KEYWORDS: Epoxies, Failure analysis, Polymers, High speed cameras, Scanning electron microscopy, Cameras, Digital cameras, Electron microscopes, Civil engineering, Adhesives
The failure processes of an epoxy polymer (Epicote 21506) were studied by using a high speed camera evolving over a range of strain rates from 0.0001s-1 to 668s-1. The front surface of the specimen was monitored by the high speed camera to capture the deformation and cracking processes. A split Hopkinson
pressure bar (SHPB) was utilized to examine the dynamic response of the material, and the uniaxial compression test was applied for its quasi-static behavior. The microstructure of the specimen fracture
surface after quasi-static and dynamic compression was also investigated by using a Scanning Electron Microscope (SEM) to look insight into the failure mechanism of the material. With the coupled analysis of stress-strain curves and captured images, the behaviors of the specimen under static and dynamic loading can be determined precisely with sufficient details. The specimen under static loading displayed ductile failure, while that under dynamic loading revealed different brittle damage behaviors.
Access to the requested content is limited to institutions that have purchased or subscribe to SPIE eBooks.
You are receiving this notice because your organization may not have SPIE eBooks access.*
*Shibboleth/Open Athens users─please
sign in
to access your institution's subscriptions.
To obtain this item, you may purchase the complete book in print or electronic format on
SPIE.org.
INSTITUTIONAL Select your institution to access the SPIE Digital Library.
PERSONAL Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.