Laser micro-machining of amorphous PEEK has been demonstrated with 180 fs/1 kHz NIR (775 nm) and NUV (387 nm) laser pulses. The single pulse ablation threshold was found to be 2.01 ± 0.05 J/cm2 and 0.23 ± 0.02 J/cm2 at 775 nm and 387 nm respectively. The significant difference in ablation threshold is due to the requirement for 3-photon absorption at 775 nm, where PEEK is transparent while significant linear absorption within the material bandgap occurs at 387 nm, enhancing 2-photon absorption. A high 2-photon absorption coefficient, measured to be β387 ~ 38 cm GW-1 supports this view while at the bandgap edge, 400 nm, β400 ~ 0.7 cm GW-1. Multi-pulse exposure yields incubation coefficients of S775 = 0.72 ± 0.01 and S387 = 0.85 ± 0.02 hence incubation is significantly reduced in the NUV. Ablation of PEEK with NUV fs pulses demonstrates much reduced melting and re-deposition, thus precision NUV polymer micromachining is accomplished while laser induced periodic surface structures (LIPSS) with pitch Λ < 0.4 μm are observed at the base of ablated regions. Scanned areas exhibit white light diffraction due to this sub-micron periodic surface modulation. With the aid of a phase only spatial light modulator, multi-beam NUV micro-structuring is achieved, speeding micro-processing while reaching a line width < 4 μm with NA = 0.4 objective.
Access to the requested content is limited to institutions that have purchased or subscribe to SPIE eBooks.
You are receiving this notice because your organization may not have SPIE eBooks access.*
*Shibboleth/Open Athens users─please
sign in
to access your institution's subscriptions.
To obtain this item, you may purchase the complete book in print or electronic format on
SPIE.org.
INSTITUTIONAL Select your institution to access the SPIE Digital Library.
PERSONAL Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.