Objectives: The purpose of this research was to determine the mechanical properties and corrosion behavior of 0.5% Co-DI before and after heat treatment and compare with commercial ductile iron. Methods: Molten metal of newly developed ductile iron which alloyed with 0.5% Cobalt produced through CO2 sand casting method. The specimens then performed preheat to 500°C in an hour then oil quenched. Specimens then performed annealing to 900°C in half an hour before oil quenched again. 500°C, 600°C and 700°C austempering temperature had been selected subjected to the specimens in half an hour before cooled to room temperature. The tests involved are microstructure analysis which included nodule count and phase analysis, polarization test, spectrometer test, density test, tensile test (ASTM E 8M), hardness test and impact test (ASTM A327) on as cast and austempered specimen. Results: 0.5% Cobalt alloyed austempered ductile iron with 500°C austempered temperature is the optimum temperature for 0.5% Co-ADI. It's not
only increase the nodule count in the content, but also improve the mechanical properties such as impact toughness and tensile strength. Corrosion rate of 0.5% Co-DI also improved compare to unalloyed DI.
Access to the requested content is limited to institutions that have purchased or subscribe to SPIE eBooks.
You are receiving this notice because your organization may not have SPIE eBooks access.*
*Shibboleth/Open Athens users─please
sign in
to access your institution's subscriptions.
To obtain this item, you may purchase the complete book in print or electronic format on
SPIE.org.
INSTITUTIONAL Select your institution to access the SPIE Digital Library.
PERSONAL Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.