Ethanol sensitivity of bismuth molybdate thick films and sintered pellets were investigated. Sintered pellets were prepared by traditional ceramic processing. Thick films were prepared by metallorganic decomposition process. Ethanol gas sensitivity was measured at various temperatures and concentrations. Thick films of alpha phase bismuth molybdate prepared by spray pyrolysis showed a very fast response to ethanol detection. The response time for the bulk samples is about 40 sec which decreased to about 6 sec for thick films at an operating temperature of 300°C. An extremely low level approximately 10 ppm detection and fast response makes this technique ideal for sensor element fabrication for detection and estimation of alcohol in breath-analyzer. Unlike SnO2, the resistance of these sensors is not affected by humidity at the operating temperature.