) under liquid chemical conditions (in H2SO4, H3PO4, NaOH) and reactive ion etching (in plasma CF4) were investigated. A comparison of properties with commercially available photoresists SU-8, AZ4562 was also conducted. It has been shown that TAFH is resistant to liquid etching, which is the same for SU-8, but shows higher results in RIE process; TAFH exceeds the performance of photoresist AZ4562 in resistance to RIE, and significantly exceeds it in liquid (alkaline and acid) etching; thermal stability TAFH exceeds SU-8 and AZ4562.
Access to the requested content is limited to institutions that have purchased or subscribe to SPIE eBooks.
You are receiving this notice because your organization may not have SPIE eBooks access.*
*Shibboleth/Open Athens users─please
sign in
to access your institution's subscriptions.
To obtain this item, you may purchase the complete book in print or electronic format on
SPIE.org.
INSTITUTIONAL Select your institution to access the SPIE Digital Library.
PERSONAL Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.